Modeling of hardening and softening processes in Mg alloys

The tensile deformation behavior of a range of supersaturated Mg-Al solid solutions and an as-cast magnesium alloy AM60 has been studied. The Mg-Al alloys were tested at room temperature while the alloy AM60 was tested in the temperature range 293-573 K. The differences in the deformation behavior of the alloys is discussed in terms of hardening and softening processes. In order to identify which processes were active, the stress dependence of the strain-hardening coefficient was assessed using Lukac and Balik's model of hardening and softening. The analysis indicates that hardening involves solid solution hardening and interaction with forest dislocations and non-dislocation obstacles such as second phase particles. Cross slip is not a significant recovery process in the temperature range 293-423 K. At temperatures between 473 and 523 K the analysis suggests that softening is controlled by cross slip and climb of dislocations. At temperatures above 523 K softening seems to be controlled by dynamic recrystallisation. (C) 2004 Elsevier B.V. All rights reserved.

Section thickness, macrohardness and yield strength in high-pressure diecast magnesium alloy AZ91

The yield strength of high-pressure diecast (hpdc) test bars of alloy AZ91 increases with decreasing section thickness while its hardness remains approximately constant. This behaviour is in contrast with that of the gravity cast alloy, whose hardness scales with the yield strength. Vickers hardness measured on the surface of hpdc test bars using increasing loads shows that the subsurface porosity layer usually found in hpdc material may gradually collapse under the indent, lowering the hardness. However, this is insufficient to explain the lack of correlation between hardness and yield strength. It is argued that the low strain-hardening rate of high-pressure diecast material leads to lower than expected hardness values. In addition, it is shown that the plastic zone under a macro indentation is largely contained by the softer core of the castings, rendering hardness insensitive to the casting thickness. It is concluded that macrohardness is too coarse a tool for a meaningful determination of the strength of hpdc material. (c) 2005 Elsevier B.V. All rights reserved.