Layered silicate nanocomposites based on various high-functionality epoxy resins. Part II: The influence of an organoclay on the rheological behavior of epoxy prepolymers

The effect of an organically surface modified layered silicate on the viscosity of various epoxy resins of different structures and different functionalities was investigated. Steady and dynamic shear viscosities of the epoxy resins containing 0-10 wt% of the organoclay were determined using parallel plate rheology. Viscosity results were compared with those achieved through addition of a commonly used micron-sized CaCO3 filler. It was found that changes in viscosities due to the different fillers were of the same order, since the layered silicate was only dispersed on a micron-sized scale in the monomer (prior to reaction), as indicated by X-ray diffraction measurements. Flow activation energies at a low frequency were determined and did not show any significant changes due to the addition of organoclay or CaCO3. Comparison between dynamic and steady shear experiments showed good agreement for low layered silicate concentrations below 7.5 wt%, i.e. the Cox-Merz rule can be applied. Deviations from the Cox-Merz rule appeared at and above 10 wt%, although such deviations were only slightly above experimental error. Most resin organoclay blends were well predicted by the Power Law model, only concentrations of 10 wt% and above requiring the Herschel-Buckley (yield stress) model to achieve better fits. Wide-angle X-ray measurements have shown that the epoxy resin swells the layered silicate with an increase in the interlayer distance of approximately 15 Angstrom, and that the rheology behavior is due to the lateral, micron-size of these swollen tactoids.

Layered silicate nanocomposites based on various high-functionality epoxy resins: The influence of an organoclay on resin cure

The influence of an organically modified clay on the curing behavior of three epoxy systems widely used in the aerospace industry and of different structures and functionalities, was studied. Diglycidyl ether of bisphenol A (DGEBA), triglycidyl p-amino phenol (TGAP) and tetraglycidyl diamino diphenylmethane (TGDDM) were mixed with an octadecyl ammonium ion modified organoclay and cured with diethyltoluene diamine (DETDA). The techniques of dynamic mechanical thermal analysis (DMTA), chemorheology and differential scanning calorimetry (DSC) were applied to investigate gelation and vitrification behavior, as well as catalytic effects of the clay on resin cure. While the formation of layered silicate nanocomposite based on the bifunctional DGEBA resin has been previously investigated to some extent, this paper represents the first detailed study of the cure behavior of different high performance, epoxy nanocomposite systems.

Rheological Properties of Organoclay Suspensions in Epoxy Network Precursors

This paper deals with the evolution of the state of dispersion of organically modified montmorillonites in epoxy or amine precursors. The epoxy prepolymer is a diglycidyl ether of bisphenol A (DGEBA) and the curing agent is an aliphatic diamine with a polyoxypropylene backbone (Jeffamine D2000). The clay dispersion is evaluated at the platelet scale (nanoscopic scale) from X-ray spectrometry [wide-angle X-ray diffraction (WAXD) and small-angle X-ray scattering (SAXS)] and at the aggregates scale (microscopic scale) from rheological analysis. The organoclays used form gels in the monomers above the percolation threshold if no shear is applied and present a mechanical gel/sol transition when shear stress increases. Gel strength and viscosity at high shear rates are linked to the nanometric state of dispersion and reveal the existence of two different organizations depending on organoclay/monomer interactions: (i) When the clay shows good interactions with the monomer, a significant swelling of the clay galleries by the monomer is obtained. These swollen particles lead to formation of weak gels which after shearing give high relative viscosity fluids. (ii) When the clay develops poor interactions with the monomer, the clay tends to reduce its exchange surface with the monomer and leads to a strongly connected gel. Shear breaks down this physical network leading to a very low relative viscosity fluid composed of nonswollen particles keeping a high aspect ratio. (C) 2003 Elsevier B.V All rights reserved.