Corrosion behaviour of a pressure die cast magnesium alloy

High pressure die casting is the most important production method for casting magnesium alloy components, and uniformity of appearance is an important criterion for acceptance of a component by customers. This paper investigates the influence of uniformity in surface appearance of diecast AZ91D plates on their corrosion behaviour. Through immersion, hydrogen collection and weight loss measurements it was found that corrosion is more likely to occur on the areas of the plate that appear to be darker, leading to a non-uniformly corroded surface. Microstructural analysis showed that the non-uniformity in appearance is related to a difference in the morphology and distribution of porosity across the surface of a diecast AZ91D plate. The darker areas of the surface are high in porosity which breaks the continuity of the beta-phase network and provides shortcut paths for corrosion from the surface to the interior of the casting. The brighter shiny areas of the surface are much less porous, with isolated pores being confined by corrosion resistant beta-precipitates thus reducing the corrosion rate.

Anatomy of ethylene-induced floral-organ abscission in Chamelaucium uncinatum (Myrtaceae)

Postharvest abscission of Geraldton waxflower (Chamelaucium uncinatum Schauer) flower buds and flowers is ethylene-mediated. Exposure of floral organs to exogenous ethylene (1 mu L L-1) for 6 h at 20 degrees C induced separation at a morphologically and anatomically distinct abscission zone between the pedicel and. oral tube. Flower buds with opening petals and flowers with a nectiferous hypanthium were generally more responsive to exogenous ethylene than were flower buds enclosed in shiny bracteoles and aged (senescing) flowers. The anatomy of abscission-zone cells did not change at sequential stages of floral development from immature buds to aged flowers. The zone comprised a layer of small, laterally elongated-to-rounded, closely packed and highly protoplasmic parenchyma cells. Abscission occurred at a two- to four-cell-wide separation layer within the abscission zone. The process involved degradation of the middle lamella between separation layer cells. Following abscission, cells on both the proximal and distal faces of the separation layer became spherical, loosely packed and contained degenerating protoplasm. Central vascular tissues within the surrounding band of separation layer cells became torn and fractured. For flower buds, bracteoles that enclose the immature floral tube also separated at an abscission zone. However, this secondary abscission zone appeared less sensitive to ethylene than the primary ( central). oral-tube abscission zone as bracteoles generally only completely abscised when exposed to 10 mu L L-1 ethylene for the longer period of 24 h at 20 degrees C. The smooth surfaces of abscised separation-layer cells suggest that hydrolase enzymes degrade the middle lamella between adjacent cell walls.