Dendrite coherency of Al-Si-Cu alloys

The dendrite coherency point of Al-Si-Cu alloys was determined by thermal analysis and rheological measurement methods by performing parallel measurements at two cooling rates for aluminum alloys across a wide range of silicon and copper contents. Contrary to previous findings, the two methods yield significantly different values for the fraction solid at the dendrite coherency point. This disparity is greatest for alloys of low solute concentration. The results from this study also contradict previously reported tl ends in the effect of cooling rate on the dendritic coherency point. Consideration of the results shows that thermal analysis is not a valid technique for the measurement of coherency. Analysis of the results from rheological testing indicates that silicon concentration has a dominant effect on grain size and dendritic morphology, independent of cooling rate and copper content, and thus is the factor that determines the fraction solid at dendrite coherency for Al-Si-Cu alloys.

Strength-ductility behaviour of Al-Si-Cu-Mg casting alloys in T6 temper

A comparative study of the mechanical properties of 20 experimental alloys has been carried out. The effect of different contents of Si, Cu, Mg, Fe and Mn, as well as solidification rate, has been assessed using a strength-ductility chart and a quality index-strength chart developed for the alloys. The charts show that the strength generally increases and the ductility decreases with an increasing content of Cu and Mg. Increased Fe (at Fe/Mn ratio 0.5) dramatically lowers the ductility and strength of low Si alloys. Increased Si content generally increases the strength and the ductility. The increase in ductility with increased Si is particularly significant when the Fe content is high. The charts are used to show that the cracking of second phase particles imposes a limit to the maximum achievable strength by limiting the ductility of strong alloys. The (Cu + Mg) content (at.%), which determines the precipitation strengthening and the volume fraction of Cu-rich and Mg-rich intermetallics, can be used to select the alloys for given strength and ductility, provided the Fe content stays below the Si-dependent critical level for the formation of pre-eutectic alpha-phase particles or beta-phase plates.

Iron-related porosity in Al-Si-(Cu) foundry alloys

An experimental program has been undertaken to explore the effect of iron concentration on porosity levels in Al-Si alloy sand castings. The effect of iron concentrations above, below and equal to the critical iron content for alloys with either 5 or 9% Si and either 0, 1 or 3% Cu has been determined. Increasing iron concentrations were found to increase porosity in all alloys except the copper-containing Al-5% Si alloys which displayed a porosity minimum at the critical iron content. Porosity was observed to be higher in the Al-9% Si castings than the Al-5% Si castings. Differences in the primary phase volume fraction and morphology may explain this observation. The results of this experimental work do not support the existing published theories that have been proposed to explain the effect the iron on porosity. An alternative theory is therefore developed. (c) 2006 Elsevier B.V. All rights reserved.

Eutectic solidification mode in sodium modified Al-7 mass %Si-3.5 mass %Cu-0.2 mass %Mg casting alloys

The influence of sodium (Na) on nucleation and growth of the Al-Si eutectic in a commercial hypoeutectic Al-Si-Cu-Mg foundry alloy has been investigated. The microstructural evolution during eutectic solidification was studied by a quenching technique. By comparing the orientation of the aluminium in the eutectic to that of the surrounding primary aluminium dendrites by EBSD, the eutectic solidification mode could be determined. The results show that the eutectic solidification starts near the mould wall and evolves with front growth opposite the thermal gradient on a macro-scale, and on a micro-scale with independent heterogeneous nucleation of eutectic grains in interdendritic spaces. Na-modified alloys therefore behave significantly differently from those modified by other elemental additions.

The effect of iron on liquid film migration and sintering of an Al-Cu-Mg alloy

Analytical transmission electron microscopy indicates that liquid film migration occurs during sintering of an Al-Cu-Mg alloy, that intragranular liquid pools develop from migrating films and that iron segregates to these pools. It is suggested that a high localised iron concentration retards the liquid film migration rate by reducing the coherency strain in the retreating grain, causing a region of the film to detach from the boundary, thus forming an intragranular pool in the advancing grain. Alloys with low iron levels develop few intragranular pools and have high sintered densities. (C) 2003 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Aluminium phosphide as a eutectic grain nucleus in hypoeutectic Al-Si alloys

Aluminium phosphide (AlP) particles arc often suggested to be the nucleation site for eutectic silicon in Al-Si alloys, since both the crystal structure and lattice parameter of AlP (crystal structure: cubic K(4) over bar m; lattice parameter: 5.421 Angstrom) are close to that of silicon (cubic Fd3m, 5.431 Angstrom), and the melting point is higher than the Al-Si eutectic temperature. However, the crystallographic relationships between AlP particles and the surrounding eutectic silicon are seldom reported due to the difficulty in analysing the AlP particles, which react with water during sample preparation for polishing. in this study, the orientation relationships between AlP and Si are analysed by transmission electron microscopy using focused ion-beam milling for sample preparation to investigate the nucleation mechanism of eutectic silicon on AlP. The results show a clear and direct lattice relationship between centrally located AlP particles and the surrounding silicon in the hypoeutectic Al-Si alloy.

Influence of calcium on the microstructure and properties of an Al-7Si-0.3Mg-xFe alloy

The effect of Ca addition on the microstructure, physical characteristics (density/porosity), and mechanical properties (tensile and impact strength) has been investigated in an Al-7Si-0.3Mg-xFe (x = 0.2, 0.4, and 0.7) alloy. The size of Al-Fe intermetallic platelets (beta-Al5FeSi) increased with increasing Fe content. The addition of Ca modified the eutectic microstructure and also reduced the size of intermetallic Fe-platelets, causing improved elongation and impact strengths. A low level of Ca addition (39 ppm) reduced the porosity of the alloys. The tensile strength was decreased marginally with Ca addition. However, Ca addition improved the ductility of the alloy by 18.3, 16.7, and 44 pet and the impact strength by 44, 48, and 15.8 pct for Fe contents of 0.2, 0.4, and 0.7 pct, respectively.

Determination of strontium segregation in modified hypoeutectic Al-Si alloy by micro X-ray fluorescence analysis

Analysis of intra- and inter-phase distribution of modifying elements in aluminium-silicon alloys is difficult due to the low concentrations used. This research utilises a mu-XRF (X-ray fluorescence) technique at the SPring-8 synchrotron radiation facility X-ray source and reveals that the modifying element strontium segregates exclusively to the eutectic silicon phase and the distribution of strontium within this phase is relatively homogeneous. This has important implications for the fundamental mechanisms of eutectic modification in hypoeutectic aluminium-silicon alloys. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

The effect of grain refinement and silicon content on grain formation in hypoeutectic Al-Si alloys

The effect of increasing the amount of added grain refiner on grain size and morphology has been investigated for a range of hypoeutectic Al-Si alloys. The results show a transition in grain size at a silicon concentration of about 3 wt% in unrefined alloys; the grain size decreasing with silicon content before the transition, and increasing beyond the transition point. A change in morphology also occurs with increased silicon content. The addition of grain refiner leads to greater refinement for silicon contents below the transition point than for those contents above the transition point, while the transition point seems to remain unchanged. The slope of the grain size versus silicon content curve after the transition seems to be unaffected by the degree of grain refinement. The results are related to the competitive processes of nucleation and constitutional effects during growth and their impact on nucleation kinetics. (C) 1999 Elsevier Science S.A. All rights reserved.

Eutectic nucleation and growth in hypoeutectic Al-SI alloys at different strontium levels

The effects of different levels of strontium on nucleation and growth of the eutectic in a commercial hypoeutectic Al-Si foundry alloy have been investigated by optical microscopy and electron backscattering diffraction (EBSD) mapping by scanning electron microscopy (SEM). The microstructural evolution of each specimen during solidification was studied by a quenching technique at different temperatures and Sr contents. By comparing the orientation of the aluminum in the eutectic to that of the surrounding primary aluminum dendrites by EBSD, the eutectic formation mechanism could be determined. The results of these studies show that the eutectic nucleation mode, and subsequent growth mode, is strongly dependent on Sr level. Three distinctly different eutectic growth modes were found, in isolation or sometimes together, but different for each Sr content. At very low Sr contents, the eutectic nucleated and grew from the primary phase. Increasing the Sr level to between 70 and 110 ppm resulted in nucleation of independent eutectic grains with no relation to the primary dendrites. At a Sr level of 500 ppm, the eutectic again nucleated on and grew from the primary phase while a well-modified eutectic structure was still present. A slight dependency of eutectic growth radially from the mold wall opposite the thermal gradient was observed in all specimens in the early stages of eutectic solidification.