Methoxylation of α-pinene over mesoporous carbons and microporous carbons: A comparative study

A biomass derived carbon, a commercial microporous carbon and a xerogel mesoporous carbon catalysts were used in the study of α-pinene methoxilation reaction and the influence of textural and physical–chemical properties of the carbons was evaluated. Biomass carbon presented the higher activity, whereas the commercial one is the less active in the conditions studied. The main product of the reaction was α-terpinyl methyl ether and good values of selectivity were obtained over all the catalysts. A kinetic model was developed assuming that the α-pinene is consumed according to the parallel reaction network. The kinetic model presents high quality fittings to the experimental concentration profiles. These results show that it is possible to activate a waste residue using H3PO4 and convert it to high added value product such as acid catalyst.

Electrochemical analysis of the performance of carbon supported Pd nanoparticles for direct formic acid fuel cells: from gold supported electrodes to catalyst-coated membranes

In this work carbon supported Pd nanoparticles were prepared and used as electrocatalysts for formic acid electrooxidation fuel cells. The influence of some relevant parameters such as the nominal Pt loading, the Nafion/total solids ratio as well as the Pd loading towards formic acid electrooxidation was evaluated using gold supported catalytic layer electrodes which were prepared using a similar methodology to that employed in the preparation of conventional catalyst coated membranes (CCM). The results obtained show that, for constant Pd loading, the nominal Pd loading and the Nafion percentage on the catalytic layer do not play an important role on the resulting electrocatalytic properties. The main parameter affecting the electrocatalytic activity of the electrodes seems to be the Pd loading, although the resulting activity is not directly proportional to the increased Pd loading. Thus, whereas the Pd loading is multiplied by a factor of 10, the activity is only twice which evidences an important decrease in the Pd utilization. In fact, the results obtained suggest the active layer is the outer one being clearly independent of the catalytic layer thickness. Finally, catalyst coated membranes with Pd catalyst loadings of 0.1, 0.5 and 1.2 mg cm-2 were also tested in a breathing direct formic acid fuel cell.

Continuous flow nanocatalysis: reaction pathways in the conversion of levulinic acid to valuable chemicals

The selective production of 2-methyltetrahydrofuran from levulinic acid has been effectively conducted using designed Cu based catalysts and compared with a commercial Pd/C system under microwave irradiation. Optimised conditions for the most active catalysts Cu-MINT (>90% conversion, 75% selectivity to MTHF) and Pd/C (78% conversion, 92% selectivity to MTHF) were further translated into a continuous flow process using the proposed catalysts to find out the deactivation of Cu-MINT under flow conditions (79 vs. 13% conversion with a switch in selectivity to products after 30 min in flow), the high stability of Pd/C (73 vs. 70% conversion at stable selectivity under analogous conditions to those of Cu-MINT) but, most importantly, different relevant pathways to valuable products from levulinic acid depending on the type of catalyst employed.

Aqueous organocatalyzed aldol reaction of glyoxylic acid for the enantioselective synthesis of α-hydroxy-γ-keto acids

N-Tosyl-(Sa)-binam-L-prolinamide is an efficient catalyst for the aqueous aldol reaction, between glyoxylic acid, as monohydrate or aqueous solution, and ketones. This reaction led to the formation of chiral α-hydroxy-γ-keto carboxylic acids in high levels of diastereo- and enantioselectivities achieving mainly anti aldol products.

Biodiesel production by acid catalysis with heteropolyacids supported on activated carbon fibers

Different catalysts, based on heteropolyacids supported on activated carbon fibers, have been prepared for palmitic acid esterification reaction. The influence of the catalyst (heteropolyacid) and the support on the catalytic activity have been analyzed. The results prove that an adequate combination of both is required to achieve the most suitable catalysts. Regarding to the heteropolyacid, phosphomolybdic acid seems to be the most suitable appropriate taking into account its lowest leaching. About the support, it must show an optimum microporosity, which must be wide enough to allow the entrance and exit of the reagents and products but not too wide in order to avoid the leaching of the catalyst. In addition, both decreasing of the catalytic activity and its recovery over several cycles have been analyzed.

Abatement of hydrocarbons by acid ZSM-5 and BETA zeolites under cold-start conditions

Simulated cold-start tests have been carried out to evaluate the performance of H-ZSM-5 and H-BETA zeolites as hydrocarbon traps under simulated gasoline car exhaust gases, paying special attention to the effect of water on their behaviour. It is concluded that the hydrothermal treatment of the zeolites in the acidic form contributes to the better performance of these materials as hydrocarbon traps since the stabilization of the zeolites takes place. Moreover, the decrease of the surface acidity of the zeolites results in an increase of the Si/Al ratio, which contributes to the decrease of the water affinity for adsorption sites. Thus, the competition with hydrocarbon molecules in the exhaust for the adsorption sites is reduced which increases their trap efficiency. The stabilized H-ZSM-5 is the zeolite that showed the best performance with a propene offset temperature of 240 °C, which should be high enough for the three-way catalyst to carry out its role as catalytic converter.

Catalyzed addition of acid chlorides to alkynes by unmodified nano-powder magnetite: synthesis of chlorovinyl ketones, furans, and related cyclopentenone derivatives

Inexpensive and commercially available nano-powder magnetite is an excellent catalyst for the addition of acid chlorides to internal and terminal alkynes, yielding the corresponding chlorovinyl ketones in good yields. The process has been applied to the synthesis of 5-chloro-4-arylcyclopent-2-enones, 3-aryl-1H-cyclopenta[a]naphthalen-1-ones, and (E)-3-alkylidene-2,3-dihydro-1H-cyclopenta[a]naphthalen-1-ones, just by changing the nature of the starting acid chloride or the alkyne. All tested processes elapse with an acceptable or excellent regio- and stereo-selectivity. Moreover, the use of the iridium impregnated on magnetite catalyst permits the integration of the chloroacylation process with a second dehydrochlorination–annulation process to yield, in one-pot, 1-aryl-2,4-dialkylfurans in good yields, independently of the nature of the starting reagents, and including the heteroaromatic ones.

Influence of peroxometallic intermediaries present on polyoxometalates nanoparticles surface on the adipic acid synthesis

The cyclohexene oxidation by hydrogen peroxide catalysed by polyoxometalates (POM) has been shown as an adequate green route for the adipic acid synthesis. In this study, it has been demonstrated that POM's salts are effective catalysts for this reaction and how peroxopolyoxometalates intermediaries are the truly responsible species of the POM's salts catalytic activity and solubility. However, the latter can be reduced by calcining the catalyst previously. Polyoxomolybdates salts generally present a higher activity than polyoxotungstenates salts. Finally, it must be remarked the positive effect exerted by the acetic acid stabilising the peroxide of hydrogen against its decomposition.

Glyoxylic Acid versus Ethyl Glyoxylate for the Aqueous Enantio­selective Synthesis of α-Hydroxy-γ-Keto Acids and Esters by the N-Tosyl-(S a)-binam-l-prolinamide-Organocatalyzed Aldol Reaction

N-Tosyl-(S a)-binam-l-prolinamide is an efficient catalyst for the aqueous aldol reaction between ketones and glyoxylic acid, as the monohydrate or as an aqueous solution, or a 50% toluene solution of ethyl glyoxylate. These reactions led to the formation of chiral α-hydroxy-γ-keto carboxylic acids and esters in high levels of diastereo- and enantioselectivities (up to 97% ee), providing mainly anti aldol products. Only cyclopentanone and cyclohexane-1,4-dione afforded an almost 1:1 mixture of the syn/anti-diastereoisomers; however, the reaction between 4-phenylcyclohexanone and ethyl glyoxylate gave the corresponding syn,syn-product as the major diastereoisomer.

Platinum–rhodium–tin/carbon electrocatalysts for ethanol oxidation in acid media: effect of the precursor addition order and the amount of tin

Carbon-supported Pt x –Rh y –Sn z catalysts (x:y:z = 3:1:4, 6:2:4, 9:3:4) are prepared by Pt, Rh, and Sn precursors reduction in different addition order. The materials are characterized by X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy techniques and are evaluated for the electrooxidation of ethanol in acidic media by cyclic voltammetry, chronoamperometry, and anode potentiostatic polarization. The influence of both the order in which the precursors are added and the composition of metals in the catalysts on the electrocatalytic activity and physico-chemical characteristics of Pt x –Rh y –Sn z /C catalysts is evaluated. Oxidized Rh species prevail on the surface of catalysts synthesized by simultaneous co-precipitation, thus demonstrating the influence of synthesis method on the oxidation state of catalysts. Furthermore, high amounts of Sn in composites synthesized by co-precipitation result in very active catalysts at low potentials (bifunctional effect), while medium Sn load is needed for sequentially deposited catalysts when the electronic effect is most important (high potentials), since more exposed Pt and Rh sites are needed on the catalyst surface to alcohol oxidation. The Pt3–Rh1–Sn4/C catalyst prepared by co-precipitation is the most active at potentials lower than 0.55 V (related to bifunctional effect), while the Pt6–Rh2–Sn4/C catalyst, prepared by sequential precipitation (first Rh and, after drying, Pt + Sn), is the most active above 0.55 V.