The effect of the CaO/SiO2 ratio on the phase equilibria in the ZnO-“Fe2O3”-(PbO + CaO + SiO2) system in air: CaO/SiO2 = 0.1, PbO/(CaO + SiO2) = 6.2, and CaO/SiO2 = 0.6, PbO/(CaO + SiO2) = 4.3

Experimental studies on phase equilibria in the multi-component system PbO-ZnO-CaO-SiO2-FeO-Fe2O3 in air have been conducted to characterize the phase relations of a complex slag system used in the oxidation smelting of lead and in typical lead blast furnace sinters. The liquidus in two pseudoternary sections ZnO-Fe2O3-(PbO + CaO + SiO2) with the CaO/SiO2 weight ratio of 0.1 and the PbO/(CaO + SiO2) weight ratio of 6.2, and with CaO/SiO2 weight ratio of 0.6 and the PbO/(CaO + SiO2) weight ratio of 4.3, have been constructed.

Effect of curve fitting parameters on quantitative analysis of Fe0.94O and Fe2O3 using XPS

The XPS peaks of Fe 3p for Fe2+ and Fe3+ in FeO and Fe2O3, respectively, have been measured and the effects of curve fitting parameters on interpretation of the data have been analysed. Firstly, the peak fit parameters, i.e. (1) the number of peaks to be deconvoluted, (2) the range of the peak for back ground subtraction, (3) straight line (Li) or the Shirley (Sh) background subtraction method, (4) GL ratio (the ratio of Gaussian and Lorentzian contribution to the peak shape) and (5) asymmetry factor (AS), are manually selected. Secondly, the standard peak fit parameters were systematically investigated. The peak shape was fitted to a Voigt function by changing the peak position, the peak height and the full width at half maximum (FWHM) to minimize the chi(2). The recommended peak positions and peak parameters for Fe2+ and Fe3+ in iron oxides have been determined. (c) 2006 Elsevier B.V. All rights reserved.