Use of anion clay hydrotalcite to remove coloured organics from aqueous solutions

Anion clay hydrotalcite sorbents were prepared to investigate their adsorption capabilities in the removal of coloured organic substances from various aqueous systems. Anion clay hydrotalcite was found to be particularly effective at removing negatively charged species. Its excellent uptake levels of anionic species can be accounted for by its high surface area and anion exchange ability. That is, coloured substances can be adsorbed on the surface or enter the interlayer region of the clay by anion exchange. In the adsorption of Acid Blue 29 on the anion clay hydrotalcite, an equilibrium time of 1 h with dye removal exceeding 99% was obtained. The hydrotalcite was found to have an adsorption capacity marginally below that of commercial activated carbon. It should be noted that the spent sorbents can be regenerated easily by heating at 723 K to remove all adsorbed organics. The reused sorbents displayed greater adsorption capabilities than the newly prepared hydrotalcite. Hence, the anion clay hydrotalcite is easily recoverable and reusable such that it is a promising sorbent for environmental and purification purposes. (C) 2002 Elsevier Science B.V. All rights reserved.

Hydrothermal Synthesis of Layered Double Hydroxides (LDHs) from Mixed MgO and Al2O3: LDH Formation Mechanism

The formation of MgA1 layered double hydroxide (LDH) from physically mixed MgO and Al2O3 oxides upon hydrothermal treatment has been extensively investigated, and a formation mechanism has been proposed. We observed that the formation of LDH from the oxide mixture occurs upon heating at 110 degreesC. In general, LDH is the major component while the minor phases are mainly determined by the initial pH of the oxide suspension as well as the MgO/Al2O3 ratio. The neutrality in the initial suspension results in a minor Mg(OH)(2) as the impure phase, while the alkalinity in the suspension keeps some MgO unreacted throughout the whole hydrothermal treatment. We suggest that MgO and Al2O3 be hydrated into Mg(OH)(2) and Al(OH)(3), respectively, in the initial stage for all samples. We further Suggest that in the neutral condition Mg(OH)2 be quickly dissociated to Mg2+ and OH- which then deposit on the surface of Al(OH)(3)/Al2O3 to form a M-Al pre-LDH material. Al(OH)(4)(-), ionized from Al(OH)(3) in the basic solution, deposits on the surface of Mg(OH)(2)/MgO to result in a similar MgAl pre-LDH material. Such a pre-LDH material is then well crystallized upon continuous heating via the diffusion of metal ions in the solid lattice. Such a dissociation-deposition-diffusion mechanism via two pathways has been supported by the phase composition, morphological features of crystallites, and [Mg]/[Al] ratios on the crystallite surface. and presumably applied to the general formation of LDHs with various synthetic methods. Such as coprecipitation, homogeneous preparation, and reconstruction.

Layered double hydroxide nanomaterials as potential cellular drug delivery agents

This paper briefly reviews the recent progress in using layered double hydroxide (LDH) nanomaterials as cellular delivery agents. The advantages of LDHs as cellular delivery agents are summarized, and the processes of interaction/de-intercalation of anionic drugs (genes) into/from LDH nanoparticles are discussed. Then the cellular delivery of LDH-drug (gene) nanohybrids and subsequent intracellular processes are presumably proposed. At the end, some challenges and remarks for efficient delivery of drugs (genes) via LDH nanoparticles are provided to the best of our knowledge.

Dispersion and size control of layered double hydroxide nanoparticles in aqueous solutions

We report a simple but efficient method to prepare stable homogeneous suspensions containing monodispersed MgAl layered double hydroxide (LDH) nanoparticles that have wide promising applications in cellular drug ( gene) delivery, polymer/LDH nanocomposites, and LDH thin films for catalysis, gas separation, sensing, and electrochemical materials. This new method involves a fast coprecipitation followed by controlled hydrothermal treatment under different conditions and produces stable homogeneous LDH suspensions under variable hydrothermal treatment conditions. Moreover, the relationship between the LDH particle size and the hydrothermal treatment conditions ( time, temperature, and concentration) has been systematically investigated, which indicates that the LDH particle size can be precisely controlled between 40 and 300 nm by adjusting these conditions. The reproducibility of making the identical suspensions under identical conditions has been confirmed with a number of experiments. The dispersion of agglomerated LDH aggregates into individual LDH crystallites during the hydrothermal treatment has been further discussed. This method has also been successfully applied to preparing stable homogeneous LDH suspensions containing various other metal ions such as Ni2+, Fe2+, Fe3+, Co2+, Cd2+, and Gd3+ in the hydroxide layers and many inorganic anions such as Cl-, CO32-, NO3-, and SO42-.

Stable suspension of layered double hydroxide nanoparticles in aqueous solution

Seriously aggregated LDH agglomerates can be dispersed by a hydrothermal treatment into homogeneous stable suspensions that contain LDH particles in the range of 50−300 nm.