Kinetic study of the thermal degradation of high density polyethylene

The thermal degradation of high density polyethylene has been modelled by the random breakage of polymer bonds, using a set of population balance equations. A model was proposed in which the population balances were lumped into representative sizes so that the experimentally determined molecular weight distribution of the original polymer could be used as the initial condition. This model was then compared to two different cases of the unlumped population balance which assumed unimolecular initial distributions of 100 and 500 monomer units, respectively. The model that utilised the experimentally determined molecular weight distribution was found to best describe the experimental data. The model fits suggested a second mechanism in addition to random breakage at slow reaction rates. (c) 2005 Elsevier Ltd. All rights reserved.

Overcoming the problem of loss-in-capacity of calcium oxide in CO2 capture

Calcium oxide has been identified to be one of the best candidates for CO2 capture in zero-emission power-generation systems. However, it suffers a well-known problem of loss-in-capacity (i.e., its capacity of CO2 capture decreases after it undergoes cycles of carbonation/decarbonation). This problem is a potential obstacle to the adoption of the new technologies. This paper proposes a method of fabricating a CaO-based adsorbent without the problem of loss-in-capacity. An adsorbent was fabricated using the method and tested on a thermogravimetric analyzer. It was shown that the sorbent attained a utilization efficiency of more than 90% after 9 cycles of carbonation/decarbonation.