Following injury, it is inherently difficult to completely restore the biomechanical properties of ligaments. Relatively little is known about the cellular mechanisms controlling ligament healing. Numerous studies have implicated fibroblast growth factors (FGFs) as key molecules during the initiation of the cellular proliferation, differentiation, migration and matrix deposition that characterise wound healing. While current surgical emphasis concentrates on growth factor intervention, the role of their cognate receptors (FGFRs) has largely been overlooked. Following transection of the medial collateral ligament (MCL) in rabbits, we examined FGFR expression over a 14-day healing period. Using semiquantitative RT-PCR, we observed a significant upregulation in FGFR2 expression after 3 days. By 7 days post injury, FGFR2 expression fell to basal levels in line with those of FGFR1 and 3, both of which remained unaffected by surgical transection. These results demonstrate a role for FGFR2 in fibroblast and endothelial cell proliferation in damaged ligament, and suggest a window for FGF therapy.

Effect of metal chlorides on the sintering and densification of hydroxyapatite adsorbent

This work is part of a series of studies dealing with the evaluation of the effects of major elements of solid waste, especially metallic oxides, nitrates, sulfates, and chlorides, on the sintering and the densification of calcium hydroxyapatite (Ca-HAP) adsorbent. The effects of chloride salts of potassium (KCl) and zinc (ZnCl2) on sintering and densification of Ca-HAP were studied using surface area reduction and shrinkage measurements. The addition of KCl (2% w/w) activated the sintering process by bringing a swift reduction in surface area and lowering the densification temperature. However, a low final densification was achieved. Increasing the amount of this additive to 10% w/w further lowered the final densification and lowered the densification temperature of hydroxyapatite by 150 degrees C. On the other hand, the addition of 2 wt % of ZnCl2 deactivated the sintering process by slowing down the densification process and raising the densification temperature. However, the reduction of surface area was comparable to that of Ca-HAP. The densification rate contained two or more rate maxima indicating the additives (salts) bring multiple speeds in the densification process.