Galvanic corrosion of magnesium alloy AZ91D in contact with an aluminium alloy, steel and zinc

An investigation was carried out into the galvanic corrosion of magnesium alloy AZ91D in contact with zinc, aluminium alloy A380 and 4150 steel. Specially designed test panels were used to measure galvanic currents under salt spray conditions. It was found that the distributions of the galvanic current densities on AZ91D and on the cathodes were different. An insulating spacer between the AZ91D anode and the cathodes could not eliminate galvanic corrosion. Steel was the worst cathode and aluminium the least aggressive to AZ91D. Corrosion products from the anode and cathodes appeared to be able to affect the galvanic corrosion process through an alkalisation, passivation, poisoning effect or shortcut effect. (C) 2003 Elsevier Ltd. All rights reserved.

Corrosion resistance of aged die cast magnesium alloy AZ91D

The corrosion behaviour of die cast magnesium alloy AZ91D aged at 160degreesC was investigated. The corrosion rate of the alloy decreases with ageing time in the initial stages and then increases again at ageing times greater than 45 h. The dependence of the corrosion rate on ageing time can be related to the changes in microstructure and local composition during ageing. Precipitation of the beta phase (Mg17Al12) occurs exclusively along the grain boundaries during ageing. The beta phase acts as a barrier, resulting in a decreasing corrosion rate in the initial stages of ageing. In the later stages, the decreasing aluminium content of alpha grains makes the alpha matrix more active, causing an increase in the corrosion rate. Electrochemical testing results also confirm the combined effects of the changes in alpha and beta phases on the corrosion resistance of the aged die cast AZ91D alloy. (C) 2003 Elsevier B.V. All rights reserved.

Improved corrosion resistance of AZ91D magnesium alloy by an aluminium-alloyed coating

An aluminum-alloyed coating was applied onto the surface of magnesium alloy AZ91D. The coating formed in aluminium powder at 420 degrees C is rich in the beta (Mg17Al12) phase. Polarisation curve, AC impedance, salt immersion and salt spray were carried out to investigate the corrosion behaviour and assess the corrosion performance of the coated magnesium alloy. It was found that a coated AZ91D specimen was much more corrosion resistant and harder than an uncoated one. The improved corrosion resistance was mainly ascribed to the high volume fraction of beta phase in the coating. (c) 2004 Elsevier B.V. All rights reserved.

Influence of anodising current on the corrosion resistance of anodised AZ91D magnesium alloy

The thickness, chemical composition and microstructure of anodised coatings formed on magnesium alloy AZ91D at various anodising current densities were measured. It was found that all these parameters could be affected by anodising current density, and hence the coatings formed at different anodising current densities had different corrosion resistances. This suggests that the corrosion performance of an anodised coating could be improved if a properly designed current waveform is used for anodising. In addition, based on the experimental results, some physical, chemical and electrochemical reactions involved in the anodising process were proposed to explain the anodising behaviour in this paper. (c) 2005 Elsevier Ltd. All rights reserved.

Effect of aging on yield stress and corrosion resistance of die cast magnesium alloy

Corrosion resistance is an important property that could be affected by the ageing process. In order to investigate whether aging affects the corrosion resistance, corrosion rate and yield strength of diecast magnesium alloy AZ91D were measured and analysed after ageing. It was found that the dependence of the corrosion rate on ageing time can be ascribed to the changes in microstructure of the alloy and chemical composition of its matrix. Precipitation of the P phase (Mg17Al12) occurred along the grain boundaries during the initial ageing stages, resulting in a decreasing corrosion rate and an inceasing yield strength. In the later stages, the decreasing aluminium content in the alpha matrix made it more active, causing an increase in the corrosion rate. The decrease in aluminium content in the matrix also leads to a decrease in yield strength.

Boundary element method predictions of the influence of the electrolyte on the galvanic corrosion of AZ91D coupled to steel

This research investigated the galvanic corrosion of the magnesium alloy AZ91D coupled to steel. The galvanic current distribution was measured in 5% NaCl solution, corrosive water and an auto coolant. The experimental measurements were compared with predictions from a Boundary Element Method (BEM) model. The boundary condition, required as an input into the BEM model, needs to be a polarization curve that accurately reflects the corrosion process. Provided that the polarization curve does reflect steady state, the BEM model is expected to be able to reflect steady state galvanic corrosion.

Simulation of galvanic corrosion of magnesium coupled to a steel fastener in NaCl solution

The galvanic corrosion of magnesium alloy AZ91D coupled to a steel fastener was studied using a boundary element method (BEM) model and experimental measurements. The BEM model used the measured polarization curves as boundary conditions. The experimental program involved measuring the total corrosion rate as a function of distance from the interface of the magnesium in the form of a sheet containing a mild steel circular insert (5 to 30 mm in diameter). The measured total corrosion rate was interpreted as due to galvanic corrosion plus self corrosion. For a typical case, the self corrosion was estimated typically to be similar to 230 mm/y for an area surrounding the interface and to a distance of about I cm from the interface. Scanning Kelvin Probe Force Microscopy (SKPFM) revealed microgalvanic cells with potential differences of approximately 100 mV across the AZ91D surface. These microgalvanic cells may influence the relative contributions of galvanic and self corrosion to the total corrosion of AZ91D.

Corrosion of magnesium alloys in commercial engine coolants

A number of magnesium alloys show promise as engine block materials. However, a critical issue for the automotive industry is corrosion of the engine block by the coolant and this could limit the use of magnesium engine blocks. This work assesses the corrosion performance of conventional magnesium alloy AZ91D and a recently developed engine block magnesium alloy AM-SC1 in several commercial coolants. Immersion testing, hydrogen evolution measurement, galvanic current monitoring and the standard ASTM D1384 test were employed to reveal the corrosion performance of the magnesium alloys subjected to the coolants. The results show that the tested commercial coolants are corrosive to the magnesium alloys in terms of general and galvanic corrosion. The two magnesium alloys exhibited slightly different corrosion resistance to the coolants with AZ91D being more corrosion resistant than AM-SC1. The corrosivity varied from coolant to coolant. Generally speaking. an oraganic-acid based long life coolant was less corrosive to the magnesium alloys than a traditional coolant. Among the studied commercial coolants. Toyota long, life coolant appeared to be the most promising one. In addition. it was found that potassium fluoride effectively inhibited corrosion of the magnesium alloys in the studied commercial coolants. Both general and galvanic corrosion rates were significantly decreased by addition of KF, and there were no evident side effects on the other engine block materials, such as copper, solder. brass. steel and aluminium alloys, in terms of their corrosion performance. The ASTM D 1384 test further confirmed these results and suggested that Toyota long life coolant with 1%wt KF addition is a promising coolant for magnesium engine blocks.

Corrosion behaviour of pure magnesium in a simulated body fluid

The corrosion behaviour of pure magnesium in Hank's simulated body fluid (SBF) was investigated. It was found that the polarization of Mg in the SBF solution was similar to that in a NaCl aqueous solution. However, AC impedance analysis suggested that the detailed dissolution steps involved in the corrosion of Mg in the SBF could be different in terms of their rates or contributions to corrosion damage of Mg. Moreover, the corrosion rate of Mg in the SBF solution was found to be increasing with time and significant hydrogen evolution and alkalization of the SBF solution resulting from corrosion of Mg were measured in the study. The results suggested that after some proper measures are taken to retard corrosion reaction, Mg can be successfully employed as a degradable and absorbable implant material.

Crystallographyof Mg17Al12 precipitates in AZ91D alloy

Kikuchi diffraction was used to accurately determine the orientation relationship (OR) between Mg17Al12 precipitates and matrix in an AZ91D alloy. For both continuous and discontinuous precipitations, the Burgers OR and the Potter OR were equally observed. The lattice parameter of Mg17Al12 associated with the former is bigger than that of the latter. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Corrosion behaviour of a pressure die cast magnesium alloy

High pressure die casting is the most important production method for casting magnesium alloy components, and uniformity of appearance is an important criterion for acceptance of a component by customers. This paper investigates the influence of uniformity in surface appearance of diecast AZ91D plates on their corrosion behaviour. Through immersion, hydrogen collection and weight loss measurements it was found that corrosion is more likely to occur on the areas of the plate that appear to be darker, leading to a non-uniformly corroded surface. Microstructural analysis showed that the non-uniformity in appearance is related to a difference in the morphology and distribution of porosity across the surface of a diecast AZ91D plate. The darker areas of the surface are high in porosity which breaks the continuity of the beta-phase network and provides shortcut paths for corrosion from the surface to the interior of the casting. The brighter shiny areas of the surface are much less porous, with isolated pores being confined by corrosion resistant beta-precipitates thus reducing the corrosion rate.