Functionalisation of nanoparticles as electrolytes in fuel cells

Inorganic metal oxide materials are generally poor proton conductors as conductivities are lower than 10-5-10-6 S.cm-1. However, by functionalising Silica, Zirconia or Titania, proton conduction increases by up to 5 orders of magnitude. Hence, functionalised nanomaterials are becoming very competitive against conventional electrolyte materials such as Nafion. In this work, sol-gel processes are employed to produce silica phosphate, zirconia phosphate and titania phosphate functionalised nanoparticles. Furthermore, conductivities at hydrate conditions are investigated, and nanoparticle formation and functionalisation effects on proton conductivity are discussed. Results show conductivities up to 10-1 S.cm-1 (95% RH). Proton conduction increases with the functionalisation content, however heat treatment of nanoparticles locks the functionality in the crystal phase, thus inhibiting proton conduction. Controlling the mesopore phase allows for high proton conduction at hydrated conditions, clearly indicating facilitated ion transport through the pore channels.

Improvement of the electrolytic properties of Y2O3-based materials using a crystallographic index

Y2O3 is a c-type rare earth oxide with a fluorite-related structure. This material has been used to refractory because of its high thermal stability and excellent resistance to hydration. In this study, the effective index was suggested in order to improve the electrolytic properties of Y2O3-based oxide. (CexY1-x)(2)O3+delta (x = 0.25 and 0.3) and [LaaSrbCe0.25Y(1-a-b)](2)O3+delta (a = 0.05, 0.1 and 0.15, b = 0, 0.006 and 0.0125) were prepared as the examples with intermediate and high index, respectively. The specimens with high index value such as (La0.15Ce0.25Y0.60)(2)O-3.25 and (La0.1Sr0.0125Ce0.25Y0.6375)(2)O-3.24 consisted of two phases such as c-type and fluorite, although (Ce0.25Y0.75)(2)O-3.25 with intermediate index value had a single phase of c-type rare earth oxide. Microanalysis indicates that a grain in the (La0.1Sr0.0125Ce0.25Y0.6375)(2)O-3.23(7) sintered body consists of c-type and fluorite phases. An interface between c-type and fluorite phases is coherent in a grain. This suggests that this effective index guides the crystal structure in the specimen to fluorite and the examined composition introduces the interface between c-type and fluorite in the microstructure. The electrochemical properties of specimens including Y2O3 were characterized on the basis of the suggested index. The electrical conductivity of Y2O3-based materials increased with an increase of the index. The apparent activation energy of Y2O3-based materials decreased with increasing index. The ionic transport number of oxygen of the specimens was improved by enhancement of the index, confirming validity of the index. The oxide ionic conductive region of (La0.1Sr0.0125Ce0.25Y0.(6375))(2)O-3.23(7) with high effective index extended up to P-O2 = 10(-18) atm at 800 degreesC, although the specimens with low or intermediate index showed p- or n-type semi-conduction in the same P-O2 region at 800 and 1000 degreesC. These results suggest that the interface between c-type and fluorite phases also contributes to improve the electrolytic properties in the grain. It is concluded that the improvement of electrolytic properties in Y2O3-based materials is attributable to the microstructure with interface between two phases in a grain and the fluorite structure guided by the suggested index. (C) 2001 Published by Elsevier Science B.V.

A study of the vacuum gamma-radiolysis of two aromatic polyimide fluoropolymers containing phenylphosphine oxide

The vacuum gamma -radiolysis of two fluorinated polyimides containing phenylphosphine oxide units, TOR-RC and TOR-RC ODPA, have been studied at 77 K and 300 K. The phenyl phosphine oxide units provide protection of the polymers towards oxidation by oxygen atoms and the bulky fluoromethyl groups reduce the colouration of the polymers by limiting donor-acceptor complex formation through the aromatic units. At 77 K the radicals formed were identified to be a mixture of neutral radicals (60%) and anion radicals. At 300 K only neutral radicals were found. The G-values for radical formation were found to be 0.50 and 0.42 at 77 K and 0.051 and 0.052 at 300 K for TOR-RC and TOR-RC ODPA, respectively. Little change was observed in the visible spectra of the polyimides following vacuum radiolysis at 300 K up to a dose of 3.3 MGy, and the polymers were shown to undergo net cross linking with a gel dose of 0.45 MGy.

A study of the oxidation of two aromatic polyimide fluoropolymers containing phenylphosphine oxide by a water plasma and gamma-radiolysis in air

The oxidation of two fluorinated polyimides containing phenylphosphine oxide units, TOR-RC and TOR-RC ODPA, have been studied at 300 K for treatment by a water plasma and gamma -radiolysis in air. The changes in the O 1s/C 1s ratios obtained from x-ray photoelectron spectroscopy (XPS) analysis showed that for exposure to the water plasma the ratio increases at short exposure times and then levels to a constant value. Evidence for the formation of phosphate species was also obtained from the XPS analyses. Similar observations were made for gamma -radiolysis of the polymers in air. The polymers containing phenylphosphine oxide were found to be more resistant to oxidation in the water plasma than Kapton(R). Radiolysis of the polymers in air to high doses were also accompanied by a red shift in the visible absorption spectra.

Conductive hearing loss in preterm infants with bronchopulmonary dysplasia

Objective: To determine the risk of conductive hearing loss in preterm infants with bronchopulmonary dysplasia (BPD) and preterm controls. Methodology: The study population consisted of 78 infants with BPD of 26-33 weeks gestation and 78 controls of similar gestational age matched for broad-based birthweight categories. An auditory brainstem response (ABR) audiology was performed shortly before hospital discharge. Visual reinforcement orientation audiometry (VROA) and impedance audiometry were performed at 8-12 months corrected for prematurity. Infants with persistent audiological abnormalities were referred for evaluation to paediatric ENT surgeons. Results: Infants with BPD had a significantly higher rate of ABR abnormalities (BPD: 22%, controls: 9%; P = 0.028). On VROA and impedance audiometry, the infants with BPD also had a higher rate of persistent abnormalities. Following ENT assessment, 22.1% of infants with BPD and 7.7% of controls had persistent conductive dysfunction requiring myringotomy and grommet tube insertion (P = 0.03). Most of these infants had normal ABR audiometry at hospital discharge. Conclusions: Preterm infants with BPD are at high risk of persistent conductive hearing loss late in the first year of life compared to controls. An ABR audiology conducted at the time of hospital discharge does not predict accurately later conductive hearing problems. Infants with BPD should have routine audiological evaluation toward the end of the first year of life.

Synthesis and characterization of nano-hetero-structured dy doped CeO2 solid electrolytes using a combination of spark plasma sintering and conventional sintering

Doped ceria (CeO2) compounds are fluorite-type oxides that show oxide ionic conductivity higher than yttria-stabilized zirconia in oxidizing atmosphere. As a consequence of this, considerable interest has been shown in application of these materials for low (500 degrees-650 degrees C) temperature operation of solid oxide fuel cells (SOFCs). To improve the conductivity in dysprosium (Dy) doped CeO2, nano-size round shape particles were prepared using a coprecipitation method. The dense sintered bodies with small grain sizes (< 300 nm) were fabricated using a combined process of spark plasma sintering (SPS) and conventional sintering (CS). Dy-doped CeO2 sintered body with large grains (1.1 mu m) had large micro-domains. The conductivity in the sintered body was low (-3.2 S/cm at 500 degrees C). On the other hand, the conductivity in the specimens obtained by the combined process was considerably improved. The micro-domain size in the grain was minimized using the present process. It is concluded that the enhancement of conductivity in dense specimens produced by the combined process (SPS+CS) is attributable to the microstructural changes within the grains.

Design of high quality doped CeO2 solid electrolytes with nanohetero structure

Doped ceria (CeO2) compounds are fluorite related oxides which show oxide ionic conductivity higher than yttria-stabilized zirconia in oxidizing atmosphere. As a consequence of this, a considerable interest has been shown in application of these materials for low (400-650 degrees C) temperature operation of solid oxide fuel cells (SOFCs). In this paper, our experimental data about the influence of microstructure at the atomic level on electrochemical properties were reviewed in order to develop high quality doped CeO2 electrolytes in fuel cell applications. Using this data in the present paper, our original idea for a design of nanodomain structure in doped CeO2 electrolytes was suggested. The nanosized powders and dense sintered bodies of M doped CeO2 (M:Sm,Gd,La,Y,Yb, and Dy) compounds were fabricated. Also nanostiructural features in these specimens were introduced for conclusion of relationship between electrolytic properties and domain structure in doped CeO2. It is essential that the electrolytic properties in doped CeO2 solid electrolytes reflect in changes of microstructure even down to the atomic scale. Accordingly, a combined approach of nanostructure fabrication, electrical measurement and structure characterization was required to develop superior quality doped CeO2 electrolytes in the fuel cells.

Characterization of titanium phosphate as electrolytes in fuel cells

Titanium phosphate is currently a promising material for proton exchange membrane fuel cells applications (PEMFC) allowing for operation at high temperature conditions. In this work, titanium phosphate was synthesized from tetra iso-propoxide (TTIP) and orthophosphoric acid (H3PO4) in different ratios by a sol gel method. High BET surface areas of 271 m(2).g(-1) were obtained for equimolar Ti:P samples whilst reduced surface areas were observed by varying the molar ratio either way. Highest proton conductivity of 5.4 x 10(-2) S.cm(-1) was measured at 20 degrees C and 93% relative humidity (RH). However, no correlation was observed between surface area and proton conductivity. High proton conductivity was directly attributed to hydrogen bonding in P-OH groups and the water molecules retained in the sample structure. The proton conductivity increased with relative humidity, indicating that the Grotthuss mechanism governed proton transport. Further, sample Ti/P with 1:9 molar ratio showed proton conductivity in the order of 10(-1) S.cm(-1) (5% RH) and similar to 1.6x10(-2) S.cm(-1) (anhydrous condition) at 200 degrees C. These proton conductivities were mainly attributed to excess acid locked into the functionalized TiP structure, thus forming ionisable protons.

Microstructures and electrolytic properties of yttrium-doped ceria electrolytes: Dopant concentration and grain size dependences

The microstructures and electrolytic properties of YxCe1-xO2-x/2 (x = 0.10-0.25) electrolytes with average grain size in the range 90 nm-1.7 mu m were systematically investigated. Through detailed transmission electron microscopy characterization, nanosized domains were observed. The relationship of the domains, the doping level and grain sizes were determined, and their impacts on the electrolytic properties were systematically studied. It was found that the formation of domains has a negative impact on the electrolytic properties, so that electrolytic properties can be adjusted through careful control of domain formation, doping level and grain size. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Potential errors in the application of mixture theory to multifrequency bioelectrical impedance analysis

Potential errors in the application of mixture theory to the analysis of multiple-frequency bioelectrical impedance data for the determination of body fluid volumes are assessed. Potential sources of error include: conductive length; tissue fluid resistivity; body density; weight and technical errors of measurement. Inclusion of inaccurate estimates of body density and weight introduce errors of typically < +/-3% but incorrect assumptions regarding conductive length or fluid resistivities may each incur errors of up to 20%.

Conductivity, NMR and crystallographic study of N,N,N,N-tetramethylammonium dicyanamide plastic crystal phases: an archetypal ambient temperature plastic electrolyte material

N,N,N,N-Tetramethylammonium dicyanamide (Me(4)NDCA) has been examined via differential scanning calorimetry (DSC), thermogravimetric analysis, conductivity, single crystal X-ray diffraction and H-1 nuclear magnetic resonance (NMR) analyses, and was found to be highly conductive in the solid state (sigma = 10(-3) S cm(-2) at 420 K) and to also exhibit unusual plastic crystal behaviour. To investigate the correlation between such behaviour and the occurrence of molecular rotations in the crystal, H-1 NMR second moment measurements are compared with calculated values predicted from the crystal structure. While DSC analysis indicates a number of solid-solid transitions at ambient temperatures, subsequent H-1 NMR analysis of the Me4N+ cation shows that a variety of rotational motions become active at low (