Effect of the preparation technique on the catalytic properties of mesoporous V-HMS for the oxidation of toluene

Various mesoporous catalysts with vanadium loadings between 0.5 and 6 V wt.% and surface areas around 1300 m(2)/g were synthesized using the isomorphous substitution (IS) and molecular designed dispersion (MDD) techniques. Their catalytic properties were tested using toluene as a model VOC in a fixed bed reactor at temperatures between 300 and 550 degrees C. It was found that during the oxidation of toluene, over V-HMS synthesized via IS, conversion of toluene mainly results in carbon oxides, benzene, benzaldehyde and water. Total conversion is greatly improved when the vanadium content is increased from around 1.5 to 3.0 wt.%, but an increase in the textural porosity (V-TEX/V-MESO) from 0.3 to 0.6 had no discernable effect on the conversion. This can be explained by the fact that a V-TEX/V-MESO as low as 0.3 is sufficient to facilitate the access of toluene into the framework confined mesopores without any molecular transport limitations. However, when using V-HMS synthesized by MDD, conversion of toluene is greatly improved when the V-TEX/ V-MESO ratio is increased from 0.1 to 0.6. This is because the diffusion limitations are minimized by this increase. V-HMS synthesized via MDD does not exhibit selectivity to benzaldehyde, favoring total oxidation to CO and CO2. This different oxidation mechanism can be explained in terms of location, accessibility and number of active species on the surface of the HMS support. (c) 2005 Elsevier Inc. All rights reserved.

Equilibrium swelling measurements of network and semicrystalline polymers in supercritical carbon dioxide using high-pressure NMR

The extent of swelling of cross-linked poly(dimethylsiloxane) and linear low-density poly(ethylene) in supercritical CO2 has been investigated using high-pressure NMR spectroscopy and microscopy. Poly(dimethylsiloxane) was cross-linked to four different cross-link densities and swollen in supercritical CO2. The Flory-Huggins interaction parameter, x, was found to be 0.62 at 300 bar and 45 degrees C, indicating that supercritical CO2 is a relatively poor solvent compared to toluene or benzene. Linear low-density poly(ethylene) was shown to exhibit negligible swelling upon exposure to supercritical CO2 up to 300 bar. The effect Of CO2 pressure on the amorphous region of the poly(ethylene) was investigated by observing changes in the H-1 T-2 relaxation times of the polymer. These relaxation times decreased with increasing pressure, which was attributed to a decrease in mobility of the polymer chains as a result of compressive pressure.

Comparisons of the structural and catalytic properties of Ti-HMS synthesized using the hydrothermal and molecular designed dispersion methods

Titanium containing wormhole-like mesoporous silicas, denoted Ti-HMS, synthesized both via the hydrothermal synthesis route and the post synthesis grafting technique, known as molecular designed dispersion, have been successfully applied in the gas phase oxidation of Toluene to CO and CO2. Selectivity towards CO2 for all catalysts, at temperatures between 400-600degreesC, was above 80%. Benzene and benzaldehyde were observed at temperatures above 450degreesC, but in very low concentrations. The conversion of toluene was shown to increase significantly when the V-TEX/N-MESO ratios were increased from 0.07 to 0.84. No significant difference in catalytic activity was observed for catalysts prepared via the different synthesis techniques. The catalytic activity also depends on the concentration of tetrahedrally coordinated titanium atoms and not on the total concentration of titanium in the catalyst.