Synthesis, characterization, and electrical conduction of 10 mol% Dy2O3 doped CeO2 ceramics

Well-densified 10 mol% Dy2O3-doped CeO2 (20DDC) ceramics with average grain sizes of similar to 0.12-1.5 mu m were fabricated by pressureless sintering at 950-1550 degrees C using a reactive powder thermally decomposed from a carbonate precursor, which was synthesized via a carbonate coprecipitation method employing nitrates as the starting salts and ammonium carbonate as the precipitant. Electrical conductivity of the ceramics, measured by the dc three-point impedance method, shows a V-shape curve against the average grain size. The sample with the smallest grain size of 0.12 mu m exhibits a high conductivity of similar to 10(-1.74) S/cm at the measurement temperature of 700 degrees C, which is about the same conduction level of the micro-grained 10 mol% Sm2O3- or Gd2O3-doped CeO2, two leading electrolyte materials. (c) 2004 Elsevier Ltd. All rights reserved.

Local structures around Y and Ce cations in 10 mol% Y2O3 doped ceria ceramics by EXAFS spectroscopy

Local structures around host Ce and dopant Y cations in 10 mol% Y2O3 doped ceria solid solutions have been investigated by room and high temperature EXAFS spectroscopy. The results show that the local structures around the Cc cation in doped ceria samples are similar to that in the fluorite CeO2 structure though the coordination numbers of Ce-O tend to be smaller than 8. The local structures around Y cation, however, are significantly different from those around Ce cation, and show more resemblance to that around Y cation in the C-type Y2O3 Structure. A more accurate description of the local structures around Y cation in doped ceria was given by analyzing Y-K edge EXAFS spectra based on the C-type Y2O3 structure. (c) 2006 Elsevier B.V. All rights reserved.