Mode II delamination testing in uniaxially oriented PVC pipes

The mode II fracture toughness of an oriented PVC pipe was measured using an End Notched Flexure test geometry. A relatively low value of G(IIC) was found of 1.07 kJ m(-2) and this indicates that it is energetically more favorable for a crack to propagate in the tangential direction rather than radially through the wall of the pipe. Examination of the mechanism of crack advanced showed that although the crack was propagating globally in mode II, micro-cracks were opening ahead of the crack in mode I or in mixed mode. Growth of the crack occurred by linking up of these micro-cracks. This is similar to the mechanism found for mode II cracking in carbon fibre epoxy composites. (C) 2004 Kluwer Academic Publishers.

Lattice damage produced in GaN by swift heavy ions

Wurtzite GaN epilayers bombarded at 300 K with 200 MeV Au-197(16+) ions are studied by a combination of transmission electron microscopy (TEM) and Rutherford backscattering/channeling spectrometry (RBS/C). Results reveal the formation of near-continuous tracks propagating throughout the entire similar to1.5-mum-thick GaN film. These tracks, similar to100 Angstrom in diameter, exhibit a large degree of structural disordering but do not appear to be amorphous. Throughout the bombarded epilayer, high-resolution TEM reveals planar defects which are parallel to the basal plane of the GaN film. The gross level of lattice disorder, as measured by RBS/C, gradually increases with increasing ion fluence up to similar to10(13) cm(-2). For larger fluences, delamination of the nitride film from the sapphire substrate occurs. Based on these results, physical mechanisms of the formation of lattice disorder in GaN in such a high electronic stopping power regime are discussed. (C) 2004 American Institute of Physics.

Morphology and properties of thermoplastic polyurethane nancomposites incorporating hydrophilic layered silicates

Hydrophilic layered silicate/polyurethane nanocomposites were prepared via twin screw extrusion and solvent casting. Good dispersion and delamination was achieved-regardless of processing route, illustrating that the need for optimised processing conditions diminishes when there is a strong driving for de for intercalation between the polymer and organosilicate. Evidence for altered polyurethane microphase morphology in the nanocomposites was provided by DMTA and DSC. WAXD results suggested that the appearance of an additional high temperature melting endotherm in some melt-compounded nanocomposites was not due to the formation of a second crystal polymorph, but rather due to more well-ordered hard microdomains. Solvent casting was found to be the preferred processing route due to the avoidance of polyurethane and surfactant degradation associated with melt processing. While tensile strength and elongation were not improved on organosilicate addition, large increases in stiffness were observed. At a 7 wt% organosilicate loading, a 3.2-fold increase in Young's modulus was achieved by solvent casting. The nanocomposites also displayed higher hysteresis and permanent set. (C) 2004 Elsevier Ltd. All rights reserved.

Dispersion and size control of layered double hydroxide nanoparticles in aqueous solutions

We report a simple but efficient method to prepare stable homogeneous suspensions containing monodispersed MgAl layered double hydroxide (LDH) nanoparticles that have wide promising applications in cellular drug ( gene) delivery, polymer/LDH nanocomposites, and LDH thin films for catalysis, gas separation, sensing, and electrochemical materials. This new method involves a fast coprecipitation followed by controlled hydrothermal treatment under different conditions and produces stable homogeneous LDH suspensions under variable hydrothermal treatment conditions. Moreover, the relationship between the LDH particle size and the hydrothermal treatment conditions ( time, temperature, and concentration) has been systematically investigated, which indicates that the LDH particle size can be precisely controlled between 40 and 300 nm by adjusting these conditions. The reproducibility of making the identical suspensions under identical conditions has been confirmed with a number of experiments. The dispersion of agglomerated LDH aggregates into individual LDH crystallites during the hydrothermal treatment has been further discussed. This method has also been successfully applied to preparing stable homogeneous LDH suspensions containing various other metal ions such as Ni2+, Fe2+, Fe3+, Co2+, Cd2+, and Gd3+ in the hydroxide layers and many inorganic anions such as Cl-, CO32-, NO3-, and SO42-.

A bayesian artificial neural network method to characterise laminar defects using dynamic measurements

This paper reports on the development of an artificial neural network (ANN) method to detect laminar defects following the pattern matching approach utilizing dynamic measurement. Although structural health monitoring (SHM) using ANN has attracted much attention in the last decade, the problem of how to select the optimal class of ANN models has not been investigated in great depth. It turns out that the lack of a rigorous ANN design methodology is one of the main reasons for the delay in the successful application of the promising technique in SHM. In this paper, a Bayesian method is applied in the selection of the optimal class of ANN models for a given set of input/target training data. The ANN design method is demonstrated for the case of the detection and characterisation of laminar defects in carbon fibre-reinforced beams using flexural vibration data for beams with and without non-symmetric delamination damage.