Biodegradation and ecotoxicity evaluation of a bionolle and starch blend and its degradation products in compost

A polymer based on a blend of starch and Bionolle(TM) has been prepared and tested for biodegradation in compost. The polymer was completely mineralised to carbon dioxide in 45 days. The potential toxicity of the polymer was tested against the earthworm Eisenia fetida using a modification of the American Standard for Testing Materials E1976-97. The earthworms were exposed to 30 g of the polymer for 28 days and changes in weight recorded. In addition, the polymer was firstly degraded by the compost and the worms exposed to the breakdown products for 28 days. Differences in weight were also recorded. In each case the production of juveniles was noted and all earthworms were examined for pathology. The results obtained were processed statistically using a t-test. The number of juveniles, produced from the breakdown products, was highly significant (P < 0.001) when compared to the earthworms added to the intact polymer. There was a definitely significant difference (P < 0.01, t = 3.25) in change in weight between the earthworms that were exposed to the polymer directly and those that were exposed to the breakdown products. There was no indication of any pathology of any earthworms. The polymer is considered safe for this species. (C) 2002 Elsevier Science Ltd. All rights reserved.

A study of the radiation degradation of styrene/alkane and α-methylstyrene/alkane copolymers

The effects of copolymer composition and microstructure on the radiation chemistry of styrene/alkane and alpha-methylstyrene/alkane copolymers have been studied. The primary radical species formed on radiolysis of the copolymers at 77 K, and identified by ESR spectroscopy, are the same as those formed during radiolysis of the homopolymers. The yields of radicals for the copolymer are as predicted assuming that the cross-section is proportional to the electron density of each component; however, there is some evidence of radical migration to aromatic groups at 77 K. Changes in molecular structure on irradiation were detected by using C-13 NMR spectroscopy. Evidence of the consumption of terminal double bonds, and chain scission in alpha-methylstyrene/alkane copolymers was found. Measurements of viscosity supported the mechanism of cross-linking predominating in styrene/alkane copolymers, while in alpha-methylstyrene/alkane copolymers chain scission was the major result of irradiation. (C) 2003 Society of Chemical Industry.