Irreversible change of pore structure of MCM-41 upon hydration at room temperature

The pore structure stability of MCM-41 materials upon hydration/dehydration was studied by XRD, Si-29 MAS NMR, and gravimetric adsorption techniques. Results demonstrated that collapses of the pore structure of MCM-41 occurred upon rehydration at room temperature due to the hydrolysis of the bare Si-O-Si(Al) bonds in the presence of water vapor. Full structure collapses of MCM-41 were found to occur when a MCM-41 sample was left in air for three months. It is also suggested that care must be taken when XRD is used to evaluate the structure property of MCM-41 materials to avoid the possible adverse effects of water vapor.

Laser cooling of a solid from ambient temperature

A 250 mum diameter fibre of ytterbium-doped ZBLAN was cooled by 13 K from room temperature. The cooling was performed in vacuum to limit the thermal load on the fibre. 0.85 W of laser light at 1015 nm was coupled into the fibre. The ytterbium ions absorbed this light, and the excited atoms thermalized phononically and on average emitted light at a wavelength of 996 nm. Since the quantum efficiency of the transition was high, this resulted in a net loss of energy from the glass, producing net bulk cooling.

In situ electron paramagnetic resonance (EPR) study of surface oxygen species on Au/ZnO catalyst for low-temperature carbon monoxide oxidation

Some paramagnetic superoxide ions detectable by electron paramagnetic resonance (EPR) can be generated on Au/ZnO catalyst by oxygen adsorption at room temperature as well as at 553 K. In both the cases, the O-2(-) ions are present on the catalyst surface. The disappearance of the O-2(-) signal by the introduction of carbon monoxide over the catalyst surface implies that the O-2(-) ions are either the active oxygen species or the precursors of the active oxygen species. The CO3- species produced are also detected by EPR. (C) 2001 Elsevier Science B.V. All rights reserved.

Structural definition of the low-temperature phase transition of tris(ethane-1,2-diamine)zinc(II) dinitrate

The 93 K X-ray crystal structure of tris(ethane-1,2-diamine)zinc(II) dinitrate is reported. As predicted by the spectroscopic studies of other workers, there is a reversible phase transition of the structure at low temperature. We have determined this temperature to be 143 K. The structure at this temperature and below resembles that of the room temperature structure, except the crystallographic D-3 symmetry of the complex cation (296 K) is lowered to C-2 ( below 144 K) by subtle changes in cation-anion hydrogen bonding. No change in the conformation of the cation or its bond lengths and angles was found.

Temperature dependence of the crystal structure and g-values of [(HC(Ph2PO)(3))(2)Cu] (ClO4)(2)center dot 2H(2)O: Influence of dynamic Jahn-Teller coupling and lattice strain interactions

The temperature dependence of the X-ray crystal structure and powder EPR spectrum of [(HC(Ph2PO)(3))(2)CU]-(ClO4)(2)center dot 2H(2)O is reported, and the structure at room temperature confirms that reported previously. Below similar to 100 K, the data imply a geometry with near elongated tetragonal symmetry for the [(HC(Ph2PO)(3))(2)Cu](2+) complex, but on warming the two higher Cu-O bond lengths and g-values progressively converge, and by 340 K the bond lengths correspond to a compressed tetragonal geometry. The data may be interpreted satisfactorily assuming an equilibrium among the energy levels of a Cu-O-6 polyhedron subjected to Jahn-Teller vibronic coupling and a lattice strain. However, agreement with the experiment is obtained only if the orthorhombic component of the lattice strain decreases to a negligible value as the temperature approaches 340 K.

ESEM observations of SCC initiation for 4340 high strength steel in distilled water

The stress corrosion cracking (SCC) initiation process for 4340 high strength steel in distilled water at room temperature was studied using a new kind of instrument: an environmental scanning electron microscope (ESEM). It was found that the applied stress accelerated oxide film formation which has an important influence on the subsequent SCC initiation. SCC was observed to initiate in the following circumstances: (1) cracking of a thick oxide film leading to SCC initiation along metal grain boundaries, (2) the initiation of pits initiating SCC in the metal and (3) SCC initiating from the edge of the specimen. All these three SCC initiation circumstances are consistent with the following model which couples SCC initiation with cracking of a surface protective oxide. There is a dynamic interaction between oxide formation, the applied stress, oxide cracking, pitting and the initiation of SCC. An aspect of the dynamic interaction is cracks forming in a protective surface oxide because of the applied stress, exposing to the water bare metal at the oxide crack tip, and oxidation of the bare metal causing crack healing. Oxide crack healing would be competing with the initiation of intergranular SCC if an oxide crack meets the metal surface at a grain boundary. If the intergranular SCC penetration is sufficiently fast along the metal grain boundary, then the crack yaws open preventing healing of the oxide crack. If intergranular SCC penetration is not sufficiently fast, then the oxidation process could produce sufficient oxide to fill both the stress corrosion crack and the oxide crack; in this case there would be initiation of SCC but only limited propagation of SCC. Stress-induced cracks in very thin oxide can induce pits which initiate SCC, and under some conditions such stress induced cracks in a thin oxide can directly initiate SCC.

Stress corrosion crack propagation in AerMet 100

Fracture mechanics tests were carried out for AerMet 100 in distilled water and NaCl (3.5 and 35 gl(-1)). The initiation period at higher values of the stress intensity factor indicated that load application in the stress corrosion cracking (SCC) environment is a necessary but not sufficient factor for SCC and that time is needed for some other factor (e.g., the local hydrogen concentration) to reach an appropriate value. The threshold stress intensity factor, K-ISSC, was found to increase with decreasing NaCl concentration. The plateau stress corrosion crack velocity was 2 x 10(-8) ms(-1) for NaCl (3.5 and 35 gl(-1)). The fracture mode was transgranular with small areas of an intergranular nature. (C) 1998 Chapman & Hall.

Linearly-increasing-stress testing of carbon steel in 4 N NaNO3 and in Bayer liquor

This paper reports the application of linearly increasing stress testing (LIST) to the study of stress corrosion cracking (SCC) of carbon steel in 4 N NaNO3 and in Bayer liquor. LIST is similar to the constant extension-rate testing (CERT) methodology with the essential difference that the LIST is load controlled whereas the CERT is displacement controlled. The main conclusion is that LIST is suitable for the study of the SCC of carbon steels in 4 N NaNO3 and in Bayer liquor. The low crack velocity in Bayer liquor and a measured maximum stress close to that of the reference specimen in air both indicate that a low applied stress rate is required to study SCC in this system. (C) 1998 Chapman & Hall.

Free volume and water uptake in a copolymer hydrogel series

A copolymer of X-hydroxyethyl methacrylate (HEMA) with 2-ethoxy ethyl methacrylate (EEMA) was synthesized and the molecular mobility, free volume, and density properties examined as a function of composition. These properties were correlated with the equilibrium water uptake in order to determine which of the properties were most influential in causing high water sorption, as these materials are suitable candidates for hydrogel systems. It was found that the polar HEMA repeat unit results in a rigid, glassy sample at room temperature due to the high degree of hydrogen bonding between chains whereas high EEMA content leads to rubbery samples with subambient glass transition temperatures. The free volume properties on the molecular scale measured by positron annihilation Lifetime spectroscopy (PALS) showed that higher HEMA content led to smaller, fewer holes and a lower free volume fraction than EEMA. Therefore the high water uptake of HEEMA-containing copolymers is largely related to the high polarity of the HEMA unit compared to EEMA, despite the low content of free volume into which the water can initially diffuse. Trends in density with copolymer composition, as measured on a macroscopic level, differs to that seen by PALS and indicates that the two techniques are measuring different scales of packing. (C) 1998 John Wiley & Sons, Inc.

The crack tip strain field of AISI 4340 - Part I - Measurement technique

This is the first paper in a study on the influence of the environment on the crack tip strain field for AISI 4340. A stressing stage for the environmental scanning electron microscope (ESEM) was constructed which was capable of applying loads up to 60 kN to fracture-mechanics samples. The measurement of the crack tip strain field required preparation (by electron lithography or chemical etching) of a system of reference points spaced at similar to 5 mu m intervals on the sample surface, loading the sample inside an electron microscope, image processing procedures to measure the displacement at each reference point and calculation of the strain field. Two algorithms to calculate strain were evaluated. Possible sources of errors were calculation errors due to the algorithm, errors inherent in the image processing procedure and errors due to the limited precision of the displacement measurements. Estimation of the contribution of each source of error was performed. The technique allows measurement of the crack tip strain field over an area of 50 x 40 mu m with a strain precision better than +/- 0.02 at distances larger than 5 mu m from the crack tip. (C) 1999 Kluwer Academic Publishers.

Modeling the optical properties of AlSb, GaSb, and InSb

Optical constants of AlSb, GaSb, and InSb are modeled in the 1-6 eV spectral range. We employ an extension of Adachi's model of the optical constants of semiconductors. The model takes into account transitions at E-0, E-0 + Delta(0), E-1, and E-1 + Delta(1) critical points, as well as higher-lying transitions which are modeled with three damped harmonic oscillators. We do not consider indirect transitions contribution, since it represents a second-order perturbation and its strength should be low. Also, we do not take into account excitonic effects at E-1, E-1 + Delta(1) critical points, since we model the room temperature data. In spite of fewer contributions to the dielectric function compared to previous calculations involving Adachi's model, our calculations show significantly improved agreement with the experimental data. This is due to the two main distinguishing features of calculations presented here: use of adjustable line broadening instead of the conventional Lorentzian one, and employment of a global optimization routine for model parameter determination.

Clarification of the Crystal Structure of [(HC(Ph2PO)3)2Cu](ClO4)2·2H2O

EXAFS spectra of [(HC(Ph2PO)(3))(2)Cu](ClO4)(2). 2H(2)O have been measured at room temperature. These show that the CuO6 unit is tetragonally elongated, rather than having the compressed tetragonal geometry previously inferred from the X-ray crystal structure determination. [GRAPHICS]

The states, diffusion, and concentration distribution of water in radiation-formed PVA/PVP hydrogels

Hydrogels with various compositions of polyvinyl alcohol (PVA) and poly(1-vinyl-2-pyrrolidinone) (PVP) were prepared by irradiating mixtures of PVA and PVP in aqueous solutions with gamma-rays from Co-60 sources at room temperature. The states of water in the hydrogels were characterized using DSC and NMR T-2 relaxation measurements and the kinetics of water diffusion in the hydrogels were studied by sorption experiments and NMR imaging. The DSC endothermic peaks in the temperature range -10 to +10 degrees C implied that there are at least two kinds of freezable water present in the matrix. The difference between the total water content and the freezable water content was refer-red to as bound water, which is not freezable. The weight fraction of water at which only nonfreezable water is present in a hydrogel with F-VP = 0.19 has been estimated to be g(H2O)/g(Polymer) = 0.375. From water sorption experiments, it was demonstrated that the early stage of the diffusion of water into the hydrogels was Fickian. A curve-fit of the early-stage experimental data to the Fickian model allowed determination of the water diffusion coefficient, which was found to lie between 1.5 x 10(-11) m(2) s(-1) and 4.5 x 10(-11) m(2) s(-1), depending on the polymer composition, the cross-link density, and the temperature. It was also found that the energy barrier for diffusion of water molecules into PVA/PVP hydrogels was approximate to 24 kJ mol(-1). Additionally, the diffusion coefficients determined from NMR imaging of the volumetric swelling of the gels agreed well with the results obtained by the mass sorption method.

A transformation toughening white cast iron

An experimental white cast iron with the unprecedented fracture tough ness of 40 MPa m(1/2) is currently being studied to determine the mechanisms of toughening. This paper reports the investigation of the role of strain-induced martensitic (SIM) transformation. The dendritic microconstituent in the toughened alloy consists primarily of retained austenite, with precipitated M(7)C(3) carbides and some martensite. Refrigeration experiments and differential scanning calorimetry (DSC) were used to demonstrate, firstly, that this retained austenite has an ''effective'' sub-ambient M(S) temperature and, secondly, that SIM transformation can occur at ambient temperatures. Comparison between room temperature and elevated temperature K-Ic tests showed that the observed SIM produces a transformation toughening response in the alloy, contributing to, but not fully accounting for, its high tough ness. SIM as a mechanism for transformation toughening has not previously been reported for white cast irons. Microhardness traverses on crack paths and X-ray diffraction (XRD) on fracture surfaces confirmed the interpretation of the K-Ic experiments. Further DSC and quantitative XRD showed that, as heat-treatment temperature is varied, there is a correlation between fracture toughness and the volume fraction of unstable retained austenite.

Environmental assisted fracture for 4340 steel in water and air of various humidities

This paper reports on measurements of crack growth by environmental assisted fracture (EAF) for 4340 steel in water and in air at various relative humidities. Of most interest is the observation of slow crack propagation in dry air. Fractographic analysis leads to the strong suggestion that this slow crack propagation is due to hydrogen cracking caused by internal hydrogen in solid solution inside the sample material.