Strength analysis of steel-concrete composite beams in combined bending and shear

Despite experimental evidences, the contributions of the concrete slab and composite action to the vertical shear strength of simply supported steel-concrete composite beams are not considered in current design codes, which lead to conservative designs. In this paper, the finite element method is used to investigate the flexural and shear strengths of simply supported composite beams under combined bending and shear. A three-dimensional finite element model has been developed to account for geometric and material nonlinear behavior of composite beams, and verified by experimental results. The verified finite element model is than employed to quantify the contributions of the concrete slab and composite action to the moment and shear capacities of composite beams. The effect of the degree of shear connection on the vertical shear strength of deep composite beams loaded in shear is studied. Design models for vertical shear strength including contributions from the concrete slab and composite action and for the ultimate moment-shear interaction ate proposed for the design of simply supported composite beams in combined bending and shear. The proposed design models provide a consistent and economical design procedure for simply supported composite beams.

Chemical analysis of powdered metallurgical slags by X-ray fluorescence spectrometry

Slag composition determines the physical and chemical properties as well as the application performance of molten oxide mixtures. Therefore, it is necessary to establish a routine instrumental technique to produce accurate and precise analytical results for better process and production control. In the present paper, a multi-component analysis technique of powdered metallurgical slag samples by X-ray Fluorescence Spectrometer (XRFS) has been demonstrated. This technique provides rapid and accurate results, with minimum sample preparation. It eliminates the requirement for a fused disc, using briquetted samples protected by a layer of Borax(R). While the use of theoretical alpha coefficients has allowed accurate calibrations to be made using fewer standard samples, the application of pseudo-Voight function to curve fitting makes it possible to resolve overlapped peaks in X-ray spectra that cannot be physically separated. The analytical results of both certified reference materials and industrial slag samples measured using the present technique are comparable to those of the same samples obtained by conventional fused disc measurements.

Galvanic corrosion of magnesium alloy AZ91D in contact with an aluminium alloy, steel and zinc

An investigation was carried out into the galvanic corrosion of magnesium alloy AZ91D in contact with zinc, aluminium alloy A380 and 4150 steel. Specially designed test panels were used to measure galvanic currents under salt spray conditions. It was found that the distributions of the galvanic current densities on AZ91D and on the cathodes were different. An insulating spacer between the AZ91D anode and the cathodes could not eliminate galvanic corrosion. Steel was the worst cathode and aluminium the least aggressive to AZ91D. Corrosion products from the anode and cathodes appeared to be able to affect the galvanic corrosion process through an alkalisation, passivation, poisoning effect or shortcut effect. (C) 2003 Elsevier Ltd. All rights reserved.

Effect of curve fitting parameters on quantitative analysis of Fe0.94O and Fe2O3 using XPS

The XPS peaks of Fe 3p for Fe2+ and Fe3+ in FeO and Fe2O3, respectively, have been measured and the effects of curve fitting parameters on interpretation of the data have been analysed. Firstly, the peak fit parameters, i.e. (1) the number of peaks to be deconvoluted, (2) the range of the peak for back ground subtraction, (3) straight line (Li) or the Shirley (Sh) background subtraction method, (4) GL ratio (the ratio of Gaussian and Lorentzian contribution to the peak shape) and (5) asymmetry factor (AS), are manually selected. Secondly, the standard peak fit parameters were systematically investigated. The peak shape was fitted to a Voigt function by changing the peak position, the peak height and the full width at half maximum (FWHM) to minimize the chi(2). The recommended peak positions and peak parameters for Fe2+ and Fe3+ in iron oxides have been determined. (c) 2006 Elsevier B.V. All rights reserved.

Effect of sample geometry on regression rate of the melting interface for carbon steel burned in oxygen

Promoted-ignition testing on carbon steel rods of varying cross-sectional area and shape was performed in high pressure oxygen to assess the effect of sample geometry on the regression rate of the melting interface. Cylindrical and rectangular geometries and three different cross sections were tested and the regression rates of the cylinders were compared to the regression rates of the rectangular samples at test pressures around 6.9 MPa. Tests were recorded and video analysis used to determine the regression rate of the melting interface by a new method based on a drop cycle which was found to provide a good basis for statistical analysis and provide excellent agreement to the standard averaging methods used. Both geometries tested showed the typical trend of decreasing regression rate of the melting interface with increasing cross-sectional area; however, it was shown that the effect of geometry is more significant as the sample's cross sections become larger. Discussion is provided regarding the use of 3.2-mm square rods rather than 3.2-mm cylindrical rods within the standard ASTM test and any effect this may have on the observed regression rate of the melting interface.