Growth and compaction behaviour of copper concentrate granules in a rotating drum

In order to understand the growth and compaction behaviour of chalcopyrite (copper concentrate), batch granulation tests were carried out using a rotating drum. The granule growth exhibited induction-type behaviour, as defined by Iveson and Litster [AIChE J. 44 (1998) 15 10]. There were two consecutive stages during granulation: the induction stage, during which the granules are gradually being compacted and little or no growth occurs, and the rapid growth stage, which starts when the granules have become surface wet and are rapidly growing. In agreement with earlier findings. an increased amount of binder liquid shortened the induction time. The compaction behaviour was also investigated. A displaced volume method was adopted to determine the porosity of the granules. It was shown that this technique had a limitation as it was unable to detect the reduction of the volumes of the granule pores after the granules had become surface wet. Due to this, some of the measurements were not suited for fitting a three-parameter empirical model. Attempts were made to determine whether the rapid growth stage started with the pore saturation exceeding a certain critical value, but due to the scatter in the porosity measurements and the fact that some of the measurements could not be used, it was not possible to determine a critical pore saturation, However, the porosity measurements clearly demonstrated that the porosity of the granules decreased during the induction stage of an experiment and that when rapid growth occurred, the granules had a pore saturation was around 0.85. This value was slightly lower than unity, which is most likely due to trapped air bubbles. (C) 2002 Published by Elsevier Science B.V.

Horizontal rotating cylinder - A compact apparatus for studying the effect of water wetting on carbon dioxide corrosion of mild steel

Water wetting is a crucial issue in carbon dioxide (CO.) corrosion of multiphase flow pipelines made from mild steel. This study demonstrates the use of a novel benchtop apparatus, a horizontal rotating cylinder, to study the effect of water wetting on CO2 corrosion of mild steel in two-phase flow. The setup is similar to a standard rotating cylinder except for its horizontal orientation and the presence of two phases-typically water and oil. The apparatus has been tested by using mass-transfer measurements and CO2 corrosion measurements in single-phase water flow. CO2 corrosion measurements were subsequently performed using a water/hexane mixture with water cuts varying between 5% and 50%. While the metal surface was primarily hydrophilic under stagnant. conditions, a variety of dynamic water wetting situations was encountered as the water cut and fluid velocity were altered. Threshold velocities were identified at various water cuts when the surface became oil-wet and corrosion stopped.

A mechanistic model for carbon dioxide corrosion of mild steel in the presence of protective iron carbonate films - Part 3: Film growth model

A model of iron carbonate (FeCO3) film growth is proposed, which is an extension of the recent mechanistic model of carbon dioxide (CO2) corrosion by Nesic, et al. In the present model, the film growth occurs by precipitation of iron carbonate once saturation is exceeded. The kinetics of precipitation is dependent on temperature and local species concentrations that are calculated by solving the coupled species transport equations. Precipitation tends to build up a layer of FeCO3 on the surface of the steel and reduce the corrosion rate. On the other hand, the corrosion process induces voids under the precipitated film, thus increasing the porosity and leading to a higher corrosion rate. Depending on the environmental parameters such as temperature, pH, CO2 partial pressure, velocity, etc., the balance of the two processes can lead to a variety of outcomes. Very protective films and low corrosion rates are predicted at high pH, temperature, CO2 partial pressure, and Fe2+ ion concentration due to formation of dense protective films as expected. The model has been successfully calibrated against limited experimental data. Parametric testing of the model has been done to gain insight into the effect of various environmental parameters on iron carbonate film formation. The trends shown in the predictions agreed well with the general understanding of the CO2 corrosion process in the presence of iron carbonate films. The present model confirms that the concept of scaling tendency is a good tool for predicting the likelihood of protective iron carbonate film formation.

Numerical investigation of turbulent flow around a rotating stepped cylinder for corrosion study

Direct numerical simulation has been carried out for turbulent flow set up by a rotating cylinder with two backward-facing steps axisymmetrically mounted in the circumferential direction. This flow geometry creates a qualitatively similar flow pattern as observed near, a sudden, pipe expansion or a plane backward-facing step, characterized by flow separation and reattachment. A region of intense turbulence intensity and high wall-shear-stress fluctuations is formed in,the recirculating I region downstream of the step, where high mass-transfer capacity was also experimentally observed. Since, corrosion is frequently mass-transfer., controlled, our findings, put forward this apparatus as useful tool for future corrosion research.

Low-temperature single-crystal Raman and neutron-diffraction study of the hydrogenous ammonium copper(II) tutton salt and the deuterated analogue in the metastable state

Low-temperature (15 K) single-crystal neutron-diffraction structures and Raman spectra of the salts (NX4)(2)[CU(OX2)(6)](SO4)(2), where X = H or D, are reported. This study is concerned with the origin of the structural phase change that is known to occur upon deuteration. Data for the deuterated salt were measured in the metastable state, achieved by application of 500 bar of hydrostatic pressure at similar to303 K followed by cooling to 281 K and the subsequent release of pressure. This allows for the direct comparison between the hydrogenous and deuterated salts, in the same modification, at ambient pressure and low temperature. The Raman spectra provide no intimation of any significant change in the intermolecular bonding. Furthermore, structural differences are few, the largest being for the long Cu-O bond, which is 2.2834(5) and 2.2802(4) Angstrom for the hydrogenous and the deuterated salts, respectively. Calorimetric data for the deuterated salt are also presented, providing an estimate of 0.17(2) kJ/mol for the enthalpy difference between the two structural forms at 295.8(5) K. The structural data suggest that substitution of hydrogen for deuterium gives rise to changes in the hydrogen-bonding interactions that result in a slightly reduced force field about the copper(II) center. The small structural differences suggest different relative stabilities for the hydrogenous and deuterated salts, which may be sufficient to stabilize the hydrogenous salt in the anomalous structural form.