Method for determining reaction rate of mild steel containers during melting of magnesium-aluminium alloys and effect of aluminium content on directionally solidified microstructures

A magnesium alloy of eutectic composition (33 wt-'%Al) was directionally solidified in mild steel tubes at two growth rates, 32 and 580 mum s(-1,) in a temperature gradient between 10 and 20 K mm(-1). After directional solidification, the composition of each specimen varied dramatically, from 32'%Al in the region that had remained solid to 18%Al (32 mum s(-1) specimen) and 13%Al (580 mum s(-1) specimen) at the plane that had been quenched from the eutectic temperature. As the aluminium content decreased, the microstructure contained an increasing volume fraction of primary magnesium dendrites and the eutectic morphology gradually changed from lamellar to partially divorced. The reduction in aluminium content was caused by the growth of an Al-Fe phase ahead of the Mg-Al growth front. Most of the growth of the Al-Fe phase occurred during the remelting period before directional solidification. The thickness of the Al-Fe phase increased with increased temperature and time of contact with the molten Mg-Al alloy. (C) 2003 Maney Publishing.

Effect of sample geometry on regression rate of the melting interface for carbon steel burned in oxygen

Promoted-ignition testing on carbon steel rods of varying cross-sectional area and shape was performed in high pressure oxygen to assess the effect of sample geometry on the regression rate of the melting interface. Cylindrical and rectangular geometries and three different cross sections were tested and the regression rates of the cylinders were compared to the regression rates of the rectangular samples at test pressures around 6.9 MPa. Tests were recorded and video analysis used to determine the regression rate of the melting interface by a new method based on a drop cycle which was found to provide a good basis for statistical analysis and provide excellent agreement to the standard averaging methods used. Both geometries tested showed the typical trend of decreasing regression rate of the melting interface with increasing cross-sectional area; however, it was shown that the effect of geometry is more significant as the sample's cross sections become larger. Discussion is provided regarding the use of 3.2-mm square rods rather than 3.2-mm cylindrical rods within the standard ASTM test and any effect this may have on the observed regression rate of the melting interface.