Structural, electrical, and optical analysis of ion implanted semi-insulating InP

Semi-insulating InP was implanted with MeV P, As, Ga, and In ions, and the resulting evolution of structural properties with increased annealing temperature was analyzed using double crystal x-ray diffractometry and cross sectional transmission electron microscopy. The types of damage identified are correlated with scanning spreading resistance and scanning capacitance measurements, as well as with previously measured Hall effect and time resolved photoluminescence results. We have identified multiple layers of conductivity in the samples which occur due to the nonuniform damage profile of a single implant. Our structural studies have shown that the amount and type of damage caused by implantation does not scale with implant ion atomic mass. (C) 2004 American Institute of Physics.

Tailored conductivity in ion implanted polyetheretherketone

Ion implantation can be used to confer electrical conductivity upon conventional insulating polymers such as polyetheretherketone (PEEK). We have implanted PEEK films using three different types of ion implantation: conventional inert gas and metal ion implantation, and ion beam mixing. We have applied a number of analytical techniques to compare the chemical, structural and electrical properties of these films. The most effective means of increasing electrical conductivity appears to be via ion beam mixing of metals into the polymer, followed by metal ion implantation and finally, inert gas ion implantation. Our results suggest that in all cases, the conducting region corresponds to the implanted layer in the near surface to a depth of similar to750 Angstrom (ion beam mixed) to similar to5000 Angstrom (metal ion). This latter value is significantly higher than would be expected from a purely ballistic standpoint, and can only be attributed to thermal inter-diffusion. Our data also indicates that graphitic carbon is formed within the implant region by chain scission and subsequent cross-linking. All ion implanted samples retained their bulk mechanical properties, i.e. they remained flexible. The implant layers showed no signs of de-lamination. We believe this to be the first comparative study between different implantation techniques, and our results support the proposition that soft electronic circuitry and devices can be created by conductivity engineering with ion beams. (C) 2004 Elsevier B.V. All rights reserved.

Thermal stability of ion-implanted ZnO

Zinc oxide single crystals implanted at room temperature with high-dose (1.4x10(17) cm(-2)) 300 keV As+ ions are annealed at 1000-1200 degrees C. Damage recovery is studied by a combination of Rutherford backscattering/channeling spectrometry (RBS/C), cross-sectional transmission electron microscopy (XTEM), and atomic force microscopy. Results show that such a thermal treatment leads to the decomposition and evaporation of the heavily damaged layer instead of apparent defect recovery and recrystallization that could be inferred from RBS/C and XTEM data alone. This study shows that heavily damaged ZnO has relatively poor thermal stability compared to as-grown ZnO which is a significant result and has implications for understanding results on thermal annealing of ion-implanted ZnO. (c) 2005 Americian Institute of Physics.

Preparation and anode property of Pt-CeO2 electrodes supported on carbon black for direct methanol fuel cell applications

A platinum (Pt) on pure ceria (CeO2) supported by carbon black (CB) anode was synthesized using a combined process of precipitation and coimpregnation methods. The electrochemical activity of methanol oxidation reaction on synthesized Pt-CeO2/CB anodes was investigated by cyclic voltammetry and chronoamperometry experimentation. To improve the anode property on Pt-CeO2/CB, the influence of particle morphology and particle size on anode properties was examined. The morphology and particle size of the pure CeO2 particles could be controlled by changing the preparation conditions. The anode properties (i.e., peak current density and onset potential for methanol oxidation) were improved by using nanosize CeO2 particles. This indicates that a larger surface area and higher activity on the surface of CeO2 improve the anode properties. The influence of particle morphology of CeO2 on anode properties was not very large. The onset potential for methanol oxidation reaction on Pt-CeO2/CB, which consisted of CeO2 with a high surface area, was shifted to a lower potential compared with that on the anodes, which consisted of CeO2 with a low surface area. The onset potential on Pt-CeO2/CB at 60 degrees C became similar to that on the commercially available Pt-Ru/carbon anode. We suggest that the rate-determining steps of the methanol oxidation reaction on Pt-CeO2/CB and commercially available Pt-Ru/carbon anodes are different, which accounts for the difference in performance. In the reaction mechanism on Pt-CeO2/CB, we conclude that the released oxygen species from the surface of CeO2 particles contribute to oxidation of adsorbed CO species on the Pt surface. This suggests that the anode performance of the Pt-CeO2/CB anode would lead to improvements in the operation of direct methanol fuel cells at 80 degrees C by the enhancement of diffusion of oxygen species created from the surface of nanosized CeO2 particles. Therefore, we conclude that fabrication of nanosized CeO2 with a high surface area is a key factor for development of a high-quality Pt-CeO2/CB anode in direct methanol fuel cells.

Superconductivity in metal-mixed ion-implanted polymer films

Ion implantation of normally insulating polymers offers an alternative to depositing conjugated organics onto plastic films to make electronic circuits. We used a 50 keV nitrogen ion beam to mix a thin 10 nm Sn/Sb alloy film into the subsurface of polyetheretherketone and report the low temperature properties of this material. We observed metallic behavior, and the onset of superconductivity below 3 K. There are strong indications that the superconductivity does not result from a residual thin film of alloy, but instead from a network of alloy grains coupled via a weakly conducting, ion-beam carbonized polymer matrix. (c) 2006 American Institute of Physics.