Activated carbon fibre monoliths

Activated carbon fibre monoliths were prepared by physical activation of carbon fibre monoliths derived from two kinds of pitch-based carbon fibre (CF) (carbon fibres from a coal tar pitch and carbon fibres derived from a petroleum pitch). The monoliths were conformed using a coal tar pitch binder. The carbon fibre monoliths and the activated carbon fibre monoliths were studied by scanning electron microscopy (SEM) and gas adsorption (i.e. N2 at 77 K and CO2 at 273 K). The results obtained reveal that monoliths perform a good activation process that produce a quite high development of microporosity (BET surface areas around 2600 m2/g and N2 micropore volume of 1.23 cm3/g). On the other hand, it is remarkable that the activation process used allow to easily control the degree of activation and hence to select the adsorption capacities of the activated carbon fibre monoliths.

Caracterización mecánica de morteros de cemento Portland con breas de petróleo y de alquitrán de carbón

En este artículo se presentan datos experimentales de resistencia a flexión y a compresión de morteros de cemento Portland con adición y sustitución de breas de petróleo y de alquitrán de carbón, que son subproductos de la industria del carbón o del petróleo. Los materiales estudiados son breas de alquitrán de carbón A (BACA) y B (BACB), y dos breas de petróleo (BPP) y (BPT). Los datos demuestran la viabilidad del uso de estas breas en la fabricación de morteros con menores contenidos de cemento, permitiendo diseñar un nuevo material sostenible con el medio ambiente y que contribuya a reducir el impacto ambiental de los materiales de construcción, hecho que permite abrir una nueva vía de valorización de estos subproductos.

KOH activation of carbon materials obtained from the pyrolysis of ethylene tar at different temperatures

A complete study of the importance of the pyrolysis temperature (up to 1500 °C) of a petroleum residue (ethylene tar) in the activation with KOH of the resultant pyrolysis products (covering from the own ethylene tar to pitches and well developed cokes) has been carried out. The trend in the porosity found for activated carbons is as follows: the pore volume increases with the pyrolysis temperature reaching a maximum value (1.39 cm3/g) at about 460 °C, just at the transition temperature between a fluid pitch and a solid coke. It is the pitch with highest mesophase content that develops the maximum porosity when activated with KOH. The amount of H2, CO and CO2 produced during the reaction of the mesophase pitch and coke with KOH has been quantified, and a trend as described for the pore volume was found with the pyrolysis temperature. Therefore, there is a relationship between the reactivity of the precursor with KOH and the porosity developed by the activated carbon. Since the reactions that produce H2 initiate at temperatures as low as 300 °C, it seems that KOH is modifying the conditions under which the pyrolysis occurs, and this fact is critical in the development of porosity.