Hydroxide carbonates and oxide carbonate hydrate of rare earths grown on glass via a hydrothermal route

Carbonates of rare-earths, specifically hydroxide carbonate or oxide carbonate hydrate, could be prepared on common glass by a hydrothermal process involving thiourea. Examples presented in this paper include LaOHCO3, CeOHCO3 and EU2O(CO3)(2) . H2O structures formed on glass from solutions of thiourea and the relevant rare-earth reactants. The crystal structure and habit on the substrates were dependent on the preparative conditions; the influence of the concentrations of reactants and temperature on the crystal morphologies is illustrated. Second harmonic generation was found to occur in the crystals. (C) 2004 Elsevier B.V. All rights reserved.

Iron-rich intermetallic phases and their role in casting defect formation in hypoeutectic Al-Si alloys

Iron is the most common and detrimental impurity in aluminum casting alloys and has long been associated with an increase in casting defects. While the negative effects of iron are clear, the mechanism involved is not fully understood. It is generally believed to be associated with the formation of Fe-rich intermetallic phases. Many factors, including alloy composition, melt superheating, Sr modification, cooling, rate, and oxide bifilms, could play a role. In the present investigation, the interactions between iron and each individual element commonly present in aluminum casting alloys, were investigated using a combination of thermal analysis and interrupted quenching tests. The Fe-rich intermetallic phases were characterized using optical microscope, scanning electron microscope, and electron probe microanalysis (EPMA), and the results were compared with the predictions by Thermocalc. It was found that increasing the iron content changes the precipitation sequence of the beta phase, leading to the precipitation of coarse binary beta platelets at a higher temperature. In contrast, manganese, silicon, and strontium appear to suppress the coarse binary beta platelets, and Mn further promotes the formation of a more compact and less harmful a phase. They are therefore expected to reduce the negative effects of the phase. While reported in the literature, no effect of P on the amount of beta platelets was observed. Finally, attempts are made to correlate the Fe-rich intermetallic phases to the formation of casting defects. The role of the beta phase as a nucleation site for eutectic Si and the role of the oxide bifilms and AIP as a heterogeneous substrate of Fe intermetallics are also discussed.