Synthesis and mechanical properties of Cu-based bulk metallic glass composites containing in-situ TiC particles

Cu-based bulk metallic glass matrix composites (BMGMCs) containing in-situ TiC particles were fabricated successfully. The yield and fracture strength increased from 1930 MPa, 2250 MPa to 2210 MPa, 2500 MPa, respectively. The ductility was improved and the hardness was also enhanced by 25%. The fracture mechanism was investigated in detail. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

In situ TiB-reinforced Cu-based bulk metallic glass composites

Cu-based bulk metallic glass (BMG) composites containing in situ TiB particles were successfully fabricated. The reinforcing TiB particles with a size of 5-10 mu m are uniformly distributed in the amorphous matrix. The particles have a good bonding to the matrix with a reaction layer. The BMG composites exhibit an obvious ductility with a plastic strain of 2% for the 17.5 vol.% TiB sample due to the suppression of shear band propagation and the generation of multiple shear bands during compressive testing. The hardness of the materials is increased from Hv543 for monolithic BMG to Hv650 for 23.6 vol.% TiB-containing BMG composite. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Iron-related porosity in Al-Si-(Cu) foundry alloys

An experimental program has been undertaken to explore the effect of iron concentration on porosity levels in Al-Si alloy sand castings. The effect of iron concentrations above, below and equal to the critical iron content for alloys with either 5 or 9% Si and either 0, 1 or 3% Cu has been determined. Increasing iron concentrations were found to increase porosity in all alloys except the copper-containing Al-5% Si alloys which displayed a porosity minimum at the critical iron content. Porosity was observed to be higher in the Al-9% Si castings than the Al-5% Si castings. Differences in the primary phase volume fraction and morphology may explain this observation. The results of this experimental work do not support the existing published theories that have been proposed to explain the effect the iron on porosity. An alternative theory is therefore developed. (c) 2006 Elsevier B.V. All rights reserved.

Effect of manganese on grain refinement of Mg-Al based alloys

Manganese is a grain refiner for high purity Mg-3%Al, Mg-6%Al, Mg-9%Al, and commercial AZ31 (Mg-3%Al-1%Zn) alloys when introduced in the form of an Al-60%Mn master alloy splatter but the use of pure Mn flakes and ALTAB (TM) Mn75 tablets shows no grain refinement. Long time holding of the melt at 730 degrees C leads to an increase in grain size. The mechanism is attributed to the presence of all epsilon-AlMn phase (hexagonal close-packed) in the master alloy splatter. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Microstructure control in Sn-0.7mass%Cu alloys

Soldering alloys based oft the Sn-Cu alloy system are amongst the most favourable lead-free alternatives due to a range of attractive properties. Trace additions of Ni have been found to significantly improve the soldering characteristics of these alloys (reduced bridging etc.). This paper examines the mechanisms underlying the improvement in soldering properties of Sn-0.7 mass%Cu eutectic alloys modified with concentrations of Ni ranging front 0 to 1000 ppm. The alloys were investigated by thermal analysis during solidification, as well as optical/SEM microanalyses of fully solidified samples anti samples quenched during solidification. It is concluded that Ni additions dramatically alter the nucleation patterns and solidification behaviour of the Sn-Cu6Sn5 eutectic anti that these changes are related to the superior soldering characteristics of the Ni-modified Sn-0.7 mass%Cu alloys.

Crystallization behavior of (Cu60Zr30Ti10)(99)Sn-1 bulk metallic glass

The crystallization behavior and crystallization kinetics Of (CU60Zr30Ti10)(99)Sn-1 bulk metallic glass was studied by X-ray diffractometry and differential scanning calorimetry. It was found that a two-stage crystallization took place during continuous heating of the bulk metallic glass. Both the glass transition temperature T-g and the crystallization peak temperatures T-p displayed a strong dependence on the heating rate. The activation energy was determined by the Kissinger analysis method. In the first-stage of the crystallization, the transformation of the bulk metallic glass to the phase one occurred with an activation energy of 386 kJ/mol; in the second-stage, the formation of the phase two took place at an activation energy of 381 kJ/mol.

Electrochemical corrosion of unalloyed copper in chloride media–a critical review

The literature dealing with the electrochemical corrosion characteristics of unalloyed copper in aqueous chloride media is examined. The enormous quantity of polarisation and mixed/corrosion potential data that has been made available in the literature over the last 50 years has been compiled and discussed in a comprehensive review. For a wide range of electrode geometries, the importance of the chloride ion and the mass transport of anodic corrosion products on the corrosion behaviour of copper are made clear for both freshly polished and 'filmed' surfaces. (C) 2003 Elsevier Ltd. All rights reserved.

Strength-ductility behaviour of Al-Si-Cu-Mg casting alloys in T6 temper

A comparative study of the mechanical properties of 20 experimental alloys has been carried out. The effect of different contents of Si, Cu, Mg, Fe and Mn, as well as solidification rate, has been assessed using a strength-ductility chart and a quality index-strength chart developed for the alloys. The charts show that the strength generally increases and the ductility decreases with an increasing content of Cu and Mg. Increased Fe (at Fe/Mn ratio 0.5) dramatically lowers the ductility and strength of low Si alloys. Increased Si content generally increases the strength and the ductility. The increase in ductility with increased Si is particularly significant when the Fe content is high. The charts are used to show that the cracking of second phase particles imposes a limit to the maximum achievable strength by limiting the ductility of strong alloys. The (Cu + Mg) content (at.%), which determines the precipitation strengthening and the volume fraction of Cu-rich and Mg-rich intermetallics, can be used to select the alloys for given strength and ductility, provided the Fe content stays below the Si-dependent critical level for the formation of pre-eutectic alpha-phase particles or beta-phase plates.

Evaluation of silicon twinning in hypo-eutectic Al-Si alloys

It is generally accepted that growth of eutectic silicon in aluminium-silicon alloys occurs by a twin plane re-entrant edge (TPRE) mechanism. It has been proposed that modification of eutectic silicon by trace additions occurs due to a massive increase in the twin density caused by atomic effects at the growth interface. In this study, eutectic microstructures and silicon twin densities in samples modified by elemental additions of barium (Ba), calcium (Ca), yttrium (Y) and ytterbium (Yb) (elements chosen due to a near-ideal atomic radii for twinning) in an A356.0 alloy have been determined by optical microscopy, thermal analysis, X-ray diffractometry (XRD) and transmission electron microscopy (TEM). Addition of barium or calcium caused the silicon structure to transform to a fine fibrous morphology, while the addition of yttrium or ytterbium resulted in a refined plate-like eutectic structure. Twin densities in all modified samples are higher than in unmodified alloys, and there are no significant differences between fine fibrous modification (by Ba and Ca) and refined plate-like modification (by Y and Yb). The twin density in all modified samples is less than expected based on the predictions by the impurity induced twining model. Based on these results it is difficult to explain the modification with Ba, Ca, Y and Yb by altered twin densities alone.