ESEM observations of SCC initiation for 4340 high strength steel in distilled water

The stress corrosion cracking (SCC) initiation process for 4340 high strength steel in distilled water at room temperature was studied using a new kind of instrument: an environmental scanning electron microscope (ESEM). It was found that the applied stress accelerated oxide film formation which has an important influence on the subsequent SCC initiation. SCC was observed to initiate in the following circumstances: (1) cracking of a thick oxide film leading to SCC initiation along metal grain boundaries, (2) the initiation of pits initiating SCC in the metal and (3) SCC initiating from the edge of the specimen. All these three SCC initiation circumstances are consistent with the following model which couples SCC initiation with cracking of a surface protective oxide. There is a dynamic interaction between oxide formation, the applied stress, oxide cracking, pitting and the initiation of SCC. An aspect of the dynamic interaction is cracks forming in a protective surface oxide because of the applied stress, exposing to the water bare metal at the oxide crack tip, and oxidation of the bare metal causing crack healing. Oxide crack healing would be competing with the initiation of intergranular SCC if an oxide crack meets the metal surface at a grain boundary. If the intergranular SCC penetration is sufficiently fast along the metal grain boundary, then the crack yaws open preventing healing of the oxide crack. If intergranular SCC penetration is not sufficiently fast, then the oxidation process could produce sufficient oxide to fill both the stress corrosion crack and the oxide crack; in this case there would be initiation of SCC but only limited propagation of SCC. Stress-induced cracks in very thin oxide can induce pits which initiate SCC, and under some conditions such stress induced cracks in a thin oxide can directly initiate SCC.

Synthesis of silica films at the air/water interface: Effect of template chain length and ionic strength

We have grown surfactant-templated silicate films at the air-water interface using n-alkyltrimethylammonium bromide and chloride in an acid synthesis with tetraethyl orthosilicate as the silicate source. The films have been grown with and without added salt (sodium chloride, sodium bromide) and with n-alkyl chain lengths from 12 to 18, the growth process being monitored by X-ray reflectometry. Glassy, hexagonal, and lamellar structures have been produced in ways that are predictable from the pure surfactant-water phase diagrams. The synthesis appears to proceed initially through an induction period characterized by the accumulation of silica-coated spherical micelles near the surface. All syntheses, except those involving C(12)TACl, show a sudden transformation of the spherical micellar phase to a hexagonal phase. This occurs when the gradually increasing ionic strength and/or changing ethanol concentration is sufficient to change the position of boundaries within the phase diagram. A possible mechanism for this to occur may be to induce a sphere to rod transition in the micellar structure. This transformation, as predicted from the surfactant-water phase diagram, can be induced by addition of salts and is slower for chloride than bromide counteranions. The hexagonal materials change in cell dimension as the chain length is changed in a way consistent with theoretical model predictions. All the materials have sufficiently flexible silica frameworks that phase interconversion is observed both from glassy to hexagonal and from hexagonal, to lamellar and vice versa in those surfactant systems where multiple phases are found to exist.

Adsorption hysteresis and criticality in regular mesoporous materials

In the present work, various theories predicting the critical diameter for the absence of capillary condensation and hysteresis are applied to experimental adsorption isotherms of vapors on regular mesoporous materials. Among the various theories studied, the tensile strength approximation proposed by the authors was found to be the most successful. Reversibility of nitrogen adsorption at 77.4 K was studied on pure MCM-41 of various pore sizes, as well as mixtures of pure MCM-41 samples in a 1:1 ratio. The results of PSD and hysteresis on MCM-41 mixtures are close to that expected from studies of the pure materials. The estimates of hysteresis critical temperature and diameter of MCM-41, HMS, FSM and KIT materials are also provided.

Loose abrasive truing and dressing of resin bond diamond cup wheels for grinding fibre optic connectors

A loose abrasive lapping technology was developed for truing and dressing ultrafine diamond cup wheels for grinding spherical end faces of fibre optic connectors. The relative densities of exposed grits and grit pull-outs measured from wheel surfaces prepared using the loose abrasive lapping and the bonded abrasive dressing were compared. It was found that the lapping method with loose abrasives produced wheel surfaces with more exposed grits and less grit pull-outs, especially for finer grit size wheels. For dressing ultrafine grit size wheels, the particle size of the lapping paste should be smaller than the wheel grit size to achieve a better result. It is also found that the wheels dressed using the lapping method demonstrate an excellent grinding performance. (C) 2004 Elsevier B.V.. All rights reserved.

High speed versus conventional grinding in high removal rate machining of alumina and alumina-titania

High removal rate (up to 16.6 mm(3)/s per mm) grinding of alumina and alumina-titania was investigated with respect to material removal and basic grinding parameters using a resin-bond 160 mu m grit diamond wheel at the speeds of 40 and 160 m/s, respectively. The results show that the material removal for the single-phase polycrystalline alumina and the two-phase alumina-titania composite revealed identical mechanisms of microfracture and grain dislodgement under the grinding conditioned selected. There were no distinct differences in surface roughness and morphology for both materials ground at either conventional or high speed. An increase in material removal rate did not necessarily worsen the surface toughness for the two materials at both speeds. Also the grinding forces for the two ceramics demonstrated similar characteristics at any grinding speeds and specific removal rates. Both normal and tangential grinding forces and their force ratios at the high speed were lower than those at the conventional speed, regardless of removal rates. An increase in specific removal rate caused more rapid increases in normal and tangential forces obtained at the conventional grinding speed than those at the high speed. Furthermore, it is found that the high speed grinding at all the removal rates exerted a great amount of coolant-induced normal forces in grinding zone, which were 4-6 times higher than the pure normal grinding forces. (c) 2004 Elsevier Ltd. All rights reserved.

Polarised infrared and differential scanning calorimetry studies on oriented vinyl pipe materials

The molecular orientation in a conventionally extruded PVC pipe, a uniaxially oriented PVC pipe and a biaxially oriented PVC pipe has been studied via Infrared dichroism. The degree of order or crystallinity has also been studied by Differential Scanning Calorimetry and also via Infrared Spectroscopy. The fundamental structural difference between the conventional and oriented pipes was that polymer chains were preferentially aligning in the hoop direction for oriented pipes whereas they were fairly isotropic in the conventional pipe with a slight preferential alignment in the axial direction. Analysis of the C-Cl stretching mode indicated that the uniaxially oriented pipe had much higher alignment of the C-Cl bond in the axial direction than the biaxial pipe, which correlates with higher fracture toughness for circumferential cracking in the biaxial pipe. Both DSC and Infrared spectroscopy detected little change in the crystallinity or order in the oriented pipes compared to the conventionally extruded pipes. (C) 2002 Kluwer Academic Publishers.

The strength of concentrated Mg-Zn solid solutions

Solid solution effects on the hardness and flow stress have been studied for zinc contents between 0.2 and 2.4 at% (0.5 and 6.9 wt%) in Mg. The alloys were grain refined with 0.6 wt% zirconium to ensure a similar grain size at all compositions. The hardness increases with the zinc content as Hv(10) (kg mm(-2)) = 9 Zn (at%) + 33. At low solute concentrations the (0.2%) proof strength does not change significantly with concentration. At concentrations above 0.7 at%, within the supersaturated solid solution region, the rate of solid solution hardening is high, following a c(2) rule, where c is the atom fraction of Zn. It is suggested that short-range order may account for most of the observed strengthening in concentrated Mg-Zn alloys.