NMR study of the gamma radiolysis of poly(dimethyl siloxane) under vacuum at 303 K

The structural changes which occur on the gamma -radiolysis of poly(dimethyl siloxane) (PDMS) under vacuum at 303 K have been investigated using Si-29 and C-13 NMR. New structural units consistent with main chain scission and crosslinking through both H-linking and Y-linking reactions have been identified. The results obtained at various absorbed doses have been used to calculate the G-values for scission and crosslinking. G-values for scission of G(S) = 1.3 +/- 0.2, for H-linking of G(D-CH2-R) = 0.34 +/- 0.02 and for Y-Linking of G(Y) = 1.70 +/- 0.09 were obtained for radiolysis under vacuum at 303 K. Thus crosslinking predominates over scission for radiolysis of PDMS under these conditions, and, by contrast with previous studies, Y-links have been shown to be the predominant form of crosslinks. (C) 2001 Elsevier Science Ltd. All rights reserved.

Water sorption into poly[(2-hydroxyethyl methacrylate)-co-(1-vinyl-2-pyrrolidone]at 310 K

Poly(2-hydroxyethyl methacrylate) and copolymers of 2-hydroxyethyl methacrylate (HEMA) and 1-vinyl-2-pyrrolidone (VP) in the form of cylindrical samples (approximate to8mm x 20mm) have been prepared and the sorption of water into these cylinders has been studied by the mass-uptake methods and by magnetic-resonance imaging. The equilibrium water contents for the cylinders were found to vary systematically with the copolymer composition. Diffusion of water into the cylinders was found to follow Fickian behaviour for cylinders with high HEMA contents, with the diffusion coefficients obtained from mass-uptake studies dependent on the copolymer composition, varying from 1.7 x 10(-11) m(2) s(-1) for poly(HEMA) to 2.0 x 10(-11) m(2) s(-1) for poly(HEMA-co-VP) with a composition of 1:1. However, NMR-imaging studies showed that, while the profiles of the water diffusion fronts for cylinders with high HEMA contents were Fickian, that for the 1:1 copolymer was not and indicated that the mechanism was Case III. The polymers which were rich in VP were characterized by a water-sorption process which follows Case-III behaviour. (C) 2003 Society of Chemical Industry.

NMR imaging of the diffusion of water at 310 K into semi-IPNs of PEM and Poly(HEMA-co-THFMA)

Magnetic resonance imaging has been used to monitor the diffusion of water at 310 K into a series of semi-IPNs of poly(ethyl methacrylate), PEM, and copolymers of 2-hydroxyethyl methacrylate, HEMA, and tetrahydrofurfuryl methacrylate, THFMA. The diffusion was found to be well described by a Fickian kinetic model in the early stages of the water sorption process, and the diffusion coefficients were found to be slightly smaller than those for the copolymers of HEMA and THFMA, P(HEMA-co-THFMA), containing the same mole fraction of HEMA in the matrix. A second stage sorption process was identified in the later stage of water sorption by the PEM/PTHFMA semi-IPN and for the systems containing a P(HEMA-co-THFMA) component with a mole fraction HEMA of 0.6 or less. This was characterized by the presence of Water near the surface of the cylinders with a longer NMR T-2 relaxation time, which would be characteristic of mobile water, such as water present in large pores or surface fissures. The presence of the drug chlorhexidine in the polymer matrixes at a concentration of 5.625 wt % was found not to modify the properties significantly, but the diffusion coefficients for the water sorption were systematically smaller when the drug was present.

NMR imaging of the diffusion of water at 310 K into poly[(2-hydroxyethyl methacrylate)-co-(tetrahydrofurfuryl methacrylate)] containing vitamin B12 or aspirin

The ingress of water into copolymers of 2-hydroxyethyl methacrylate (HEMA) and tetrahydrofurfuryl methacrylate (THFMA) loaded with either one of two model drugs, ie vitamin B-12 or aspirin, was studied at 310 K using three-dimensional nuclear magnetic resonance (3D NMR) imaging. The poly(HEMA) was loaded with 5 wt% of the drugs. From the imaging profiles it was observed that incorporation of vitamin B-12 into the polymers rich in HEMA resulted in crack formation at the interface between the rubbery region and the glassy core on sorption of water, although these cracks were 'healed' behind the diffusion front. However, for the copolymers with low HEMA contents and for those containing aspirin, no evidence for similar crack formation was found. For the copolymers loaded with 5 wt% of aspirin or vitamin B-12 the values of the water diffusion coefficients, determined by curve-fitting the relative water concentration profiles from magnetic resonance imaging (MRI) measurements, were found to be smaller than those obtained from a mass uptake study. (C) 2004 Society of Chemical Industry.

Effect of temperature on the gamma-radiolysis of poly(tetrafluoroethylene-co-perfluoromethyl vinyl ether)

The effect of irradiation temperature on the polymer properties was investigated for the fluoroelastomer poly(tetrafluoroethylene-co-perfluoromethylvinyl ether) (TFE/PMVE). TFE/PMVE samples were gamma-irradiated to 150 kGy at temperatures ranging from 77 K to 373 K. Analysis of the sol/gel behaviour, tensile properties, and glass transition temperatures indicated that crosslinking commenced in the temperature range 195 to 263 K, for a dose of 150 kGy. The latter temperature was 13 K below the glass transition temperature. Crosslinking remained relatively constant to higher temperatures. Chain scission reactions were found to occur well below the glass transition temperature and increased at higher temperatures. The optimum temperature for the radiation crosslinking of TFE/PMVE, for the temperatures investigated, was 263 K. (C) 1998 Elsevier Science Ltd. All rights reserved.

Thermal and mechanical properties of radiation crosslinked poly(tetrafluoroethylene-co-perfluoromethyl vinyl ether)

The gamma-radiolysis of poly(tetrafluoroethylene-co-perfluoromethyl vinyl ether) (TFE/PMVE) was investigated using chemical and mechanical analyses. The polymer was found to form an insoluble network with a dose of gelation of 15.8 kGy. Tensile and glass transition temperature measurements indicated the predominance of crosslinking, with optimal elastomeric properties reached in the dose range of 120 to 200 kGy. Photoacoustic FTIR spectroscopy CPAS) showed the formation of new carboxylic acid end groups on irradiation. These new end groups were shown to decrease the thermal oxidative stability of the crosslinked network as determined by thermal gravimetric analysis. Electron spin resonance (ESR) studies of the polymer at 77 K indicated the presence of radical precursors. A G-value of 1.1 was determined for radical production at 77 K. Comparison of radical concentrations for a copolymer with a different mole ratio of PMVE, indicated that the PMVE units contribute to scission reactions. (C) 1998 Elsevier Science Ltd. All rights reserved.

The use of crosslinking promoters in the gamma-radiolysis of poly(tetrafluoroethylene-co-perfluoromethylvinyl ether). I

Incorporation of 1 wt % of triallyl isocyanurate (TAIC) significantly enhanced the radiation crosslinking of the perfluoroelastomer, poly(tetrafluoroethylene-co-perfluoromethylvinyl ether) (TFE/PMVE). The dose for gelation was lowered by 70% with the presence of TAIC. The additive also improved the tensile properties of TFE/ PMVE both before and after crosslinking by irradiation. Higher radical yields were obtained with the presence of TAIC at 77 K, indicating the crosslinking promoter was acting as a radical trap. ESR studies showed that radiolysis of TAIC and subsequent photobleaching cleaved an allyl branch from the ring structure. Upon thermal annealing, an allyl radical on the TAIC molecule was observed. (C) 1999 John Wiley & Sons, Inc.

Miscibility and specific interactions in blends of poly(4-vinylphenol) and poly(2-ethoxyethyl methacrylate)

The properties of the hydrogen-bonded polymer blends of poly(4-vinylphenol) and poly(2-ethoxyethyl methacrylate) are presented. Spectroscopic techniques such as C-13 solid-state NMR and FT-IR are used to probe specific interactions of the blends at various compositions. Spectral features from both techniques revealed that site-specific interactions are present, consistent with a significant degree of mixing of the blend components. Changes in chemical shift and line shape of the phenolic carbon and carbonyl resonances in the C-13 CPMAS spectra of the blends as a function of composition are interpreted as resulting from changes in the relative intensities of two closely overlapped signals. A quantitative measure of hydrogen-bonded carbonyl groups using C-13 NMR has been obtained which agreed well with the results from FT-IR analyses. It is also shown that C-13 NMR can be used to measure the fraction of hydroxyl groups associated with carbonyl groups, which was not possible previously using FT-IR due to extensive overlapping of bands in the hydroxyl stretching region. The results of measurements of H-1 T-1 and 1H T-1 rho indicate that PVPh and PEEMA are intimately mixed on a scale less than 2-3 nm.

The radiation chemistry of poly(dimethylsiloxane)

The radiation chemistry of poly(dimethyl siloxane) has been investigated with respect to identification of the nature of the small molecule chain scission products. Low molecular weight linear and cyclic products have been identified through the use of Si-29 solution NMR, GPC and MALDI-TOF mass spectrometry. It has been suggested that the low molecular weight cyclic products are formed by back-biting depolymerization reactions.

Metabolic and kinetic analysis of poly(3-hydroxybutyrate) production by recombinant Escherichia coli

A quantitatively repeatable protocol was developed for poly(3-hydroxybutyrate) (PHB) production by Escherichia coli XL1-Blue (pSYL107). Two constant-glucose fed-batch fermentations of duration 25 h were carried out in a 5-L bioreactor, with the measured oxygen volumetric mass-transfer coefficient (k(L)a) held constant at 1.1 min(-1). All major consumption and production rates were quantified. The intracellular concentration profiles of acetyl-CoA (300 to 600 mug.g RCM-1) and 3-hydroxy-butyryl-CoA (20 to 40 mug.g RCM-1) were measured, which is the first time this has been performed for E. coli during PHB production. The kinetics of PHB production were examined and likely ranges were established for polyhydroxyalkanoate (PHA) enzyme activity and the concentration of pathway metabolites. These measured and estimated values are quite similar to the available literature estimates for the native PHB producer Ralstonia eutropha. Metabolic control analysis performed on the PHB metabolic pathway showed that the PHB flux was highly sensitive to acetyl-CoA/CoA ratio (response coefficient 0.8), total acetyl-CoA + CoA concentration (response coefficient 0.7), and pH (response coefficient -1.25). It was less sensitive (response coefficient 0.25) to NADPH/NADP ratio. NADP(H) concentration (NADPH + NADP) had a negligible effect. No single enzyme had a dominant flux control coefficient under the experimental conditions examined (0.6, 0.25, and 0.15 for 3-ketoacyl-CoA reductase, PHA synthase, and 3-ketothiolase, respectively). In conjunction with metabolic flux analysis, kinetic analysis was used to provide a metabolic explanation for the observed fermentation profile. In particular, the rapid onset of PHB production was shown to be caused by oxygen limitation, which initiated a cascade of secondary metabolic events, including cessation of TCA cycle flux and an increase in acetyl-CoA/CoA ratio. (C) 2001 John Wiley & Sons. Inc. Biotechnol Bioeng 74: 70-80, 2001.

NMR characterization of blends of poly(hydroxybutyrate-co-hydroxyvalerate) with poly(vinyl acetate)

The extent of mixing in blends of poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) (27% HV) and poly(vinyl acetate) (PVAc) has been measured using a number of different techniques, principally solid-state NMR. Differential scanning calorimetry DSC measurements indicated effective mixing of the polymer chains on a scale of several nanometres. The results of H-1 T-1 and H-1 T-1rho. measurements confirm intimate mixing of the chains. A change on blending in the H-1 T-1rho, and the H-1 NMR line width of the signal from the protons of PVAc was consistent with an increase in the amplitude and frequency of motion of this component. The PVAc chains reside within the inter-lamellar space, as confirmed by spin diffusion measurements after H-1 T-1rho preparation. (C) 2003 Society of Chemical Industry.

NMR imaging of water sorption into poly(hydroxyethyl methacrylate-co-tetrahydrofurfuryl methacrylate)

The diffusion of water into a series of hydroxyethyl methacrylate, HEMA, copolymers with tetrahydrofurfuryl methacrylate, THFMA, has been studied over a range of copolymer compositions using NMR imaging analyses. For polyHEMA the diffusion was found to be consistent with a Fickian model. The mass diffusion coefficient of water in polyHEMA at 37 degreesC was determined from the profiles of the diffusion front to be 1.5 x 10(-11) m(2) s(-1), which is less than the value based upon mass uptake, 2.0 x 10(-11) m(2) s(-1). The profiles of the water diffusion front obtained from the NMR images showed that stress was induced at the interface between the rubbery and glassy regions which led to formation of small cracks in this region of the glassy matrix of polyHEMA and its copolymers with mole fractions of HEMA greater than 0.6. Water was shown to be able to enter these cracks forming water pools. For copolymers of HEMA and THFMA with mole fractions of HEMA less than 0.6 the absence of cracks was attributed to the ability of the THFMA sequences to undergo stress relaxation by creep.

An ESR study on gamma-irradiated poly(vinyl alcohol)

The formation of radicals in poly(vinyl alcohol), PVA, powder irradiated at 77 K by gamma -rays and the transformations of these radicals during photolysis with visible wavelengths and on thermal annealing have been studied. After irradiation a four-line ESR spectrum was observed. It was assigned to a triplet of the C-alpha-radical (38%), with a splitting of 3.27 mT, superimposed on a doublet (62%) with a splitting of 2.7 mT. The doublet appears to be composed of two radicals, one of which is photo-bleachable (58%) and the other which is not photo-bleachable (42%). This suggests that the latter radical is a neutral radical. The photo-bleachable component of the doublet has been assigned to a carbonyl anion radical. but the second doublet due to a neutral radical is unassigned. The total G-value for formation of radicals at 77 K was found to be 2.41 +/- 0.03. Upon illumination with visible light, the anion radicals were removed and the doublet components or the spectrum diminished in intensity, while the three-line spectrum of the C-alpha-radical became more clearly visible. This transition was due to the photo-detachment of electrons from traps which were proposed to be located on carbonyl groups in the polymer resulting from incomplete hydrolysis of the vinyl acetate. The photo-decay of the anion radicals could be satisfactorily described by a two-stage process. The first stage comprised the decay of approximately 80% of the anion radicals present, while the second stage was associated with the decay of the remaining 20%. Subsequent thermal annealing of a photolysed sample to 290 K led to a change in the shape of the spectrum to form a more clearly defined triplet, As the doublet of the neutral radical decays on thermal annealing between 150 and 250K, the C-alpha-radical is formed. (C) 2001 Elsevier Science Ltd. All rights reserved.