Environmental influence on the stress corrosion cracking of rock bolts

In order to understand rock bolt Stress Corrosion Cracking (SCC), a series of experiments have been performed in Linearly Increasing Stress Test (LIST) apparatus. One series of experiments determined the threshold stress of various bolt metallurgies (900 MPa for Steel A, and 800 MPa for Steel B and C). The high values of threshold stress suggest that SCC begins in rock bolts when they are sheared by moving rock strata. Typical crack velocity values have been measured to be 2.5 x 10(-8) m s(-1), indicating that there is not much benefit for rock bolt steel of higher fracture toughness. Another series of experiments were performed to understand the environmental conditions causing SCC of steel A and galvanised Steel A rock bolt steel. SCC only occurred for environmental conditions for which produce hydrogen on the sample surface, leading to hydrogen embrittlement and SCC. Fracture surfaces of LIST samples failed by SCC were found to display the same fracture regions as fracture surfaces of rock bolts failed in service by SCC: Tearing Topography Surface (TTS), Corrugated Irregular Surface (CIS), quasi Micro Void Coalescence (qMVC) and Fast Fracture Surface (FFS). Water chemistry analysis were carried out on samples collected from various Australian mines in order to compare laboratory electrolyte conditions to those found in underground mines.

Electron beam current loss at the high-vacuum-high-pressure boundary in the environmental scanning electron microscope

A significant loss in electron probe current can occur before the electron beam enters the specimen chamber of an environmental scanning electron microscope (ESEM). This loss results from electron scattering in a gaseous jet formed inside and downstream (above) the pressure-limiting aperture (PLA), which separates the high-pressure and high-vacuum regions of the microscope. The electron beam loss above the PLA has been calculated for three different ESEMs, each with a different PLA geometry: an ElectroScan E3, a Philips XL30 ESEM, and a prototype instrument. The mass thickness of gas above the PLA in each case has been determined by Monte Carlo simulation of the gas density variation in the gas jet. It has been found that the PLA configurations used in the commercial instruments produce considerable loss in the electron probe current that dramatically degrades their performance at high chamber pressure and low accelerating voltage. These detrimental effects are minimized in the prototype instrument, which has an optimized thin-foil PLA design.

Dimensional change behavior of caribbean pine using an environmental scanning electron microscope

Moisture transport and dimensional change during wood drying or wetting processes were analyzed based on pictures from an environmental scanning electron microscope (ESEM). This provides quantitative relationships between dimensional changes of total area, cell wall, and lumen, and moisture content for earlywood and latewood. Earlywood and latewood behave similarly but show some quantitative differences. The overall outcome for sections containing both kinds of wood seems to be dominated by the latewood behavior. The observed strain behavior of wood during drying is anisotropic in ways that are inconsistent with explanations solely related to microfibril orientation or earlywood/latewood interactions and more likely may be influenced by ray tracheids.