The effect of Cu addition and milling contaminations on the microstructure evolution of ball milled Al-Pb alloy during sintering

Al-10 wt.%Pb and Al-10 wt.%Pb-x wt.%Cu (x = 0-7.0) bulk alloys were prepared by sintering the mechanically alloyed powders at various temperatures. The microstructure changes of the as consolidated powders in the course of sintering were analyzed by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction analysis and transmission electron microscopy. It has been found that, with respect to the Al-10 wt.%Pb-x wt.%Cu alloy, CuAl2 and Cu9Al4 phases formed in the milling process, and the amount of CuAl2 phase increased while the Cu9Al4 phase disappeared gradually in the sintering process. In both Al-10 wt.%Pb and Al-10 wt.%Pb-x wt.%Cu alloys, the sintering process results in the coarsening of Pb phase and the growth rate of Pb phase fulfills the Lifshitz-Slyozov-Wagner equation even though the size of the Pb phase was in nanometer range. The Pb particle exhibits cuboctahedral morphology and has a cubic to cubic orientation relationship with the Al matrix. The addition of Cu strongly depressed the growth rate of Pb. Contamination induced by milling has apparent influence on the microstructure of the sintered alloys. Al7Cu2Fe and aluminium oxide phases were identified in the sintered alloys. The cuboctahedral morphology of Pb particles was broken up by the presence of the oxide phase. (c) 2006 Elsevier B.V. All rights reserved.

Blast fragmentation modelling for a green field open cut gold deposit

This paper outlines the methodology of blast fragmentation modeling undertaken for a green field feasibility study at the Riska gold deposit in Indonesia. The favoured milling process for the feasibility study was dump leaching,with no crushing of the ore material extracted from the pit. For this reason,blast fragmentation was a critical issue to be addressed by the study. A range of blast designs were considered with bench heights and blasthole diameters ranging from 4 m to 7 m and 76 mm to 102 mm respectively. Rock mass data was obtained from 19 diamond drill cores across the deposit (total drill length approximately 2200 m). Intact rock strength was estimated from qualitative strength descriptors,while the in situ block size distribution of the rock mass was estimated from the Rock Quality Designation (RQD) of the core.

Effect of fluoromica platelet size on the properties of segmented polyurethane nanocomposites

Segmented polyurethane nanocomposites containing three different size fractions of SomasifTM ME100 (synthetic fluoromica) have been prepared via solvent casting. The platelet size was adjusted via a proprietary milling process, and average diameters of approximately 500 nm, 100 nm and 30 nm were measured via TEM. To the best of our knowledge this is the first time the effect of aspect ratio has been studied with the same t-o-t structured mineral. The mechanical properties of these nanocomposites have been found to be highly dependent upon the platelet size. Depending on the aspect ratio and surface treatment selected, significant improvements in tensile strength can be achieved with a minimal reduction in resilience: a problem encountered with elastomeric layered silicate nanocomposites.