A rheological assessment of the effect of trace level Ni additions on the solidification of Sn-0.7Cu

The influence of trace level Ni additions on the eutectic solidification mode of Sn-0.7Cu has been studied using continuous torque experiments during solidification. The solid fraction at which resistance to paddle rotation at the thermal centre of the sample occurs is related to the spatial distribution of solid during solidification. The results indicate that a transition in solidification mode occurs in the range 0-300 ppm Ni. Growth occurs antiparallel to heat flow from near the mould walls in the Ni-free alloy, while equiaxed growth from distributed centres dominates in alloys containing at least 300 ppm Ni. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effects of boron on eutectic modification of hypoeutectic Al-Si alloys

The effects of boron on the eutectic modification and solidification mode of hypoeutectic Al-Si alloys have been studied adding different boride phases. The results show that boron does not cause modification of the eutectic silicon. Boron-containing samples display eutectic nucleation and growth characteristics similar to that of unmodified alloys. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Eutectic modification of Al-Si alloys with rare earth metals

The effects of different concentrations of individual additions of rare earth metals (La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) on eutectic modification in Al-10mass%Si has been studied by thermal analysis and optical microscopy. According to the twin-plane re-entrant edge (TPRE) and impurity induced twinning mechanism, rare earth metals with atomic radii of about 1.65 times larger than that of silicon, are possible candidates for eutectic modification. All of the rare earth elements caused a depression of the eutectic growth temperature, but only Eu modified the eutectic silicon to a fibrous morphology. At best, the remaining elements resulted in only a small degree of refinement of the plate-like silicon. The samples were also quenched during the eutectic arrest to examine the eutectic solidification modes. Many of the rare-earth additions significantly altered the eutectic solidification mode from that of the unmodified alloy. It is concluded that the impurity induced twinning model of modification, based on atomic radius alone, is inadequate and other mechanisms are essential for the modification process. Furthermore, modification and the eutectic nucleation and growth modes are controlled independently of each other.

The influence of strontium on porosity formation in Al-Si alloys

Strontium modification is known to alter the amount, characteristics, and distribution of porosity in Al-Si castings. Although many theories have been proposed to account for these effects, most can be considered inadequate because of their failure to resolve contradictions and discrepancies in the literature. In an attempt to critically appraise some of these theories, the amount, distribution, and morphology of porosity were examined in sand-cast plates of Sr-free and Sr-containing pure Al, Al-l wt pet Si, and Al-9 wt pet Si alloys. Statistical significance testing was used to verify apparent trends in the porosity data. No apparent differences in the amount, distribution, and morphology of porosity were observed between Sr-free and Sr-containing alloys with no or very small eutectic volume fractions. However, Sr modification significantly changed the amount, distribution, and morphology of porosity in alloys with a significant volume fraction of eutectic. ne addition of Sr reduced porosity in the hot spot region of the casting, and the pores became well dispersed and rounded. This result can be explained by considering the combined effect of the casting design and the differences in the pattern of eutectic solidification between unmodified and Sr-modified alloys.

Solidification mechanisms of unmodified and strontium-modified hypereutectic aluminium-silicon alloys

The effects of strontium on the solidi. cation mode of hypereutectic aluminium-silicon alloys have been studied. Samples were prepared from an aluminium-17wt% silicon-based alloy and strontium was added at several different concentrations. The development of the microstructure was investigated by cooling curve analysis, interrupted solidi. cation experiments and optical and scanning electron microscopy. It was found that nucleation of primary silicon is suppressed by additions of strontium. The suppressed nucleation results in supersaturation of the liquid prior to nucleation, and an increased growth rate after nucleation. As a result, the silicon crystals become less faceted and more dendritic with increasing strontium additions. Increasing the strontium concentration slightly refined the eutectic spacing and introduced a small amount of fibrous silicon. Electron back-scatter diffraction measurements were performed to determine the crystallographic relation between the primary and eutectic silicon phases. The eutectic silicon in the unmodified alloy does not have any crystallographic relationship with the primary silicon crystals. In contrast, the eutectic silicon crystals in the strontium-modified alloys often share an identical or twin relationship with nearby primary silicon crystals. The incidence of twinning within primary silicon crystals was relatively low and did not appear to increase with strontium additions.