Immobilization of aluminum chloride on MCM-41 as a new catalyst system for liquid-phase isopropylation of naphthalene

A great deal of effort has been made at searching for alternative catalysts to replace conventional Lewis acid catalyst aluminum trichloride (AlCl3). In this paper, immobilization of AlCl3 on mesoporous MCM-41 silica with and without modification was carried out. The catalytic properties of the immobilized catalyst systems for liquid-phase isopropylation of naphthalene were studied and compared with those of H/MCM-41 and H/mordenite. The structures of the surface-immobilized aluminum chloride catalysts were studied and identified by using solid-state magic angle spinning nuclear magnetic resonance (MAS NMR), Fourier transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), nitrogen adsorption, and X-ray diffraction (XRD) techniques. The catalytic activity of the immobilized catalysts was found to be similar to that of acidic mordenite zeolite. A significant enhancement in the selectivity of 2,6-diisopropylnaphthalene (2,6-DIPN) was observed over the immobilized aluminum chloride catalysts. Immobilization of aluminum chloride on mesoporous silica coupled with surface silylation is a promising way of developing alternative catalyst system for liquid-phase Friedel-Crafts alkylation reactions. (C) 2002 Elsevier Science B.V. All rights reserved.

Rapid manufacturing of aluminum components

A manufacturing technique for the production of aluminum components is described. A resin-bonded part is formed by a rapid prototyping technique and then debound and infiltrated by a second aluminum alloy under a nitrogen atmosphere. During thermal processing, the aluminum reacts with the nitrogen and is partially transformed into a rigid aluminum nitride skeleton, which provides the structural rigidity during infiltration. The simplicity and rapidity of this process in comparison to conventional production routes, combined with the ability to fabricate complicated parts of almost any geometry and with high dimensional precision, provide an additional means to manufacture aluminum components.

Damage by eutectic particle cracking in aluminum casting alloys A356/357

The strain dependence of particle cracking in aluminum alloys A356/357 in the T6 temper has been studied in a range of microstructures produced by varying solidification rate and Mg content, and by chemical (Sr) modification of the eutectic silicon. The damage accumulates linearly with the applied strain for all microstructures, but the rate depends on the secondary dendrite arm spacing and modification state. Large and elongated eutectic silicon particles in the unmodified alloys and large pi-phase (Al9FeMg3Si5) particles in alloy A357 show the greatest tendency to cracking. In alloy A356, cracking of eutectic silicon particles dominates the accumulation of damage while cracking of Fe-rich particles is relatively unimportant. However, in alloy A357, especially with Sr modification, cracking of the large pi-phase intermetallics accounts for the majority of damage at low and intermediate strains but becomes comparable with silicon particle cracking at large strains. Fracture occurs when the volume fraction of cracked particles (eutectic silicon and Fe-rich intermetallics combined) approximates 45 pct of the total particle volume fraction or when the number fraction of cracked particles is about 20 pct. The results are discussed in terms of Weibull statistics and existing models for dispersion hardening.

Simple texture-based liberation modelling of ores

Mineralogical analysis is often used to assess the liberation properties of particles. A direct method of estimating liberation is to actually break particles and then directly obtain liberation information from applying mineralogical analysis to each size-class of the product. Another technique is to artificially apply random breakage to the feed particle sections to estimate the resultant distribution of product particle sections. This technique provides a useful alternative estimation method. Because this technique is applied to particle sections, the actual liberation properties for particles can only be estimated by applying stereological correction. A recent stereological technique has been developed that allows the discrepancy between the linear intercept composition distribution and the particle section composition distribution to be used as guide for estimating the particle composition distribution. The paper will show results validating this new technique using numerical simulation. (C) 2004 Elsevier Ltd. All rights reserved.

Eutectic grains in unmodified and strontium-modified hypoeutectic aluminum-silicon alloys

Additions of strontium to hypoeutectic aluminum-silicon alloys modify the morphology of the eutectic silicon phase from a coarse platelike structure to a fine fibrous structure. Thermal analysis, interrupted solidification, and microstructural examination of sand castings in this work revealed that, in addition to a change in silicon morphology, modification with strontium also causes an increase in the size of eutectic grains. The eutectic grain size increases because fewer grains nucleate, possibly due to poisoning of the phosphorus-based nucleants, that are active in the unmodified alloy. A simple growth model is developed to estimate the interface velocity during solidification of a eutectic grain. The model confirms, independent of microstructural observations, that the addition of 100 ppm strontium increases the eutectic grain size by at least an order of magnitude compared with the equivalent unmodified alloy. The model predicts that the growth velocity varies significantly during eutectic growth. At low strontium levels, these variations may be sufficient to cause transitions between flake and fibrous silicon morphologies depending on the casting conditions. The model can be used to rationally interpret the eutectic grain structure and silicon morphology of fully solidified aluminum-silicon castings and, when coupled with reliable thermal data, can be used to estimate the eutectic grain size.

Timing, magnitude, and location of initial soluble aluminum injuries to mungbean roots

Despite a century's knowledge that soluble aluminum (Al) is associated with acid soils and poor plant growth, it is still uncertain how Al exerts its deleterious effects. Hypotheses include reactions of Al with components of the cell wall, plasmalemma, or cytoplasm of cells close to the root tip, thereby reducing cell expansion and root growth. Digital microscopy was used to determine the initial injuries of soluble Al to mungbean (Vigna radiata L.) roots. Roots of young seedlings were marked with activated carbon particles and grown in 1 mm CaCl2 solution at pH 6 for ca. 100 min (control period), and AlCl3 solution was added to ensure a final concentration of 50 muM Al (pH 4). Further studies were conducted on the effects of pH 4 with and without 50 muM Al. Four distinct, but possibly related, initial detrimental effects of soluble Al were noted. First, there was a 56-75% reduction in the root elongation rate, first evident 18-52 min after the addition of Al, root elongation continuing at a decreased rate for ca. 20 It. Decreasing solution pH from 6 to 4 increased the root elongation rate 4-fold after 5 min, which decreased to close to the original rate after 130 min. The addition of Al during the period of rapid growth at pH 4 reduced the root elongation rate by 71% 14 min after the addition of Al. The activated carbon marks on the roots showed that, during the control period, the zone of maximum root growth occurred at 2,200-5,100 mum from the root tip (i.e. the cell elongation zone). It was there that Al first exerted its detrimental effect and low pH increased root elongation. Second, soluble Al prevented the progress of cells from the transition to the elongation phase, resulting in a considerable reduction of root growth over the longer term. The third type of soluble Al injury occurred after exposure for ca. 4 h to 50 mum Al when a kink developed at 2,370 mum from the root tip. Fourth, ruptures of the root epidermal and cortical cells at 1,900-2,300 mum from the tip occurred greater than or equal to4.3 h after exposure to soluble Al. The timing and location of Al injuries support the contention that Al initially reduces cell elongation, thus decreasing root growth and causing damage to epidermal and cortical cells.

Experimental study of phase equilibria in the Al-Fe-Zn-O system in air

The phase equilibria in the Al-Fe-Zn-O system in the range 1250 °C to 1695 °C in air have been experimentally studied using equilibration and quenching techniques followed by electron probe X-ray microanalysis. The phase diagram of the binary Al2O3-ZnO system and isothermal sections of the Al2O3-“Fe2O3”-ZnO system at 1250 °C, 1400 °C, and 1550 °C have been constructed and reported for the first time. The extents of solid solutions in the corundum (Al,Fe)2O3, hematite (Fe,Al)2O3, Al2O3*Fe2O3 phase (Al,Fe)2O3, spinel (Al,Fe,Zn)O4, and zincite (Al,Zn,Fe)O primary phase fields have been measured. Corundum, hematite, and Al2O3*Fe2O3 phases dissolve less than 1 mol pct zinc oxide. The limiting compositions of Al2O3*Fe2O3 phase measured in this study at 1400 °C are slightly nonstoichiometric, containing more Al2O3 then previously reported. Spinel forms an extensive solid solution in the Al2O3-“Fe2O3”-ZnO system in air with increasing temperature. Zincite was found to dissolve up to 7 mole pct of aluminum in the presence of iron at 1550 °C in air. A meta-stable Al2O3-rich phase of the approximate composition Al8FeZnO14+x was observed at all of the conditions investigated. Aluminum dissolved in the zincite in the presence of iron appears to suppress the transformation from a round to platelike morphology.

XPS study of basic aluminum sulphate and basic aluminium nitrate

Basic aluminium sulphate and nitrate crystals were prepared by forced hydrolysis of aluminium salt solution followed by precipitation with a sulphate solution or by evaporation for the basic aluminium nitrate. X-ray Photoelectron Spectroscopy (XPS) confirms the chemical composition determined by ICP-AES in earlier work. High resolution XPS scans of the individual elements allow the identification of both the central (AlO4)-Al-IV group and the 12 aluminium octahedra in the [IVAlO4AlVI(OH)(24)(H2O)(12)] building unit by two Al 2p transitions with binding energies of 73.7 and 74.2 eV in both the basic aluminium sulphate and nitrate. Four different types of oxygen atoms were identified in the basic aluminium sulphate associated with the central AlO4, OH, H2O and SO4 groups in the crystal structure with transitions at 529.4, 530.1, 530.7 and 531.8 eV, respectively. (c) 2005 Elsevier B.V. All rights reserved.

Crystallographic study of grain refinement in aluminum alloys using the edge-to-edge matching model

The edge-to-edge matching model for describing the interfacial crystallographic characteristics between two phases that are related by reproducible orientation relationships has been applied to the typical grain refiners in aluminum alloys. Excellent atomic matching between Al3Ti nucleating substrates, known to be effective nucleation sites for primary Al, and the Al matrix in both close packed directions and close packed planes containing these directions have been identified. The crystallographic features of the grain refiner and the Al matrix are very consistent with the edge-to-edge matching model. For three other typical grain refiners for Al alloys, TiC (when a = 0.4328 nm), TiB2 and AIB(2), the matching only occurs between the close packed directions in both phases and between the second close packed plane of the Al matrix and the second close packed plane of the refiners. According to the model, it is predicted that Al3Ti is a more powerful nucleating substrate for Al alloy than TiC, TiB2 and AlB2. This agrees with the previous experimental results. The present work shows that the edge-to-edge matching model has the potential to be a powerful tool in discovering new and more powerful grain refiners for Al alloys. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.