Thermal characterization of copolymers obtained by radiation grafting of styrene onto poly(tetrafluoroethyleneperfluoropropylvinylether) substrates: thermal decomposition, melting behavior and low-temperature transitions

Differential scanning calorimetric (DSC) and thermogravimetric analysis (TGA) have been used to study the thermal decomposition, the melting behavior and low-temperature transitions of copolymers obtained by radiation-induced grafting of styrene onto poly (tetrafluoroethylene- perfluoropropylvinylether) (PFA) substrates. PFA with different contents of perfluoropropylvinylether (PPVE) as a comonomer have been investigated. A two step degradation pattern was observed from TGA thermograms of all the grafted copolymers, which was attributed to degradation of PSTY followed by the degradation of the PFA backbone at higher temperature. One broad melting peak can be identified for all copolymers, which has two components in the samples with higher PPVE content. The melting peak, crystal-crystal transition and the degree of crystallinity of the grafted copolymers increases with radiation grafting up to 50 kGy, followed by a decrease at higher doses. No such decrease was observed in the ungrafted PFA samples after irradiation. This indicated that the changes in the heats of transitions and crystallinity at low doses are due to the radiation effects on the microstructure of PFA (chain scission), whereas at higher doses the grafted PSTY is the driving force behind these changes. (C) 2001 Elsevier Science Ltd. All rights reserved.

Synthesis of monocyclic and linear polystyrene using the reversible coupling/cleavage of thiol/disulfide groups

By carefully controlling the concentration of alpha,omega-thiol polystyrene in solution, we achieved formation of unique monocyclic polystyrene chains (i.e., polymer chains with only one disulfide linkage). The presence of cyclic polystyrene was confirmed by its lower than expected molecular weight due to a lower hydrodynamic volume and loss of thiol groups as detected by using Ellman's reagent. The alpha,omega-thiol polystyrene was synthesized by polymerizing styrene in the presence of a difunctional RAFT agent and subsequent conversion of the dithioester end groups to thiols via the addition of hexylamine. Oxidation gave either monocyclic polymer chains (i.e., with only one disulfide linkage) or linear multiblock polymers with many disulfide linkages depending on the concentration of polymer used with greater chance of cyclization in more dilute solutions. At high polymer concentrations, linear multiblock polymers were formed. To control the MWD of these linear multiblocks, monofunctional X-PSTY (X = PhCH2C(S)-S-) was added. It was found that the greatest ratio of X-PSTY to X-PSTY-X resulted in a low M-n and PDI. We have shown that we can control both the structure and MWD using this chemistry, but more importantly such disulfide linkages can be readily reduced back to the starting polystyrene with thiol end groups, which has potential use for a recyclable polymer material.