Crystallography of carbide-free bainite in a hard bainitic steel

The convergent beam Kikuchi line diffraction technique has been used to accurately determine the orientation relationships between bainitic ferrite and retained austenite in a hard bainitic steel. A reproducible orientation relationship has been uniquely observed for both the upper and lower bainite. It is [GRAPHICS] However, the habit plane of upper bainite is different from that of lower bainite. The former has habit plane that is either within 5 degrees of (221)(A) or of (259)(A). The latter only corresponds with a habit plane that is within 5 degrees of (259)(A). The determined orientation relationship is completely consistent with reported results determined using the same technique with an accuracy of +/- 0.5 degrees in lath martensite in an Fe-20 wt.% Ni-6 wt.% Mn alloy and in a low carbon low alloy steel. It also agrees well with the orientation relationship between granular bainite and austenite in an Fe-19 wt.% Ni-3.5 wt.% Mn-0.15 wt.% C steel. Hence it is believed that, at least from a crystallographic point view, the bainite transformation has the characteristics of martensitic transformation. (c) 2006 Elsevier B.V. All rights reserved.

The effect of resin type on the sintering of freeformed maraging steel

The role of the resin type on the sintering of maraging steel with boron additions has been investigated. Two different resins were added to the steel mixture and their subsequent debinding was evaluated and sintering responses compared with that of a resin-free alloy. The two resins used, nylon and a mixture of phenolic resin and synthetic wax, possessed different debinding behaviour, with the latter causing significant carbon contamination of the parts. This caused the formation of a Ti-Mo carbide, depleting the matrix of these elements. Consequently, the microstructure consisted of the equilibrium Fe-Fe2B eutectic, as well as a Mo-rich boride. The liquid phase also appeared to contain significant amounts of carbon, which lowered the temperature at which the liquid formed, resulting in high density occurring at a much lower temperature. When nylon was used as the binder, a similar sintering response to the resin-free alloy was observed. (C) 2002 Published by Elsevier Science B.V.