The effect of the CaO/SiO2 ratio on the phase equilibria in the ZnO-“Fe2O3”-(PbO + CaO + SiO2) system in air: CaO/SiO2 = 0.1, PbO/(CaO + SiO2) = 6.2, and CaO/SiO2 = 0.6, PbO/(CaO + SiO2) = 4.3

Experimental studies on phase equilibria in the multi-component system PbO-ZnO-CaO-SiO2-FeO-Fe2O3 in air have been conducted to characterize the phase relations of a complex slag system used in the oxidation smelting of lead and in typical lead blast furnace sinters. The liquidus in two pseudoternary sections ZnO-Fe2O3-(PbO + CaO + SiO2) with the CaO/SiO2 weight ratio of 0.1 and the PbO/(CaO + SiO2) weight ratio of 6.2, and with CaO/SiO2 weight ratio of 0.6 and the PbO/(CaO + SiO2) weight ratio of 4.3, have been constructed.

Effect of Al2O3 and Cr2O3 on loquidus temperatures in the cristobalite and tridymite primary phase fields of the MgO-"FeO"-SiO2 ststem in equilibrium with metallic iron

The effects of alumina and chromite impurities on the liquidus temperatures in the cristobalite/tridymite (SiO2) primary phase fields in the MgO-FeO-SiO, system in equilibrium with metallic iron have been investigated experimentally. Using high temperature equilibration and quenching followed by electron probe X-ray microanalysis (EPMA), liquiclus isotherms have been determined in the temperatures range 1 673 to 1 898 K. The results are presented in the form of pseudo-ternary sections of the MgO-FeO-SiO, system at 2, 3 and 5 wt% Al2O3, 2 wt% Cr2O3, and 2 wt% Cr2O3+2 wt% Al2O3. The study enables the liquidus to be described for a range of SiO2/MgO and MgO/FeO ratios. It was found that liquiclus temperatures in the cristobalite and tridymite primary phase fields, decrease significantly with the addition of Al2O3 and Cr2O3.