Fractal effects on the measurement of the specific surface areas of single-walled carbon nanotubes

The specific surface area (SSA) of single-walled carbon nanotubes (SWNTs) has been measured by different groups. Fujiwara et al. measured the SSA of SWNT bundles by using nitrogen and oxygen as adsorbates, and found that the SSA from O2-adsorption was 6.6% larger than that from N2-adsorption for the same SWNT sample [1]. Also Wei et al. [2] measured the SSA of HiPco SWNTs by using O2, N2 and Ar, and found that, for the same samples, Vm(Ar) > Vm(O2) > Vm(N2), here Vm is the monolayer adsorption capacity at the standard conditions of temperature and pressure (STP). Those research results indicate that, for the same SWNT sample, its measured surface area depends on the employed adsorbate.

Van der Waals interactions between two parallel infinitely long single-walled nanotubes

The potential energies of van der Waals (VDW) interactions between two parallel, infinitely long and perfect SWNTs with identical, and different sizes were studied based on the continuum Lennard-Jones model. The conclusion of Girifalco's work on (n, n) SWNTs that the potentials of SWNT-SWNT fell on a single curve, is also applicable to SWNTs with different sizes. We further obtained the corresponding constants of the well depth phi(0) and equilibrium VDW gap g(0) for SWNTs with a radius from 2 to 25 Angstrom. (C) 2005 Elsevier B.V. All rights reserved.

Simple approach to estimating the van der Waals interaction between carbon nanotubes

The van der Waals (vdW) interactions between carbon nanotubes (CNTs) were studied based on the continuum Lennard-Jones model. It was found that all the vdW potentials between two arbitrary CNTs fall on the same curve when plotted in terms of certain reduced parameters, the well depth, and the equilibrium vdW gap. Based on this observation, an approximate approach is developed to obtain the vdW potential between two CNTs without time-consuming computations. The vdW potential estimated by this approach is close to that obtained from complex integrations. Therefore, the developed approach can greatly simplify the calculation of vdW interactions between CNTs.

Effect of pore packing defects in 2-D ordered mesoporous carbons on ionic transport

Ordered mesoporous materials show great importance in energy, environmental, and chemical engineering. The diffusion of guest species in mesoporous networks plays an important role in these applications, especially for energy storage, such as supercapacitors based on ordered mesoporous carbons ( OMCs). The ion diffusion behavior in two different 2-D hexagonal OMCs was investigated by using cyclic voltametry and electrochemical impedance spectroscopy. In addition, transmission electron microscopy, small-angle X-ray diffraction, and nitrogen cryosorption methods were used to study the pore structure variations of these two OMCs. It was found that, for the OMC with defective pore channels ( termed as pore packing defects), the gravimetric capacitance was greatly decayed when the voltage scan rate was increased. The experimental results suggest that, for the ion diffusion in 2-D hexagonal OMCs with similar mesopore size distribution, the pore packing defect is a dominant dynamic factor.

Preparation of high purity ZnO nanobelts by thermal evaporation of ZnS

High purity one-dimensional ZnO nanobelts were synthesized by thermally evaporating commercial ZnS powders in a hydrogen-oxygen mixture gas at 1050 degrees C. It was found that these ZnO nanobelts had a single crystal hexagonal wurtzite structure growing along the [0001] direction. They had a rectangle-shaped cross-section with typical widths of 20 to 100 nanometers and lengths of up to hundreds of micrometers with lattice constants of a = 0.325 nm and c = 0.520 nm. The self-catalytic hydrogen-oxygen assisted growth of ZnO nanobelt is discussed. The photoluminescence (PL) characterization of the ZnO nanobelts shows strong near-band UV emission (about 383 nm) and one broad peak at 501 nm, which indicates that the ZnO nanobelts have good potential application in optoelectronic devices.

Visible light photocatalyst: Iodine-doped mesoporous titania with a bicrystalline framework

Iodine-doped (I-doped) mesoporous titania with a bicrystalline (anatase and rutile) framework was synthesized by a two-step template hydrothermal synthesis route. I-doped titania with anatase structure was also synthesized without the use of a block copolymer as a template. The resultant titania samples were characterized by X-ray diffraction, Raman spectroscopy, Fourier transform infrared, nitrogen adsorption, transmission electron microscopy, X-ray photoelectron spectroscopy, and UV-visible absorption spectroscopy. Both I-doped titania samples, with and without template, show much better photocatalytic activity than commercial P25 titania in the photodegradation of methylene blue under the irradiation of visible light (> 420 nm) and UV-visible light. Furthermore, I-doped mesoporous titania with a bicrystalline framework exhibits better activity than I-doped titania with anatase structure. The effect of rutile phase in titania on the adsorptive capacity of water and surface hydroxyl, and photocatalytic activity was investigated in detail. The excellent performance of I-doped mesoporous titania under both visible light and UV-visible light can be attributed to the combined effects of bicrystalline framework, high crystallinity, large surface area, mesoporous structure, and high visible light absorption induced by I-doping.