Crystallography of zirconium hydrides in recrystallized Zircaloy-2 fuel cladding lay electron backscatter diffraction

Precipitation morphology and habit planes of the delta-phase Zr hydrides, which were precipitated within the a-phase matrix grains and along the grain boundaries of recrystallized Zircaloy-2 cladding tube, have been examined by electron backscatter diffraction (EBSD). Radially-oriented hydrides, induced by residual tensile stress, precipitated in the outside region of the cladding, and circumferentially-oriented hydrides in the stress-free middle region of the cladding. The most common crystallographic relationship for both types of the hydrides precipitated at the inter- and intra-granular sites was identical at (0001)(alpha) // {111}(delta), with {1017}(alpha) // {111}(delta) being the occasional exception only for the inter-granular radial hydrides. When tensile stress was loaded, the intra-granular hydrides tended to preferentially precipitate in the grains with circumferential basal pole textures. The inter-granular hydrides tended to preferentially precipitate on the grain faces opposite to tensile axis. The change of prioritization in the precipitation sites for the hydrides due to tensile stress could be explained in terms of the relaxation effect of constrained elastic energy on the terminal solid solubility of hydrogen at hydride precipitation.

Proton conductivity of mesoporous sol-gel zirconium phosphates for fuel cell applications

Zirconium phosphate has been extensively studied as a proton conductor for proton exchange membrane (PEM) fuel cell applications. Here we report the synthesis of mesoporous, templated sol-gel zirconium phosphate for use in PEM applications in an effort to determine its suitability for use as a surface functionalised, solid acid proton conductor in the future. Mesoporous zirconium phosphates were synthesised using an acid-base pair mechanism with surface areas between 78 and 177 m(2) g(-1) and controlled pore sizes in the range of 2-4 nm. TEM characterisation confirmed the presence of a wormhole like pore structure. The conductivity of such materials was up to 4.1 x 10(-6) S cm(-1) at 22degreesC and 84% relative humidity (RH), while humidity reduction resulted in a conductivity decrease by more than an order of magnitude. High temperature testing on the samples confirmed their dependence on hydration for proton conduction and low hydroscopic nature. It was concluded that while the conductivity of these materials is low compared to Nafion, they may be a good candidate as a surface functionalised solid acid proton conductor due to their high surface area, porous structure and inherent ability to conduct protons.

Enhanced glass-forming ability of a Zr-based bulk metallic glass with yttrium doping

A significant enhancement in glass formation in a newly developed Zr51Cu20.7Ni12Al16.3 alloy has been achieved by yttrium doping. With just 0.5 at.% yttrium doping, the critical diameter of the as-cast alloys for glass formation has been increased from 3 mm to at least 10 mm. In the undoped, large-sized alloys, massive oxygen stabilized crystalline phases are observed but disappear in yttrium doped alloys. Very small amounts of stable alpha-Y2O3 phases found in the yttrium doped alloys, and their negligible effect on the metallic glasses' properties, provide a superior solution to achieve metallic glasses with a high glass formability. (c) 2006 Elsevier B.V. All rights reserved.

Zirconium alloying and grain refinement of magnesium alloys

Factors that influence alloying zirconium to magnesium with a Mg-33.3Zr master alloy and the subsequent grain refinement are discussed based on a large number of experiments conducted at the laboratory scale (up to 30 kg of melt). It is shown that the zirconium particles released from the Zirmax(R) master alloy must be brought into thorough contact with the melt by an appropriate stirring process in order to attain a good dissolution of zirconium. The influence of alloying temperature on the recovery of zirconium was found to be negligible in the range from 680 to 780 degreesC. An ideal zirconium alloying process should end up with both high soluble and high total zirconium in the melt in order to achieve the best grain refinement in the final alloy. The distribution of zirconium in the final alloy microstructure is inhomogeneous and almost all of the zirconium in solution is concentrated in zirconium-rich cores in the microstructure.

A new zirconium-rich master alloy for the grain refinement of magnesium alloys

A new zirconium-rich magnesium-zirconium master alloy (designated AM-cast) has been developed by the CRC for Cast Metals Manufacturing in collaboration with Australian Magnesium Corporation for use as a grain refiner for magnesium alloys that do not contain aluminium. This work describes the microstructural characteristics of this new grain refiner and its grain refining ability when added to different magnesium alloys under various conditions (alloying temperature from 680 °C to 750 °C; weight of melt from 1 kg to 150 kg and sample thickness from 7 mm to 62 mm). Owing to its highly alloyable microstructure, AM-cast can be readily introduced into molten magnesium at any temperature when assisted by a few minutes of stirring or puddling. Little sludge has been found at the bottom of the alloying vessel in these trials due to the fine zirconium particles contained in the master alloy. The recovery of zirconium is normally in the range from 40% to 60% with respect to 1% zirconium addition as the master alloy. It is shown that this new master alloy is an excellent grain refiner for aluminium-free magnesium alloys.