Modelling of microstructure formation and evolution during solidification

A comprehensive probabilistic model for simulating microstructure formation and evolution during solidification has been developed, based on coupling a Finite Differential Method (FDM) for macroscopic modelling of heat diffusion to a modified Cellular Automaton (mCA) for microscopic modelling of nucleation, growth of microstructures and solute diffusion. The mCA model is similar to Nastac's model for handling solute redistribution in the liquid and solid phases, curvature and growth anisotropy, but differs in the treatment of nucleation and growth. The aim is to improve understanding of the relationship between the solidification conditions and microstructure formation and evolution. A numerical algorithm used for FDM and mCA was developed. At each coarse scale, temperatures at FDM nodes were calculated while nucleation-growth simulation was done at a finer scale, with the temperature at the cell locations being interpolated from those at the coarser volumes. This model takes account of thermal, curvature and solute diffusion effects. Therefore, it can not only simulate microstructures of alloys both on the scale of grain size (macroscopic level) and the dendrite tip length (mesoscopic level), but also investigate nucleation mechanisms and growth kinetics of alloys solidified with various solute concentrations and solidification morphologies. The calculated results are compared with values of grain sizes and solidification morphologies of microstructures obtained from a set of casting experiments of Al-Si alloys in graphite crucibles.

Alloying of pure magnesium with Mg-33.3 wt-%Zr master alloy

To capitalise on the strengthening potential of zirconium as a potent grain refiner for magnesium alloys, the mechanisms of adding zirconium to magnesium and its subsequent grain refining action need to be understood. Using a Mg-33.3Zr master alloy (Zirmax supplied by Magnesium Elektron Ltd) as a zirconium alloying additive, the influence of different alloying conditions on the dissolution of zirconium in magnesium was investigated. It was found that owing to the highly alloyable microstructure of Zirmax, the dissolution of zirconium was generally complete within a few minutes in the temperature range 730 to 780degreesC. Prolonging and/or intensifying stirring were found to have no conspicuous influence on further enhancing the dissolution of zirconium. In all cases studied, the average grain size increased with increasing holding time at temperature while the total zirconium content decreased. The finest grain structure and highest total zirconium content corresponded to sampling immediately after stirring. Pick up of iron by molten magnesium from the mild steel crucibles used for melting and holding, was significantly delayed or avoided in the temperature range 730 to 780degreesC by coating the crucibles with boron nitride. It is therefore feasible to conduct zirconium alloying at 730degreesC without the need of a considerable excess of Zirmax addition using a properly coated or lined steel crucible.

Effect of iron on grain refinement of high-purity MG-Al alloys

The effect of iron on the grain refinement of high-purity Mg-3%Al and Mg-91%Al alloys has been investigated using anhydrous FeCl3 as an iron additive at 750degreesC in carbon-free aluminium titanite crucibles. It was shown that grain refinement was readily achievable for both alloys. Fe- and Al-rich intermetallic particles were observed in many magnesium grains. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

The effect of manganese on the grain size of commercial AZ31 alloy

The effect of manganese on gain refinement of a commercial AZ31 alloy has been investigated using an Al-60%Mn master alloy splatter as an alloying additive at 730 degrees C in aluminium titanite crucibles. It is shown that grain refinement by manganese is readily achievable in AZ31. Electron microprobe analyses reveal that prior to the addition of extra manganese the majority of the intermetallic particles found in AZ31 are of the AL(8)Mn(5) type. However, after the addition of extra manganese in the range from 0.1% to 0.8%, the predominant group of intermetallic particles changes to the metastable AlMn type. This leads to a hypothesis that the metastable AlMn intermetallic particles are more effective than Al8Mn5 as nucleation sites for magnesium grains. The hypothesis is supported by the observation that a long period of holding at 730 degrees C leads to an increase in grain size, due probably to the transformation of the metastable AlMn to the stable Al8Mn5. The hypothesis has also been used to understand the mechanism of grain refinement by superheating.