Phase separation, porous structure, and cure kinetics in aliphatic epoxy resin containing hyperbranched polyester

Thermosetting blends of an aliphatic epoxy resin and a hydroxyl-functionalized hyperbranched polymer (HBP), aliphatic hyperbranched polyester Boltorn H40, were prepared using 4,4'-diaminodiphenylmethane (DDM) as the curing agent. The phase behavior and morphology of the DDM-cured epoxy/HBP blends with HBP content up to 40 wt% were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and scanning electron microscopy (SEM). The cured epoxy/HBP blends are immiscible and exhibit two separate glass transitions, as revealed by DMA. The SEM observation showed that there exist two phases in the cured blends, which is an epoxy-rich phase and an HBP-rich phase, which is responsible for the two separate glass transitions. The phase morphology was observed to be dependent on the blend composition. For the blends with HBP content up to 10 wt%, discrete HBP domains are dispersed in the continuous cured epoxy matrix, whereas the cured blend with 40 wt% HBP exhibits a combined morphology of connected globules and bicominuous phase structure. Porous epoxy thermosets with continuous open structures on the order of 100-300 nm were formed after the HBP-rich phase was extracted with solvent from the cured blend with 40 wt% HBP. The DSC study showed that the curing rate is not obviously affected in the epoxy/HBP blends with HBP content up to 40 wt %. The activation energy values obtained are not remarkably changed in the blends; the addition of HBP to epoxy resin thus does not change the mechanism of cure reaction of epoxy resin with DDM. (c) 2006 Wiley Periodicals, Inc.

Quantitative prediction of phase diagrams for polymer partitioning in aqueous two-phase systems

Published polymer distribution data for aqueous poly(ethylene glycol)/dextran mixtures have been reassessed to illustrate the feasibility of their quantitative characterization in terms of the Flory-Huggins theory of polymer thermodynamics. Phase diagrams predicted by this characterization procedure provide better descriptions of the experimental data than those based on an earlier, oversimplified treatment in similar terms. (C) 2003 Wiley Periodicals, Inc.

A new approach to the synthesis of nanocrystal conjugated polymer composites

A novel one pot process has been developed for the preparation of PbS nanocrystals in the conjugated polymer poly 2-methoxy,5-(2 ethyl-hexyloxy-p-phenylenevinylene) (MEH-PPV). Current techniques for making such composite materials rely upon synthesizing the nanocrystals and conducting polymer separately, and subsequently mixing them. This multi-step technique has two serious drawbacks: templating surfactant must be removed before mixing, and co-solvent incompatibility causes aggregation. In our method, we eliminate the need for an initial surfactant by using the conducting polymer to terminate and template nanocrystal growth. Additionally, the final product is soluble in a single solvent. We present materials analysis which shows PbS nanocrystals can be grown directly in a conducting polymer, the resulting composite is highly ordered and nanocrystal size can be controlled.

Screening, characterization and flocculating property of carbohydrate polymer from newly isolated Enterobacter cloacae WD7

A total of 188 carbohydrate polymer-producing bacterial strains were isolated from recycled sludge of five seafood processing plants. Among three selected isolates, identified as Enterobacter cloacae WD7, Enterobacter agglomerans WD50 and Pseudomonas alcaligenes WD22. E. cloacae WD7 generated a viscous culture broth exhibiting the highest flocculating activity and a crude polymer yield of 2.27 g/L after 3 days cultivation. Partial purification of this polymer was performed by precipitation with 95% ethanol, dialysis and freeze-drying. It was characterized as an acidic heteropolysaccharide, composed of neutral sugars (29.4%), uronic acids (14.2%) and amino sugars (0.93%). The functional group analysis by FT-IR spectroscopy showed the presence of hydroxyl, carboxyl, carbonyl and methoxyl groups. Thermal analysis by DSC showed the crystalline transition and the crystalline melting point (T-m) at 300 degrees C. This polysaccharide was soluble in water and insoluble in any organic solvents tested; gelation occurred under alkaline conditions in the presence of divalent cations in which copper as CuSO4 gave the best result. Studies on the flocculation property revealed that this polysaccharide was stable at 4-60 degrees C and pH 5-7. The optimal concentrations for the flocculating activity were 2 mg/L polysaccharide and 40 mM CaCl2 which played the synergistic effect on kaolin flocculation. Moreover, this polysaccharide could flocculate the kaolin suspension over a wide range of pH (pH 2-8) and temperature (4-50 degrees C) tested in the presence of CaCl2. (c) 2006 Elsevier Ltd. All rights reserved.

Synthesis of soluble phosphate polymers by RAFT and their in vitro mineralization

Soluble linear (non-cross-linked) poly(monoacryloxyethyl phosphate) (PMAEP) and poly(2-(methacryloyloxy)ethyl phosphate) (PMOEP) were successfully synthesized through reversible addition-fragmentation chain transfer (RAFT)-mediated polymerization and by keeping the molecular weight below 20 K. Above this molecular weight, insoluble (cross-linked) polymers were observed, postulated to be due to residual diene (cross-linkable) monomers formed during purification of the monomers, MOEP and MAEP. Block copolymers consisting of PMAEP or PMOEP and poly(2-(acetoacetoxy) ethyl methacrylate) (PAAEMA) were successfully prepared and were immobilized on aminated slides. Simulated body fluid studies revealed that calcium phosphate (CaP) minerals formed on both the soluble polymers and the cross-linked gels were very similar. Both the PMAEP polymers and the PMOEP gel showed a CaP layer most probably brushite or monetite based on the Ca/P ratios. A secondary CaP mineral growth with a typical hydroxyapatite (HAP) globular morphology was found on the PMOEP gel. The soluble PMOEP film formed carbonated HAP according to Fourier transform infrared (FTIR) spectroscopy. Block copolymers attached to aminated slides showed only patchy mineralization, possibly due to the ionic interaction of negatively charged phosphate groups and protonated amines.