Eutectic grain size and strontium concentration in hypoeutectic aluminium-silicon alloys

Recently it has been shown that modification with strontium causes an increase in the size of eutectic grains. The eutectic grain size increases because there are fewer nucleation events, possibly due to the poisoning of phosphorus-based nuclei that are active in the unmodified alloy. The current paper investigates the effect of strontium concentration on the eutectic grain size. In the aluminium-10 wt.% silicon alloy used in this research, for fixed casting conditions, the eutectic grain size increases as the strontium concentration increases up to approximately 150ppm, beyond which the grain size is relatively stable. This critical strontium concentration is likely to differ depending on the composition of the base alloy, including the concentration of minor elements and impurities. It is concluded that processing and in-service properties of strontium modified aluminium-silicon castings are likely to be more stable if a minimum critical strontium concentration is exceeded. If operating below this critical strontium concentration exceptional control over composition and casting conditions is required. (c) 2005 Elsevier B.V. All rights reserved.

Variation in body size and sexual dimorphism across geographical and environmental space in the frogs Limnodynastes tasmaniensis and L. peronii

This study aimed to identify potential factors responsible for geographically structured morphological variation within the widespread Australian frogs Limnodynastes tasmaniensis Gunther and L. peronii Dumeril & Bibron. There was support for James's rule, and both latitude and present climate explained large amounts of the variation in body size and shape (particularly in L. peronii). There was also some support for the influence of several biogeographical barriers. Finally, both species were sexually dimorphic for body size and the degree of sexual size dimorphism (SSD) varied geographically. Climate was an important explanation for SSD variation in L. peronii, while latitude was most important for L. tasmaniensis. Geographical variations in sexual selection via male-male physical competition and climate-related resources are suggested as potential explanations for SSD variation in L. peronii. (C) 2004 The Linnean Society of London.

The effect of grain refinement and cooling rate on the hot tearing of wrought aluminium alloys

Using modifications to the Rappaz-Drezet-Gremaud hot tearing model, and using empirical equations developed for grain size and dendrite arm spacing (DAS) on the addition of grain refiner for a range of cooling rates, the effect of grain refinement and cooling rate on hot tearing susceptibility has been analysed. It was found that grain refinement decreased the grain size and made the grain morphology more globular. Therefore refining the grain size of an equiaxed dendritic grain decreased the hot tearing susceptibility. However, when the alloy was grain refined such that globular grain morphologies where obtained, further grain refinement increased the hot tearing susceptibility. Increasing the cooling decreased the grain size and made the grain morphology more dendritic and therefore increased the likelihood of hot tearing. The effect was particularly strong for equiaxed dendritic grain morphologies; hence grain refinement is increasingly important at high cooling rates to obtain more globular grain morphologies to reduce the hot tearing susceptibility.

An analysis of the relationship between grain size, solute content, and the potency and number density of nucleant particles

To be able to determine the grain size obtained from the addition of a grain refining master alloy, the relationship between grain size (d), solute content (defined by the growth restriction factor Q), and the potency and number density of nucleant particles needs to be understood. A study was undertaken on aluminium alloys where additions of TiB2 and Ti were made to eight wrought aluminum alloys covering a range of alloying elements and compositions. It was found from analysis of the data that d = a/(3)root pct TiB2 + b/Q. From consideration of the experimental data and from further analysis of previously published data, it is shown that the coefficients a and b relate to characteristics of the nucleant particles added by a grain refiner. The term a is related to the maximum density of active TiB2 nucleant particles within the melt, while b is related to their potency. By using the analysis methodology presented in this article, the performance characteristics of different master alloys were defined and the effects of Zr and Si on the poisoning of grain refinement were illustrated.

Microstructures and electrolytic properties of yttrium-doped ceria electrolytes: Dopant concentration and grain size dependences

The microstructures and electrolytic properties of YxCe1-xO2-x/2 (x = 0.10-0.25) electrolytes with average grain size in the range 90 nm-1.7 mu m were systematically investigated. Through detailed transmission electron microscopy characterization, nanosized domains were observed. The relationship of the domains, the doping level and grain sizes were determined, and their impacts on the electrolytic properties were systematically studied. It was found that the formation of domains has a negative impact on the electrolytic properties, so that electrolytic properties can be adjusted through careful control of domain formation, doping level and grain size. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.