Synthesis, characterization, and electrical conduction of 10 mol% Dy2O3 doped CeO2 ceramics

Well-densified 10 mol% Dy2O3-doped CeO2 (20DDC) ceramics with average grain sizes of similar to 0.12-1.5 mu m were fabricated by pressureless sintering at 950-1550 degrees C using a reactive powder thermally decomposed from a carbonate precursor, which was synthesized via a carbonate coprecipitation method employing nitrates as the starting salts and ammonium carbonate as the precipitant. Electrical conductivity of the ceramics, measured by the dc three-point impedance method, shows a V-shape curve against the average grain size. The sample with the smallest grain size of 0.12 mu m exhibits a high conductivity of similar to 10(-1.74) S/cm at the measurement temperature of 700 degrees C, which is about the same conduction level of the micro-grained 10 mol% Sm2O3- or Gd2O3-doped CeO2, two leading electrolyte materials. (c) 2004 Elsevier Ltd. All rights reserved.

Muscle fiber conduction velocity of the upper trapezius muscle during dynamic contraction of the upper limb in patients with chronic neck pain

The purpose of this study was to compare average muscle fiber conduction velocity (CV) and its changes over time in the upper trapezius muscle during a repetitive upper limb task in people with chronic neck pain and in healthy controls. Surface EMG signals were detected bilaterally from the upper trapezius muscle of 19 patients and nine healthy controls using linear adhesive arrays of four electrodes. Subjects were asked to tap their hands in a cyclic manner between targets positioned mid-thigh and 120 degrees of shoulder flexion, to the beat of a metronome set at 88 beats/min for up to 5 min. Muscle fiber CV and instantaneous mean power spectral frequency were estimated for each cycle at the time instant corresponding to 90 degrees of shoulder flexion. Average muscle fiber CV of the upper trapezius muscle was higher in people with chronic neck pain (mean +/- SE, 4.8 +/- 0.1 m/s) than in control subjects (4.4 +/- 0.1 m/s; P