Sintering of freeformed maraging steel with boron additions

This paper describes the sintering of an 18Ni(350) maraging steel with additions of boron, with the aim of producing high hardness rapid tooling. Reaction of the boron with the alloying elements in the maraging steel resulted in the formation of a Mo- and Ti-rich borides. The former melted at similar to1220degreesC, providing a liquid phase for enhanced sintering. Although densification could occur regardless of the boron content, especially at high temperature, 0.4% B was required to produce a near full density component. The formation of the various borides depleted the matrix of critical age hardening elements. However, by altering the starting powder composition to compensate for this, hardness close to the wrought alloy has been achieved. This hardness was comparable to a common die casting tool steel. Examples of dies produced using selective laser sintering (SLS) are also shown. (C) 2003 Elsevier B.V. All rights reserved.

Morphological features of interfacial intermetallics and interfacial reaction rate in Al-11Si-2.5Cu-(0.15/0.60)Fe cast alloy/die steel couples

Soldering reactions are commonly observed during high pressure die casting of aluminium alloys, and involve the formation and growth of interfacial intermetallics between the die and the cast alloy. It is generally believed that close to 1% Fe is necessary in the aluminium alloy to reduce soldering. However, the role of iron in the interfacial reaction has not been studied in detail. In this investigation, reaction couples were formed between H13 tool steel substrates and an Al-11Si-2.5Cu melt containing either 0.15 or 0.60% Fe. Examination revealed distinctly different intermetallic layer morphology. The overall growth and chemistry of the reaction layer and the reaction rate measured by the consumption of the substrate were compared for the two alloy melts. It was demonstrated that a higher iron content reduces the rate of interfacial reaction, consistent with an observed thicker compact ( solid) intermetallic layer. Hence, the difference in reaction rate can be explained by a significant reduction in the diffusion flux due to a thicker compact layer. Finally, the mechanism of the growth of a thicker compact layer in the higher iron melt is proposed, based on the phase relations and diffusion both within and near the interfacial reaction zone. (C) 2004 Kluwer Academic Publishers.