Modification of MCM-41 by surface silylation with trimethylchlorosilane and adsorption study

Siliceous MCM-41 samples were modified by silylation using trimethylchlorosilane (TMCS). The surface coverage of functional groups was studied systematically in this work. The role of surface silanol groups during modification was evaluated using techniques of FTIR and Si-29 CP/MAS NMR. Adsorption of water and benzene on samples of various hydrophobicities was measured and compared. It was found that the maximum degree of surface attachments of trimethylsilyl (TMS) groups was about 85%, corresponding to the density of TMS groups of 1.9 per nm(2). The degree of silylation is found to linearly increase with increasing pre-outgassing temperature prior to silylation. A few types of silanol groups exist on MCM-41 surfaces, among which both free and geminal ones are responsible for active silylation. Results of water adsorption show that aluminosilicate MCM-41 materials are more or less hydrophilic, giving a type IV isotherm, similar to that of nitrogen adsorption, whereas siliceous MCM-41 are hydrophobic, exhibiting a type V adsorption isotherm. The fully silylated Si-MCM-41 samples are more hydrophobic giving a type III adsorption isotherm. Benzene adsorption on all MCM-41 samples shows type IV isotherms regardless of the surface chemistry. Capillary condensation occurs at a higher relative pressure for the silylated MCM-41 than that for the unsilylated sample, though the pore diameter was found reduced markedly by silylation. This is thought attributed to the diffusion constriction posed by the attached TMS groups. The results show that the surface chemistry plays an important role in water adsorption, whereas benzene adsorption is predominantly determined by the pore geometry of MCM-41.

Experimental and theoretical investigations of adsorption hysteresis and criticality in MCM-41: Studies with O-2, Ar, and CO2

MCM-41 materials of six different pore diameters were prepared and characterized using X-ray diffraction, transmission electron microscopy, helium pycnometry, small-angle neutron scattering, and gas adsorption (argon at 77.4 and 87.4 K, nitrogen and oxygen at 77.4 K, and carbon dioxide at 194.6 K). A recent molecular continuum model of the authors, previously used for adsorption of nitrogen at 77.4 K, was applied here for adsorption of argon, oxygen, and carbon dioxide. While model predictions of single-pore adsorption isotherms for argon and oxygen are in satisfactory agreement with experimental data, significant deviation was found for carbon dioxide, most likely due to its high quadrupole moment. Predictions of critical pore diameter, below which reversible condensation occurs: were possible by the model and found to be consistent with experimental estimates, for the adsorption of the various gases. On the other hand, existing models such as the Barrett-Joyner-Halenda (BJH), Saito-Foley, and Dubinin-Astakhov models were found to be inadequate, either predicting an incorrect pore diameter or not correlating the isotherms adequately. The wall structure of MCM-41 appears to be close to that of amorphous silica, as inferred from our skeletal density measurements.

Preparation, characterization, and catalytic properties of clay-based nickel catalysts for methane reforming

Naturally occurring clays and pillared clays are used as supports of nickel catalysts for the methane reforming reaction with carbon dioxide to synthesis gas. The structural and textural characteristics of the supports and catalysts are systematically examined by N-2 adsorption/desorption and X-ray diffraction (XRD) techniques. It is found that the pore structures and surface properties of supports greatly affect the catalytic activities of the catalysts prepared. The catalysts supported on the mesoporous clays or pillared clays are obviously superior to those on microporous supports because the mesoporous supports are highly thermal stable compared to the microporous ones. It is found that introducing lanthanum to the supports can improve the catalyst basicity and thus enhance the catalytic activities of these catalysts. Deactivation of catalysts prepared and factors influencing their stability are also discussed. (C) 1998 Academic Press.

Thickness and stability of adsorbed film in cylindrical mesopores

The adsorbed film in small cylindrical mesopores is studied by using MCM-41 samples of uniform cylindrical channels as model systems. It is found that at a given relative pressure, the smaller the pore radius, the thicker the adsorbed film is, as postulated by Broekhoff and De Beer. Thermodynamics analysis established that the stability of the adsorbed film is determined by interface curvature and the potential of interaction between adsorbate and adsorbent. A semiempirical equation is proposed to describe the state of stable adsorbed films in cylindrical mesopores. It is also shown to be useful in calculations of pore size distributions of mesoporous solids.

Development of composite adsorbents of carbon and intercalated clay for N2 and O2 adsorption: A preliminary study

Composite adsorbents of carbon and alumina intercalated montmorillonite were prepared and characterized by adsorption of N-2 and O-2 at various temperatures. The effects of pyrolysis, temperature, heating rate, subsequent degassing, and doping of cations and anions were investigated. The adsorption capacities of the composite adsorbents developed at higher temperatures (0 and -79 degrees C) are found to be larger than those of normal alumina pillared clays. The experimental results showed that the framework of these adsorbents is made of alumina particles and clay sheets while the pyrolyzed carbon distributes in the space of interlayers and interpillars. The pores between the carbon particles, clay sheets, and alumina pillars are very narrow with very strong adsorption forces, leading to enhanced adsorption capacities at 0 and -79 degrees C. The composite adsorbents exhibit features similar to those of carbonaceous adsorbents. Their pore structures, adsorption capacities, and selectivities to oxygen can be tailored by a controlled degassing procedure. Meanwhile, ions can be doped into the adsorbents to modify their adsorption properties, as usually observed for oxide adsorbents like zeolite and pillared clays. Such flexibility in pore structure tailoring is a potential advantage of the composite adsorbents developed for their adsorption and separation applications. (C) 1999 Academic Press.

A novel method for tailoring the pore-opening size of MCM-41 materials

A novel pore tailoring method is proposed by which the pore-opening sizes of MCM-41 materials can be finely tuned without significant loss in pore volume and surface area.

Characterization of the structural and surface properties of chemically modified MCM-41 material

Mesoporous Mobil catalytic materials of number 41 (MCM-41) silica was chemically modified using both inorganic and organic precursors and characterized using the techniques, XRD, XPS, MAS NMR, FTIR, W-Vis, and physical adsorption of nitrogen, hydrocarbons (hexane, benzene, acetone, and methanol) and water vapor. Modification using organic reagents was found to result in a significant loss in porosity and a shape change of surface properties (increased hydrophobicity and decreased acidity). With inorganic modifying reagents, the decrease in porosity was also observed while the surface properties were not significantly altered as reflected by the adsorption isotherms of organics and water vapors. Chemical modifications can greatly improve the hydrothermal stability of MCM-41 material because of the enhanced surface hydrophobicity (with organic modifiers) or increased pore wall thickness (with inorganic modifiers). (C) 2000 Elsevier Science B.V. All rights reserved.

Comprehensive structural characterization of MCM-41: From mesopores to particles

In the present work the meso- and macro-structural characteristics of the mesoporous adsorbent MCM-41 have been estimated with the help of various techniques. The structure is found to comprise four different length scales: that of the mesopores, the crystallites, the grains and of the particles. It was found that the surface area estimated by the use of small angle scattering techniques is higher, while that estimated by mercury porosimetry is much lower, than that obtained from gas adsorption methods. Based on the macropore characterization by mercury porosimetry, and the considerable macropore area determined, it is seen that the actual mesopore area of MCM-41 may be significantly lower than the BET area. TEM studies indicated that MCM-41 does not have an ideal mesopore structure; however, it may still be treated as a model mesoporous material for gas adsorption studies because of the large radius of curvature of the channels.

Copper/MCM-41 as catalyst for the wet oxidation of phenol

A heterogeneous copper catalyst supported on mesoporous MCM-41 was developed. The parent MCM-41 has a large pore area of over 1400 m(2)/g. Copper was chosen as the active element of catalyst and loaded into MCM-41 by adsorption at ambient temperature. The prepared catalysts were evaluated in the catalytic wet oxidation of phenol solution with an initial concentration of 1,300 ppm at 150 and 200 degreesC. The catalyst was found to be of high catalytic activity. It is also shown that the catalyst with a higher copper loading exhibits higher ability of accelerating the catalytic reaction to certain extent but reaches its constant level afterwards. (C) 2001 Elsevier Science B.V. All rights reserved.

Copper/MCM-41 as catalyst for photochemically enhanced oxidation of phenol by hydrogen peroxide

Heterogeneous copper catalyst was developed using the mesoporous molecular sieve MCM-41 as the catalyst support. Copper was impregnated onto the support. Catalysts with different copper loadings were obtained. The performance of the developed catalysts was evaluated in photochemically enhanced oxidation of phenol using hydrogen peroxide as the oxidant. The catalyst was found to significantly increase the oxidation rate and enhance the removal level of phenol with UV light present. The effects of copper loading on the catalyst, photo (UV), H2O2 concentration, and catalyst dosage on the photo-oxidation of phenol were studied. (C) 2001 Elsevier Science B.V. All rights reserved.

Structural development of silicated films self-assembled at the air-water interface

The development of structure perpendicular to and in the plane of the interface has been studied for mesoporous silicate films self-assembled at the air/water interface. The use of constrained X-ray and neutron specular reflectometry has enabled a detailed study of the structural development perpendicular to the interface during the pre-growth phase. Off-specular neutron reflectometry and grazing incidence X-ray diffraction has enabled the in-plane structure to be probed with excellent time resolution. The growth mechanism under the surfactant to silicate source ratios used in this work is clearly due to the self-assembly of micellar and molecular species at the air/liquid interface, resulting in the formation of a planar mesoporous film that is tens of microns thick. (C) 2003 Elsevier Science B.V. All rights reserved.

Comprehensive study of surface chemistry of MCM-41 using Si-29 CP/MAS NMR, FTIR, pyridine-TPD, and TGA

A comprehensive study was conducted on mesoporous MCM-41. Spectroscopic examinations demonstrated that three types of silanol groups, i.e., single, (SiO)(3)Si-OH, hydrogen-bonded, (SiO)(3)Si-OH-OH-Si(SiO)(3), and geminal, (SiO)(2)Si(OH)(2), can be observed. The number of silanol groups/nm(2), alpha(OH), as determined by NMR, varies between 2.5 and 3.0 depending on the template-removal methods. All these silanol groups were found to be the active sites for adsorption of pyridine with desorption energies of 91.4 and 52.2 kJ mol(-1), respectively. However, only free silanol groups (involving single and geminal silanols) are highly accessible to the silylating agent, chlorotrimethylsilane. Silylation can modify both the physical and chemical properties of MCM-41.