Modification-related porosity formation in hypoeutectic aluminum-silicon alloys

A series of aluminum-10 wt pet silicon castings were produced in sand molds to investigate the effect of modification on porosity formation. Modification with individual additions of either strontium or sodium resulted in a statistically significant increase in the level of porosity compared to unmodified castings. The increase in porosity with modification is due to the presence of numerous dispersed pores, which were absent in the unmodified casting. It is proposed that these pores form as a result of differences in size of the aluminum-silicon eutectic grains between unmodified and modified alloys. A geometric model is developed to show how the size of eutectic grains can influence the amount and distribution of porosity. Unlike traditional feeding-based models, which incorporate the effect: of microstructure on permeability, this model considers what happens when liquid is isolated from the riser and can no longer flow. This simple isolation model complements rather than contradicts existing theories on modification-related porosity formation and should be considered in the development of future comprehensive models.

Loose abrasive truing and dressing of resin bond diamond cup wheels for grinding fibre optic connectors

A loose abrasive lapping technology was developed for truing and dressing ultrafine diamond cup wheels for grinding spherical end faces of fibre optic connectors. The relative densities of exposed grits and grit pull-outs measured from wheel surfaces prepared using the loose abrasive lapping and the bonded abrasive dressing were compared. It was found that the lapping method with loose abrasives produced wheel surfaces with more exposed grits and less grit pull-outs, especially for finer grit size wheels. For dressing ultrafine grit size wheels, the particle size of the lapping paste should be smaller than the wheel grit size to achieve a better result. It is also found that the wheels dressed using the lapping method demonstrate an excellent grinding performance. (C) 2004 Elsevier B.V.. All rights reserved.

Modeling of columnar-to-equiaxed transition in solidified Al-Si alloys

A Cellular-Automaton Finite-Volume-Method (CAFVM) algorithm has been developed, coupling with macroscopic model for heat transfer calculation and microscopic models for nucleation and growth. The solution equations have been solved to determine the time-dependent constitutional undercooling and interface retardation during solidification. The constitutional undercooling is then coupled into the CAFVM algorithm to investigate both the effects of thermal and constitutional undercooling on columnar growth and crystal selection in the columnar zone, and formation of equiaxed crystals in the bulk liquid. The model cannot only simulate microstructures of alloys but also investigates nucleation mechanisms and growth kinetics of alloys solidified with various solute concentrations and solidification morphologies.

Determination of mechanical properties of PECVD silicon nitride thin films for tunable MEMS Fabry-Pérot optical filters

This paper reports an investigation on techniques for determining elastic modulus and intrinsic stress gradient in plasma-enhanced chemical vapor deposition (PECVD) silicon nitride thin films. The elastic property of the silicon nitride thin films was determined using the nanoindentation method on silicon nitride/silicon bilayer systems. A simple empirical formula was developed to deconvolute the film elastic modulus. The intrinsic stress gradient in the films was determined by using micrometric cantilever beams, cross-membrane structures and mechanical simulation. The deflections of the silicon nitride thin film cantilever beams and cross-membranes caused by in-thickness stress gradients were measured using optical interference microscopy. Finite-element beam models were built to compute the deflection induced by the stress gradient. Matching the deflection computed under a given gradient with that measured experimentally on fabricated samples allows the stress gradient of the PECVD silicon nitride thin films introduced from the fabrication process to be evaluated.

Characterization of mechanical properties of silicon nitride thin films for MEMS devices by nanoindentation

An experimental investigation of mechanical properties of thin films using nanoindentation was reported. Silicon nitride thin films with different thicknesses were deposited using plasma enhanced chemical vapor deposition (PECVD) on Si substrate. Nanoindentation was used to measure their elastic modulus and hardness. The results indicated that for a film/substrate bilayer system, the measured mechanical properties are significantly affected by the substrate properties. Empirical formulas were proposed for deconvoluting the film properties from the measured bilayer properties.

A study on stress corrosion cracking and hydrogen embrittlement of AZ31 magnesium alloy

The stress corrosion cracking (SCC) behavior and pre-exposure embrittlement of AZ31 magnesium alloy have been studied by slow strain rate tensile (SSRT) tests in this paper. It is showed that AZ31 sheet material is susceptible to SCC in distilled water, ASTM D1.387 solution, 0.01 M NaCl and 0.1 M NaCl solution. The AZ31 magnesium alloy also becomes embrittled if pre-exposed to 0.01 M NaCl solution prior to tensile testing. The degree of embrittlement increased with increasing the pre-exposure time, It is proposed that both the pre-exposure embrittlement and SCC were due to hydrogen which reduces the cohesive strength. i,e,. hydrogen embrittlement, (c) 2005 Elsevier B.V. All rights reserved.

The states, diffusion, and concentration distribution of water in radiation-formed PVA/PVP hydrogels

Hydrogels with various compositions of polyvinyl alcohol (PVA) and poly(1-vinyl-2-pyrrolidinone) (PVP) were prepared by irradiating mixtures of PVA and PVP in aqueous solutions with gamma-rays from Co-60 sources at room temperature. The states of water in the hydrogels were characterized using DSC and NMR T-2 relaxation measurements and the kinetics of water diffusion in the hydrogels were studied by sorption experiments and NMR imaging. The DSC endothermic peaks in the temperature range -10 to +10 degrees C implied that there are at least two kinds of freezable water present in the matrix. The difference between the total water content and the freezable water content was refer-red to as bound water, which is not freezable. The weight fraction of water at which only nonfreezable water is present in a hydrogel with F-VP = 0.19 has been estimated to be g(H2O)/g(Polymer) = 0.375. From water sorption experiments, it was demonstrated that the early stage of the diffusion of water into the hydrogels was Fickian. A curve-fit of the early-stage experimental data to the Fickian model allowed determination of the water diffusion coefficient, which was found to lie between 1.5 x 10(-11) m(2) s(-1) and 4.5 x 10(-11) m(2) s(-1), depending on the polymer composition, the cross-link density, and the temperature. It was also found that the energy barrier for diffusion of water molecules into PVA/PVP hydrogels was approximate to 24 kJ mol(-1). Additionally, the diffusion coefficients determined from NMR imaging of the volumetric swelling of the gels agreed well with the results obtained by the mass sorption method.

Superior electric double layer capacitors using ordered mesoporous carbons

This paper reports for the first time superior electric double layer capacitive properties of ordered mesoporous carbon (OMCs) with varying ordered pore symmetries and mesopore structure. Compared to commercially used activated carbon electrode, Maxsorb, these OMC carbons have superior capacitive behavior, power output and high-frequency performance in EDLCs due to the unique structure of their mesopore network, which is more favorable for fast ionic transport than the pore networks in disordered microporous carbons. As evidenced by N-2 sorption, cyclic voltammetry and frequency response measurements, OMC carbons with large mesopores, and especially with 2-D pore symmetry, show superior capacitive behaviors (exhibiting a high capacitance of over 180 F/g even at very high sweep rate of 50 mV/s, as compared to much reduced capacitance of 73 F/g for Maxsorb at the same sweep rate). OMC carbons can provide much higher power density while still maintaining good energy density. OMC carbons demonstrate excellent high-frequency performances due to its higher surface area in pores larger than 3 nm. Such ordered mesoporous carbons (OMCs) offer a great potential in EDLC capacitors, particularly for applications where high power output and good high-frequency capacitive performances are required. (C) 2005 Elsevier Ltd. All rights reserved.

Effects of Si content on defect band formation in hypoeutectic Al-Si die castings

Al-3-11% Si alloys have been high-pressure die-cast and characterized microstructurally. Alstruc was used to calculate the solidification characteristics and fraction of eutectic. Defect bands were observed at all Si contents, although their constitution, position and distinctiveness were a function of Si content. The defect bands contain a higher fraction Al-Si eutectic than the surroundings in all alloys, and porosity was additionally found in the band in AlSi3. With decreasing Si content, the defect bands formed closer to the casting surface, became more prevalent and also the width of the bands decreased. These differences are discussed by considering the effect of Si content on the distribution of solid in the mushy wall layers and on the feeding potentials of the alloys. The observations are consistent with the mechanism proposed by Gourlay et al. in which bands form due to deformation within the solidifying mushy wall layers. (c) 2005 Elsevier B.V. All rights reserved.

Shear deformation at 29% solid during solidification of magnesium alloy AZ91 and aluminium alloy A356

Partially solid commercial Al-Si and Mg-Al alloys have been deformed in shear during solidification using vane rheometry. The dendritic mush was deformed for a short period at 29% solid and allowed to cool naturally after deformation. Both alloys exhibited yield point behaviour and deformation was highly localised at the surface of maximum shear stress. The short period of deformation was found to have a distinct impact on the as-cast microstructure leading to fragmented dendrites in the deformation region of both alloys. In the case of the Mg-Al alloy, a concentrated region of interdendritic porosity was also observed in the deformation region. Concentrated porosity was not observed in the Al-Si alloy. (c) 2005 Elsevier B.V. All rights reserved.

Eutectic modification and microstructure development in Al-Si alloys

Recent increasing applications for cast Al-Si alloys are particularly driven by the need for lightweighting components in the automotive sector. To improve mechanical properties, elements such as strontium, sodium and antimony can be added to modify the eutectic silicon from coarse and plate-like to fine and fibrous morphology. It is only recently being noticed that the morphological transformation resulting from eutectic modification is also accompanied by other, equally significant, but often unexpected changes. These changes can include a 10-fold increase in the eutectic grain size, redistribution of low-melting point phases and porosity as well as surface finish, consequently leading to variations in casting quality. This paper shows the state-of-the-art in understanding the mechanism of eutectic nucleation and growth in Al-Si alloys, inspecting samples, both quenched and uninterrupted, on the macro, micro and nano-scale. It shows that significant variations in eutectic nucleation and growth dynamics occur in AI-Si alloys as a function of the type and amount of modifier elements added. The key role of AIP particles in nucleating silicon is demonstrated. (c) 2005 Elsevier B.V. All rights reserved.

Improved VDC casting of aluminium alloys through an understanding of the surface properties of the molten metal

Vertical direct chill (VDC) casting of aluminium alloys is a mature process that has evolved over many decades through gradual change to both equipment design and casting practice. Today, air-pressurised, continuous lubrication, hot top mould systems with advanced station automation are selected as the process of choice for producing extrusion billet. Specific sets of operating parameters are employed on these stations for each alloy and size combination to produce optimal billet quality. The designs and parameters are largely derived from past experience and accumulated know-how. Recent experimental work at the University of Queensland has concentrated on understanding the way in which the surface properties of liquid aluminium alloys, e.g., surface tension, wetting angle and oxide skin strength, influence the size and shape of the naturally-stab le meniscus for a given alloy, temperature and atmosphere. The wide range of alloy-and condition-dependent values measured has led to the consideration of how these properties impact the stability of the enforced molten metal meniscus within the hot top mould cavity. The actual shape and position of the enforced meniscus is controlled by parameters such as the upstream conduction distance (UCD) from sub-mould cooling and the molten metal head. The degree of deviation of this actual meniscus from the predicted stable meniscus is considered to be a key driver in surface defect formation. This paper reports on liquid alloy property results and proposes how this knowledge might be used to better design VDC mould systems and casting practices.

The microstructure of mechanically alloyed MoSi2 with Ni and Al additions

The effect of Ni and Al additions on grain boundary silica in mechanically alloyed and hot isostatically pressed (HTPed) MoSi2 was investigated. Mechanical alloying Mo and Si in the absence of Al produced finely dispersed silica within a fine grained structure. Mechanically alloyed and HIPed Mo and Si with Ni and Al partially transformed the silica to crystalline oxide phases, including Al2O3. An improvement in high temperature properties is not expected due to the retention of a grain boundary silica film. Rapid grain growth resulted during HIPing, possibly due to the formation of a Ni/Fe/Al liquid phase.

Atmospheric corrosion of copper at Heron Island

Atmospheric corrosion tests have been conducted at Heron Island, Queensland, a low SO2 marine environment. The corrosion rates for copper followed the linear bi-logarithmic law. X-ray diffraction identified atacamite (basic copper chloride) and cuprite (cuprous oxide) as the predominant corrosion products. Biogenic and anthropogenic sources of pollution did not have a measurable influence.

A transformation toughening white cast iron

An experimental white cast iron with the unprecedented fracture tough ness of 40 MPa m(1/2) is currently being studied to determine the mechanisms of toughening. This paper reports the investigation of the role of strain-induced martensitic (SIM) transformation. The dendritic microconstituent in the toughened alloy consists primarily of retained austenite, with precipitated M(7)C(3) carbides and some martensite. Refrigeration experiments and differential scanning calorimetry (DSC) were used to demonstrate, firstly, that this retained austenite has an ''effective'' sub-ambient M(S) temperature and, secondly, that SIM transformation can occur at ambient temperatures. Comparison between room temperature and elevated temperature K-Ic tests showed that the observed SIM produces a transformation toughening response in the alloy, contributing to, but not fully accounting for, its high tough ness. SIM as a mechanism for transformation toughening has not previously been reported for white cast irons. Microhardness traverses on crack paths and X-ray diffraction (XRD) on fracture surfaces confirmed the interpretation of the K-Ic experiments. Further DSC and quantitative XRD showed that, as heat-treatment temperature is varied, there is a correlation between fracture toughness and the volume fraction of unstable retained austenite.