NMR imaging of the diffusion of water at 37 degrees C into poly(2-hydroxyethyl methacrylate) containing aspirin or vitamin B-12

The ingress of water into poly(2-hydroxyethyl methacrylate), PHEMA, loaded with either one of two model drugs, vitamin B-12 or aspirin, was studied at 37 degreesC using three-dimensional NMR imaging. PHEMA was loaded with 5 and 10 wt % of the drugs. From the imaging profiles, it was observed that incorporation of vitamin B-12 into PHEMA resulted in enhanced crack formation on sorption of water and the crack healing behind the diffusion front was slower than for PHEMA without added drug. This was accounted for by the anti-plasticization of PHEMA by vitamin B-12. Crack formation was inhibited in the P-HEMA-aspirin systems because of the plasticizing effect of the aspirin on the PHEMA matrix. All of the polymers were found to absorb water according to an underlying Fickian diffusion mechanism. For PHEMA loaded with 5 wt % of aspirin or vitamin B-12, the best values of the water diffusion coefficients were both found to be 1.3 +/- 0.1 x 10(-11) m(2) s(-1) at 37 degreesC, while the values for the polymer loaded with 10 wt % of the drugs were slightly higher, 1.5 +/- 0.1 x 10(-11) m(2) s(-1).

Mass uptake study of the diffusion of water and SBF into poly(2-hydroxyethyl methacrylate-co-tetrahydrofurfuryI methacrylate) containing aspirin or vitamin B-12

The ingress of water and Kokubo simulated body fluid (SBF) into poly (2-hydroxyethyl methacrylate) (PHEMA), and its co-polymers with tetrahydrofurduryl methacrylate (THFMA), loaded with either one of two model drugs, vitamin 1312 or aspirin, was studied by mass uptake over the temperature range 298-318 K. The polymers were studied as cylinders and were loaded with either 5 wt% or 10 wt% of the drugs. From DSC studies it was observed that vitamin B-12 behaved as a physical cross-linker restricting chain segmental mobility, and so had a small anti-plasticisation effect on PHEMA and the co-polymers rich in HEMA, but almost no effect on the T-g of co-polymers rich in THFMA. On the other hand, aspirin exhibited a plasticising effect on PHEMA and the copolymers. All of the polymers were found to absorb water and SBF according to a Fickian diffusion mechanism. The polymers were all found to swell to a greater extent in SBF than in water, which was attributed to the presence of Tris buffer in the SBF. The sorptions of the two penetrants were found to follow Fickian kinetics in all cases and the diffusion coefficients at 310 K for SBF were found to be smaller than those for water, except for the polymers containing aspirin where the diffusion coefficients were higher than for the other systems. For example, for sorption into PHEMA the diffusion coefficient for water was 1.41 X 10(-11) m(2)/s and for SBF was 0.79 x 10-11 m(2)/s, but in the presence of 5 wt% aspirin the corresponding values were 1.27 x 10(-1)1 m(2)/s and 1.25 x 10(-11) m(2)/s, respectively. The corresponding values for PHEMA loaded with 5 wt% B-12 were 1.25 x 10(-11) m(2)/s and 0.74 x 10(-11) m(2)/s, respectively.

Towards identifying the new structures formed on the γ-radiolysis of Ultem

Ultem irradiated up to 10.0 MGy has been analysed using C-13, H-1 and D-2 proton-carbon and proton-proton correlation NMR spectroscopy to shed light on the formation of new structures. Chemical shifts and correlation data were used to determine the structure or partial structures of several new components. The spectra indicated the presence of new groups and structures involving the isopropylidene group, the imide ring, and hydrogen-abstraction reactions. Possible pathways for formation of the new structures are proposed and the G-values for their formation have been estimated. (C) 2003 Elsevier Science Ltd. All rights reserved.

The health of children in immigration detention: how does Australia compare?

We live in an age when the number of refugees worldwide is increasing. All of them have suffered physically or emotionally to a varying degree in their country of origin. The transit to a country of resettlement is fraught with further difficulties or the risk of death. This article explores the different approach taken to the management of this issue by Denmark and Iceland, in comparison to that of Australia. In particular, the different approaches to health care for children and their families are identified. The management of these issues by Denmark and Iceland would appear to be a model to follow. Outcomes of the different managements have not been assessed.

Experimental Calcification of HEMA-Based Hydrogels in the Presence of Albumin and a Comparison to the in Vivo Calcification

The precipitation patterns and characteristics of calcium phosphate (CaP) phases deposited on HEMA-based hydrogels upon incubation in simulated body fluid (SBF-2) containing a protein (human serum albumin) have been investigated in relation to the calcification in an organic-free medium (SBF-1) and to that occurring after subcutaneous implantation in rats. In SBF-2, the deposits occurred exclusively as a peripheral layer on the surface of the hydrogels and consisted mainly of precipitated hydroxyapatite, a species deficient in calcium and hydroxyl ions, similarly to the deposits formed on the implanted hydrogels, where the deposited layer was thicker. In SBF-1, the deposits were mainly of brushite type. There was no evidence that albumin penetrated the interstices of hydrogels. As the X-ray diffraction patterns of the CaP deposits generated in SBF-2 showed a similar nature with those formed on the implanted hydrogel, it was concluded that the calcification in SBF-2 can mimic to a reliable extent the calcification process taking place in a biological environment.

FT-Raman studies of a range of polyimides subjected to high-energy Radiations at room and elevated temperatures

A range of polyimides have been subjected to electron beam radiolysis at different temperatures. These polyimides were chemically designed to suit space applications, being either transparent or having groups which provide oxidation resistance. The structural changes that occur in the polyimides, when subjected to electron beam irradiation doses up to 18.5 MGy and up to temperatures close to their glass transition temperatures, were studied using FT-Raman spectroscopy. The range of polyimides studied included a series of perfluoropolyimides, a silicon-modified polyimide, and Ultem. The changes in the Raman peak intensities of the different groups indicated scission reactions involving the imide rings and ether linkages. (c) 2006 Wiley Periodicals, Inc.

Investigation of spontaneous microemulsion formation in supercritical carbon dioxide using high-pressure NMR

NMR spectroscopy and relaxometry were used to investigate microemulsion formation in supercritical CO2. The droplets were stabilised by the salt of a perfluorinated polyether. Spontaneous microemulsion formation was observed over a period of 5 h in the absence of applied sheer. Time-resolved relaxation times of the surfactant tail showed a stepwise increase in mobility of the tail over this period. Conversely, the translational mobility of water confined within the droplet decreased over the same interval. This data is consistent with the gradual decrease in droplet size as time progressed. Indeed, NMR self-diffusion coefficients were used to show that droplets with a radius of approximately 5 nm were formed at equilibrium.

NMR microscopy: A tool for measuring monomer diffusion in supercritical CO2

The diffusion of styrene into linear low density polyethylene in a solution of supercritical CO2 was investigated using NMR microimaging. For both pure styrene and styrene dissolved in supercritical CO2, the diffusion was found to follow Fickian kinetics. Supercritical CO2 was found to enhance the rate and extent of diffusion of styrene into the substrate by up to three times under the conditions of this investigation, compared to pure styrene. NMR imaging was used to measure the concentration profiles of the styrene penetrants in real time, and the results were fitted to a Fickian model for diffusion. At a CO2 pressure of 150 bar and temperature of 40 degrees C, the diffusion coefficient of a 30 wt-% solution of styrene into LLDPE was calculated to be 1 X 10(-11) m(2). s(-1). This is significantly faster than the diffusion coefficient measured for pure styrene diffusion at 40 degrees C (3 x 10(-12) m(2). s(-1)). The diffusion coefficients determined by gravimetric analysis were slightly higher than those determined by the imaging method. This was probably due to residual styrene and/or polystyrene adhering to the surface of the films in the gravimetric technique.