Stress corrosion crack propagation in AerMet 100

Fracture mechanics tests were carried out for AerMet 100 in distilled water and NaCl (3.5 and 35 gl(-1)). The initiation period at higher values of the stress intensity factor indicated that load application in the stress corrosion cracking (SCC) environment is a necessary but not sufficient factor for SCC and that time is needed for some other factor (e.g., the local hydrogen concentration) to reach an appropriate value. The threshold stress intensity factor, K-ISSC, was found to increase with decreasing NaCl concentration. The plateau stress corrosion crack velocity was 2 x 10(-8) ms(-1) for NaCl (3.5 and 35 gl(-1)). The fracture mode was transgranular with small areas of an intergranular nature. (C) 1998 Chapman & Hall.

Race modeling: An effective cognitive strategy for the 100 m sprinter?

The purpose of this study was to investigate the effects of a specific cognitive race plan on 100 m sprint performance, Twelve elite sprinters (11 male and 1 female) performed 100 m time trials under normal (control) conditions and then under experimental conditions (use of race cues). In the experimental condition, participants were asked to think about specific thought content in each of three segments of the 100 m. A multiple baseline design was employed. A mean improvement of 0.26 s was found. Eleven of the 12 participants showed improvement using the specific cognitive race plan (p < .005). Participants also produced more consistent sprint performances when using the cues (p < .01). Subjective evaluations made by the participants unanimously supported the use of the race plan for optimizing sprint performance. Environmental conditions, effort, and practice effects were considered as possible influences on the results.