The effects of J-gate potential and interfaces on donor exchange coupling in the Kane quantum computer architecture

We calculate the electron exchange coupling for a phosphorus donor pair in silicon perturbed by a J-gate potential and the boundary effects of the silicon host geometry. In addition to the electron-electron exchange interaction we also calculate the contact hyperfine interaction between the donor nucleus and electron as a function of the varying experimental conditions. Donor separation, depth of the P nuclei below the silicon oxide layer and J-gate voltage become decisive factors in determining the strength of both the exchange coupling and hyperfine interaction-both crucial components for qubit operations in the Kane quantum computer. These calculations were performed using an anisotropic effective-mass Hamiltonian approach. The behaviour of the donor exchange coupling as a function of the parameters varied in this work provides relevant information for the experimental design of these devices.

Microanalysis of quenched and self-extinguished aluminium rods burned in oxygen

Promoted ignition tests and quench tests have been conducted and analysed for 3.2 mm aluminum rods in 99.995% oxygen. Tests have been conducted in oxygen pressures varying from 538 kPa to 773 kPa. Samples that self-extinguished or were quenched were selected for further analysis. The microstructure of the selected samples were analysed by electron microscopy, using energy dispersive spectrometry and electron back-scatter techniques, to identify and visualize, respectively, the species present. The grain structures of these samples were etched, viewed and photographed under polarized light by an optical microscope. From the micrographs produced by the post-test analysis, clearly defined boundaries between the oxide and the melted and resolidified metal have been observed. In both the melted and resolidified metal and the oxide layer, significant numbers of gas bubbles, solid inclusions and several diffuse oxide bubbles have been captured during the cooling process. It is concluded that convective movement is occurring within the molten drop and that analysis of quenched samples provides more useful information on the state of the burning droplet than samples allowed to cool slowly to room temperature. Recommendations are made regarding future investigations into aluminum burning, focusing on the transport of reactants through the liquid oxide layer.

Thermal stability of ion-implanted ZnO

Zinc oxide single crystals implanted at room temperature with high-dose (1.4x10(17) cm(-2)) 300 keV As+ ions are annealed at 1000-1200 degrees C. Damage recovery is studied by a combination of Rutherford backscattering/channeling spectrometry (RBS/C), cross-sectional transmission electron microscopy (XTEM), and atomic force microscopy. Results show that such a thermal treatment leads to the decomposition and evaporation of the heavily damaged layer instead of apparent defect recovery and recrystallization that could be inferred from RBS/C and XTEM data alone. This study shows that heavily damaged ZnO has relatively poor thermal stability compared to as-grown ZnO which is a significant result and has implications for understanding results on thermal annealing of ion-implanted ZnO. (c) 2005 Americian Institute of Physics.

Preparation and catalytic properties of ZrO2-Al2O3 composite oxide supported nickel catalysts for methane reforming with carbon dioxide

ZrO2-Al2O3 composite oxides and supported Ni catalysts were prepared, and characterized by N-2 adsorption/desorption, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques. The catalytic performance and carbon deposition was also investigated. This mesoporous composite oxide is shown to be a promising catalyst support. An increase in the catalytic activity and stability of methane and carbon dioxide reforming reaction was resulted from the zirconia addition, especially at 5wt% ZrO2 content. The Ni catalyst supported ZrO2-Al2O3 has a strong resistance to sintering and the carbon deposition in a relatively long-term reaction.

Degradation of azo-dye Orange II by a photoassisted Fenton reaction using a novel composite of iron oxide and silicate nanoparticles as a catalyst

A novel nanocomposite of iron oxide and silicate, prepared through a reaction between a solution of iron salt and a dispersion of Laponite clay, was used as a catalyst for the photoassisted Fenton degradation of azo-dye Orange II. This catalyst is much cheaper than the Nafion-based catalysts, and our results illustrate that it can significantly accelerate the degradation of Orange II under the irradiation of UV light (lambda = 254 nm). An advantage of the catalyst is its long-term stability that was confirmed through using the catalyst for multiple runs in the degradation of Orange II. The effects of the H2O2 molar concentration, solution pH, wavelength and power of the LTV light, catalyst loading, and initial Orange II concentration on the degradation of Orange 11 were studied in detail. In addition, it was also found that discoloration of Orange 11 undergoes a faster kinetics than mineralization of Orange II and 75% total organic carbons of 0.1 mM Orange II can be eliminated after 90 min in the presence of 1.0 g of Fe-nanocomposite/L, 4.8 mM H2O2, and 1 x 8W UVC.

Long-term in vivo biostability of poly(dimethylsiloxane) / poly(hexamethylene oxide) mixed macrodiol-based polyurethane elastomers

The long-term biostability of a novel thermoplastic polyurethane elastomer (Elast-Eon(TM) 2 80A) synthesized using poly(hexamethylene oxide) (PHMO) and poly(dimethylsiloxane) (PDMS) macrodiols has been studied using an in vivo ovine model. The material's biostability was compared with that of three commercially available control materials, Pellethane(R) 2363-80A, Pellethane(R) 2363-55D and Bionate(R) 55D, after subcutaneous implantation of strained compression moulded flat sheet dumbbells in sheep for periods ranging from 3 to 24 months. Scanning electron microscopy, attenuated total reflectance-Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy were used to assess changes in the surface chemical structure and morphology of the materials. Gel permeation chromatography, differential scanning calorimetry and tensile testing were used to examine changes in bulk characteristics of the materials. The results showed that the biostability of the soft flexible PDMS-based test polyurethane was significantly better than the control material of similar softness, Pellethane(R) 80A, and as good as or better than both of the harder commercially available negative control polyurethanes. Pellethane(R) 55D and Bionate(R) 55D. Changes observed in the surface of the Pellethane(R) materials were consistent with oxidation of the aliphatic polyether soft segment and hydrolysis of the urethane bonds joining hard to soft segment with degradation in Pellethane(R) 80A significantly more severe than that observed in Pellethane(R) 55D. Very minor changes were seen on the surfaces of the Elast-Eon(TM) 2 80A and Bionate(R) 55D materials. There was a general trend of molecular weight decreasing with time across all polymers and the molecular weights of all materials decreased at a similar relative rate. The polydispersity ratio, M-w/M-n, increased with time for all materials. Tensile tests indicated that UTS increased in Elast-Eon(TM) 2 80A and Bionate(R) 55D following implantation under strained conditions. However, ultimate strain decreased and elastic modulus increased in the explanted specimens of all three materials when compared with their unimplanted unstrained counterparts. The results indicate that a soft, flexible PDMS-based polyurethane synthesized using 20% PHMO and 80% PDMS macrodiols has excellent long-term biostability compared with commercially available polyurethanes. (C) 2004 Elsevier Ltd. All rights reserved.

Overcoming the problem of loss-in-capacity of calcium oxide in CO2 capture

Calcium oxide has been identified to be one of the best candidates for CO2 capture in zero-emission power-generation systems. However, it suffers a well-known problem of loss-in-capacity (i.e., its capacity of CO2 capture decreases after it undergoes cycles of carbonation/decarbonation). This problem is a potential obstacle to the adoption of the new technologies. This paper proposes a method of fabricating a CaO-based adsorbent without the problem of loss-in-capacity. An adsorbent was fabricated using the method and tested on a thermogravimetric analyzer. It was shown that the sorbent attained a utilization efficiency of more than 90% after 9 cycles of carbonation/decarbonation.