The effect of grain refinement and silicon content on grain formation in hypoeutectic Al-Si alloys

The effect of increasing the amount of added grain refiner on grain size and morphology has been investigated for a range of hypoeutectic Al-Si alloys. The results show a transition in grain size at a silicon concentration of about 3 wt% in unrefined alloys; the grain size decreasing with silicon content before the transition, and increasing beyond the transition point. A change in morphology also occurs with increased silicon content. The addition of grain refiner leads to greater refinement for silicon contents below the transition point than for those contents above the transition point, while the transition point seems to remain unchanged. The slope of the grain size versus silicon content curve after the transition seems to be unaffected by the degree of grain refinement. The results are related to the competitive processes of nucleation and constitutional effects during growth and their impact on nucleation kinetics. (C) 1999 Elsevier Science S.A. All rights reserved.

Equiaxed solidification of Al-Si alloys

An experimental programme has been undertaken to determine which of the grain formation mechanisms of equiaxed crystals are dominant in the solidification of Al-Si foundry alloys. Small ingots were cast from alloys of varying silicon concentration with and without gauze barriers, using different types of mould materials and different mould preheats. The results show that two mechanisms of grain nucleation are operating. The first is a wall mechanism where crystals are nucleated either on or near the mould wall owing to thermal undercooling. The second is a constitutional supercooling mechanism where nucleants are activated in the constitutionally undercooled zone ahead of the advancing interface. As a consequence, the grain size decreases with increasing silicon content. However a transition in the growth mode occurs once a critical degree of constitutional undercooling is exceeded. This change in growth is accompanied by an increase in grain size. The transition point can be shifted with respect to solute content by changing the casting conditions, and a mechanism is proposed to explain this effect. MST/4109

Modeling the optical constants of AlxGa1-xAs alloys

The extension of Adachi's model with a Gaussian-like broadening function, in place of Lorentzian, is used to model the optical dielectric function of the alloy AlxGa1-xAs. Gaussian-like broadening is accomplished by replacing the damping constant in the Lorentzian line shape with a frequency dependent expression. In this way, the comparative simplicity of the analytic formulas of the model is preserved, while the accuracy becomes comparable to that of more intricate models, and/or models with significantly more parameters. The employed model accurately describes the optical dielectric function in the spectral range from 1.5 to 6.0 eV within the entire alloy composition range. The relative rms error obtained for the refractive index is below 2.2% for all compositions. (C) 1999 American Institute of Physics. [S0021-8979(99)00512-5].

Detection of lead(II) and silver(I) in aqueous solution using a piezoelectric device

The gold surface of a quartz crystal microbalance was modified by the attachment of silica particles derivatised with N-[(3-trimethoxysilyl)propyl] ethylenediaminetriacetic acid. The device was employed to study the kinetics of the interaction of aqueous solutions of lead(II) nitrate and silver(I) nitrate with the surface and for the selective separation of the metal ions.

On the use of trace additions of Sn to enhance sintered 2xxx series Al powder alloys

The mechanical properties of a typical sintered aluminium alloy (Al-4.4Cu-0.8Si-0.5Mg) have been improved by the simultaneous use of trace additions of Sn, high sintering temperatures and modified heat treatments. Tin increases densification, but the Sn concentration is limited to less than or equal to 0.1wt% because incipient melting occurs during solution treatment at higher Sn levels. A sintering temperature of 620 degrees C increases the liquid volume over that formed at the conventional 590 degrees C sintering temperature. However, the higher sintering temperature results in the formation of an embrittling phase which can be eliminated if solution treatment is incorporated into the sintering cycle (a modified TS heat treatment). These conditions produce a tensile strength of 375 MPa, an increase of nearly 20% over the unmodified alloy. (C) 1999 Elsevier Science S.A. All rights reserved.

Aluminium alloys - their physical and mechanical properties: Grain formation in AlSi7Mg0.35 foundry alloy at low superheat

Hypoeutectic AI-Si alloys represent the most widely used alloy system for cast aluminium applications. This system has a unique behaviour with respect to grain formation where an increase in silicon content results in a transition to larger grain sizes after a minimum at an intermediate concentration. As a result of the already large solute content, grain refinement by solute additions is inefficient and nucleant particles from the common aluminium grain refiners are not as effective as in wrought alloys. However, casting conditions, such as a low pouring temperature, that promote the formation of wall crystals tie. crystals nucleated in the thermally undercooled layer at or next to mould walls) are very effective in yielding a small grain size. This paper presents results of an investigation of the effect of low superheat and mould preheat temperature on grain size. It was found that pouring temperature controls the effectiveness of the wall mechanism while mould preheat has little effect until high preheat temperatures at which a large increase in grain size occurs. The observed changes in grain size are explained in terms of the balance between nucleation rate and survival rate of crystal nuclei resulting from changes in superheat and mould temperature.

Influence of Mg content on the microstructure and solid solution chemistry of Al-7%Si-Mg casting alloys during solution treatment

The solution treatment stage of the T6 heat-treatment of Al-7%Si-Mg foundry alloys influences microstructural features such as Mg2Si dissolution, and eutectic silicon spheroidisation and coarsening. Microstructural and microanalytical studies have been conducted across a range of Sr-modified Al-7%Si alloys, with an Fe content of 0.12% and Mg contents ranging from 0.3-0.7wt%. Qualitative and quantitative metallography have shown that, in addition to the above changes, solution treatment also results in changes to the relative proportions of iron-containing intermetallic particles and that these changes are composition-dependent. While solution treatment causes a substantial transformation of pi phase to beta phase in low Mg alloys (0.3-0.4%), this change is not readily apparent at higher Mg levels (0.6-0.7%). The pi to beta transformation is accompanied by a release of Mg into the aluminum matrix over and above that which arises from the rapid dissolution of Mg2Si. Since the level of matrix Mg retained after quenching controls an alloy's subsequent precipitation hardening response, a proper understanding of this phase transformation is crucial if tensile properties are to be maximised.

Corrosion mechanisms of magnesium alloys

The high strength to weight ratio of magnesium alloys makes them extremely attractive for applications in transport or aerospace technology. However, their corrosion behavior is a major issue and one reason why they are still not as popular as aluminum alloys. This papers reviews the corrosion mechanisms of magnesium and provides the basis for the design of new alloys with improved corrosion properties.

Dendrite coherency of Al-Si-Cu alloys

The dendrite coherency point of Al-Si-Cu alloys was determined by thermal analysis and rheological measurement methods by performing parallel measurements at two cooling rates for aluminum alloys across a wide range of silicon and copper contents. Contrary to previous findings, the two methods yield significantly different values for the fraction solid at the dendrite coherency point. This disparity is greatest for alloys of low solute concentration. The results from this study also contradict previously reported tl ends in the effect of cooling rate on the dendritic coherency point. Consideration of the results shows that thermal analysis is not a valid technique for the measurement of coherency. Analysis of the results from rheological testing indicates that silicon concentration has a dominant effect on grain size and dendritic morphology, independent of cooling rate and copper content, and thus is the factor that determines the fraction solid at dendrite coherency for Al-Si-Cu alloys.

Eutectic nucleation and growth in hypoeutectic Al-SI alloys at different strontium levels

The effects of different levels of strontium on nucleation and growth of the eutectic in a commercial hypoeutectic Al-Si foundry alloy have been investigated by optical microscopy and electron backscattering diffraction (EBSD) mapping by scanning electron microscopy (SEM). The microstructural evolution of each specimen during solidification was studied by a quenching technique at different temperatures and Sr contents. By comparing the orientation of the aluminum in the eutectic to that of the surrounding primary aluminum dendrites by EBSD, the eutectic formation mechanism could be determined. The results of these studies show that the eutectic nucleation mode, and subsequent growth mode, is strongly dependent on Sr level. Three distinctly different eutectic growth modes were found, in isolation or sometimes together, but different for each Sr content. At very low Sr contents, the eutectic nucleated and grew from the primary phase. Increasing the Sr level to between 70 and 110 ppm resulted in nucleation of independent eutectic grains with no relation to the primary dendrites. At a Sr level of 500 ppm, the eutectic again nucleated on and grew from the primary phase while a well-modified eutectic structure was still present. A slight dependency of eutectic growth radially from the mold wall opposite the thermal gradient was observed in all specimens in the early stages of eutectic solidification.

Modification-related porosity formation in hypoeutectic aluminum-silicon alloys

A series of aluminum-10 wt pet silicon castings were produced in sand molds to investigate the effect of modification on porosity formation. Modification with individual additions of either strontium or sodium resulted in a statistically significant increase in the level of porosity compared to unmodified castings. The increase in porosity with modification is due to the presence of numerous dispersed pores, which were absent in the unmodified casting. It is proposed that these pores form as a result of differences in size of the aluminum-silicon eutectic grains between unmodified and modified alloys. A geometric model is developed to show how the size of eutectic grains can influence the amount and distribution of porosity. Unlike traditional feeding-based models, which incorporate the effect: of microstructure on permeability, this model considers what happens when liquid is isolated from the riser and can no longer flow. This simple isolation model complements rather than contradicts existing theories on modification-related porosity formation and should be considered in the development of future comprehensive models.

Modeling of columnar-to-equiaxed transition in solidified Al-Si alloys

A Cellular-Automaton Finite-Volume-Method (CAFVM) algorithm has been developed, coupling with macroscopic model for heat transfer calculation and microscopic models for nucleation and growth. The solution equations have been solved to determine the time-dependent constitutional undercooling and interface retardation during solidification. The constitutional undercooling is then coupled into the CAFVM algorithm to investigate both the effects of thermal and constitutional undercooling on columnar growth and crystal selection in the columnar zone, and formation of equiaxed crystals in the bulk liquid. The model cannot only simulate microstructures of alloys but also investigates nucleation mechanisms and growth kinetics of alloys solidified with various solute concentrations and solidification morphologies.