Ultrasonic measurement technique of burning metals in normal and reduced gravity

The in situ real time measurement of the regression rate of a melting interface (RRMI) is performed by the ultrasonic measurement system reported here. The RRMI is the rate at which a solid/liquid interface (SLI) moves along a metallic rod while burning in an oxygen-enriched atmosphere and is an important flatnmability indicator. The ultrasonic transducer and associated equipment used to drive the transducer and record the echo signal is described, along with the process that transforms the acquired signals into a RRMI value. Test rods of various metals and geometric shapes were burned at several test conditions in different test facilities. The RRMI results with quantified errors are presented and reviewed. The effect of reduced gravity on burning metals is important to space-applications and RRMI results obtained in a reduced gravity environment are also presented.

Instantaneous RRMI of iron rods in reduced gravity

Standard upward-burning promoted ignition tests (“Standard Test Method for Determining the Combustion Behavior of Metallic Materials in Oxygen-Enriched Atmospheres,” ASTM G4-124 [1] or “Flammability, Odor, Offgassing, and Compatibility Requirements and Test Procedures for Materials in Environments that Support Combustion,” NASA-STD-6001, NASA Test 17 [2]) were performed on cylindrical iron (99.95% pure) rods in various oxygen purities (95.0–99.98%) in reduced gravity onboard NASA JSC's KC-135 to investigate the effect of gravity on the regression rate of the melting interface. Visual analysis of experiments agrees with previous published observations showing distinct motions of the molten mass attached to the solid rod during testing. Using an ultrasonic technique to record the real-time rod length, comparison of the instantaneous regression rate of the melting interface and visual recording shows a non-steady-state regression rate of the melting interface for the duration of a test. Precessional motion is associated with a higher regression rate of the melting interface than for test periods in which the molten mass does not show lateral motion. The transition between the two types of molten mass motion during a test was accompanied by a reduced regression rate of the melting interface, approximately 15–50% of the average regression rate of the melting interface for the entire test.