Enhanced optical properties of the GaAsN/GaAs quantum-well structure by the insertion of InAs monolayers

Microstructural and optical properties of InAs-inserted and reference single GaAsN/GaAs quantum-well (QW) structures grown by metalorganic chemical vapor deposition were investigated using cross-sectional transmission electron microscopy and photoluminescence (PL). Significant enhancement of PL intensity and a blueshift of PL emission were observed from the InAs-inserted GaAsN/GaAs QW structure, compared with the single GaAsN/GaAs QW structure. Strain compensation and In-induced reduction of N incorporation are suggested to be two major factors affecting the optical properties. (C) 2004 American Institute of Physics.

Preparation of high purity ZnO nanobelts by thermal evaporation of ZnS

High purity one-dimensional ZnO nanobelts were synthesized by thermally evaporating commercial ZnS powders in a hydrogen-oxygen mixture gas at 1050 degrees C. It was found that these ZnO nanobelts had a single crystal hexagonal wurtzite structure growing along the [0001] direction. They had a rectangle-shaped cross-section with typical widths of 20 to 100 nanometers and lengths of up to hundreds of micrometers with lattice constants of a = 0.325 nm and c = 0.520 nm. The self-catalytic hydrogen-oxygen assisted growth of ZnO nanobelt is discussed. The photoluminescence (PL) characterization of the ZnO nanobelts shows strong near-band UV emission (about 383 nm) and one broad peak at 501 nm, which indicates that the ZnO nanobelts have good potential application in optoelectronic devices.