Annealing of ion implanted gallium nitride

In this paper, we examine Si and Te ion implant damage removal in GaN as a function of implantation dose, and implantation and annealing temperature. Transmission electron microscopy shows that amorphous layers, which can result from high-dose implantation, recrystallize between 800 and 1100 °C to very defective polycrystalline material. Lower-dose implants (down to 5 × 1013 cm – 2), which are not amorphous but defective after implantation, also anneal poorly up to 1100 °C, leaving a coarse network of extended defects. Despite such disorder, a high fraction of Te is found to be substitutional in GaN both following implantation and after annealing. Furthermore, although elevated-temperature implants result in less disorder after implantation, this damage is also impossible to anneal out completely by 1100 °C. The implications of this study are that considerably higher annealing temperatures will be needed to remove damage for optimum electrical properties. ©1998 American Institute of Physics.

Investigation of the role of cadmium sulfide in the surface passivation of lead sulfide quantum dots

Surface passivation of PbS nanocrystals (NC), resulting in strong photoluminescence, can be achieved by the introduction of CdS precursors. The role of CdS in the surface passivation of PbS NCs is uncertain, as the crystalline structure of CdS and PbS are different, which should impede effective epitaxial overgrowth. Absorption spectroscopy is used to show that the CdS precursors strongly interact with the PbS NC surface. Electron microscopy reveals that the introduction of CdS precursors results in an increased particle size, consistent with overcoating. However, we also find the process to be highly non-uniform. Nevertheless, evidence for epitaxial growth is found, suggesting that effective surface passivation may be possible.

Selectively excited luminescence and magnetic circular dichroism of Cr4+-doped YAG and YGG

Site selective luminescence and magnetic circular dichroism experiments on Cr4+-doped yttrium aluminum garnet and yttrium gallium garnet have been made at low temperature. The spectral assignments for these near-IR lasing materials have been made using experimental data and ligand field calculations guided by the known geometry of the lattices. [S0163-1829(99)07003-4].