Nanocrystalline zirconia as catalyst support in methanol synthosis

Nanocrystalline zirconia was synthesized and used as catalyst support for methanol synthesis. The nanocrystallite particles have new physical and textural properties which are critical in determining the catalytic performance. Nanocrystalline zirconia changes the electronic structure and affects the metal and support interactions on the catalyst. leading to facile reduction. intimate interaction between copper and zirconia, more corner defects and oxygen vacancies on the surface of the catalyst. All these changes are beneficial to the reaction of methanol synthesis from hydrogenation of CO2. As a result. higher conversion of CO2 and selectivity of methanol are achieved compared to the catalysts prepared by conventional co-precipitation method. (C) 2004 Elsevier B.V. All rights reserved.

Preparation and electrochemical properties of the layered material of LixVyO2 (x=0.86 and y=0.8)

Layered lithium-vanadium oxide with a composition of LixVyO2 (x = 0.86 and y = 0.8) was prepared by the hydrothermal reaction of V2O3 with LiOH center dot H2O at 180 degrees C. This material corresponds to a layered rhombohedral structure related to alpha-NaFeO2 in which the vanadium ions are disordered in alternate layers of octahedral 3a (0, 0, 0) and 3b (0, 0, 1/2) sites. The electrochemical properties of this Li0.86V0.8O2 material were investigated and compared with those of the layered Li0.96VO2 made by the conventional solid-state reaction. It was found that the electrochemical capacity and reversibility of the Li0.86V0.8O2 material are significantly improved compared to those of the Li0.96VO2 material; the reversible specific capacities of the Li/Li0.86V0.8O2 and Li/Li0.96VO2 systems are similar to 100 and similar to 50 mAh g(-1), respectively, under the current densities of 7.14 mA g(-1) over 20 charge-discharge cycles with a potential window of 1.50-4.50 V. Such a reversibility results from the structural stability of Li0.86V0.8O2, whereas the increase in the reversible specific capacity can be qualitatively interpreted in terms of the presence of vanadium vacancies in the structure. (c) 2005 The Electrochemical Society.

Role of nanosized zirconia on the properties of Cu/Ga2O3/ZrO2 catalysts for methanol synthesis

The introduction of mesoporous nanosize zirconia to the catalyst for methanol synthesis dedicates the nanosized catalyst and mesoporous duplicated properties. The catalyst bears the larger surface area, larger mesoporous volume and more uniform diameter, more surface metal atoms and oxygen vacancies than the catalyst prepared with the conventional coprecipitation method. The modification of microstructure and electronic effect could result in the change of the reduced chemical state and decrease of reducuction temperature of copper, donating the higher activity and methanol selectivity to the catalyst. The results of methanol synthesis demonstrate that the Cu+ is the optimum active site. Also, the interaction between the copper and zirconia shows the synergistic effect to fulfil the methanol synthesis.