Morphology and properties of thermoplastic polyurethane nancomposites incorporating hydrophilic layered silicates

Hydrophilic layered silicate/polyurethane nanocomposites were prepared via twin screw extrusion and solvent casting. Good dispersion and delamination was achieved-regardless of processing route, illustrating that the need for optimised processing conditions diminishes when there is a strong driving for de for intercalation between the polymer and organosilicate. Evidence for altered polyurethane microphase morphology in the nanocomposites was provided by DMTA and DSC. WAXD results suggested that the appearance of an additional high temperature melting endotherm in some melt-compounded nanocomposites was not due to the formation of a second crystal polymorph, but rather due to more well-ordered hard microdomains. Solvent casting was found to be the preferred processing route due to the avoidance of polyurethane and surfactant degradation associated with melt processing. While tensile strength and elongation were not improved on organosilicate addition, large increases in stiffness were observed. At a 7 wt% organosilicate loading, a 3.2-fold increase in Young's modulus was achieved by solvent casting. The nanocomposites also displayed higher hysteresis and permanent set. (C) 2004 Elsevier Ltd. All rights reserved.

Visoelastic studies on thermoplastic polyurethane nanocomposites using a nano-hardness tester

The viscoelastic behaviour of a range of polyurethane thermoplastic elastomer montmorillonite nanocomposites has been studied using a nanohardness tester. For softer Shore hardness 80A materials, the introduction of the organo-clay increased the creep strain obtained while the nano-indentor was held at constant load. The increase in creep strain was greatest for materials containing an organo-clay modified with a more hydrophilic quaternary alkylammonium surfactant and with higher loadings of the hydrophilic organo-clay. This suggested the effect might be due to a plasticising effect of the excess surfactant. For the harder Shore hardness 55D materials, the addition of the organo-clays produced only a small decrease in the creep strain, probably due to the interconnected hard domains in this material.